Method of depositing titanium dioxide (rutile) as a gate dielectric for MIS device fabrication
Assignee: Texas Instruments Inc
•
Filing: 1978-11-20
•
Granted: 1980-04-29
•
Expires: 1998-11-20
Abstract
Abstract The invention is embodied in a novel method of forming titanium dioxide layers for metal-insulator-semiconductor device dielectrics. The titanium dioxide of a type known as rutile is formed by the deposition of titanium metal upon a layer of silicon dioxide and oxidation of titanium in an oxygen ambient at high temperatures.
Inventors
- 👤 Henry B. Morris
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 03:42
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6938; H10P14/6939; H10P14/69394; H10D; H10D64/00; H10D64/01; H10D64/013; H10D64/01302; H10D64/01332; H10D64/0135; H10D64/031; H10D64/037; H10D64/60; H10D64/66; H10D64/68; H10D64/681; H10D64/685; H10D64/691; H10P14/63; H10P14/6302; H10P14/6304; H10P14/6314; H10P14/65; H10P14/6516; H10P14/6529; H10P14/66; H10P14/662; H10P14/6921; H10P14/69215; H10D64/01336; H10D64/01346; H10P14/6306; H10P14/6308; H10P14/6309; H10P14/6322
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
84 words
A method of forming a layer of titanium dioxide on a substrate of semiconductor material, comprising: forming an insulating layer of a controlled thickness on a substrate of semiconductor material; depositing a layer of titanium metal on the insulating layer; thermally oxidizing the layer of titanium metal in a dry oxygen atmosphere at a temperature maintained in excess of 200 Degrees C.; and converting the layer of titanium metal into a titanium dioxide layer of rutile form in response to the thermal oxidation thereof.
Claim 2
Independent Claim
84 words
A method of forming a layer of titanium dioxide on a substrate of semiconductor material, comprising: forming an insulating layer of a controlled thickness on a substrate of semiconductor material; depositing a layer of titanium metal on the insulating layer; thermally oxidizing the layer of titanium metal in a dry oxygen atmosphere at a temperature maintained in excess of 200 Degrees C.; and converting the layer of titanium metal into a titanium dioxide layer of rutile form in response to the thermal oxidation thereof.
Claim 3
Independent Claim
100 words
A method of forming a layer of titanium dioxide on a substrate of semiconductor material, comprising: providing a substrate of monocrystalline silicon of one type conductivity; growing an oxide layer on the silicon substrate to a controlled thickness of the order of 50-500 Angstroms; depositing a layer of titanium metal onto the silicon oxide layer of controlled thickness; subjecting the titanium metal layer to oxidation in a heated environment at a temperature maintained in excess of 200 Degrees C.; and converting the titanium metal layer into a titanium dioxide layer of rutile form in response to its subjection to oxidation.
Claim 4
Independent Claim
100 words
A method of forming a layer of titanium dioxide on a substrate of semiconductor material, comprising: providing a substrate of monocrystalline silicon of one type conductivity; growing an oxide layer on the silicon substrate to a controlled thickness of the order of 50-500 Angstroms; depositing a layer of titanium metal onto the silicon oxide layer of controlled thickness; subjecting the titanium metal layer to oxidation in a heated environment at a temperature maintained in excess of 200 Degrees C.; and converting the titanium metal layer into a titanium dioxide layer of rutile form in response to its subjection to oxidation.
Claim 5
Dependent Claim
27 words
A method as set forth in claim 2 wherein the oxide layer is grown on the substrate to a controlled thickness of the order of 100-300 Angstroms.
Claim 6
Dependent Claim
76 words
A method as set forth in claim 2 wherein the growing of the oxide layer on the substrate is accomplished by subjecting an exposed surface of the substrate to an oxygen atmosphere at an elevated temperature of the order of 900 Degrees C.; and forming an oxide layer on the exposed surface of the substrate to a controlled thickness in response to the subjection of the exposed surface of the substrate to the heated oxygen atmosphere.
Claim 7
Dependent Claim
26 words
A method as set forth in claim 2 wherein the layer of titanium metal is deposited onto the silicon oxide layer of controlled thickness by evaporation.
Claim 8
Dependent Claim
25 words
A method as set forth in claim 2 further including subjecting the rutile-form titanium dioxide layer to a heat anneal treatment in a hydrogen atmosphere.
Claim 9
Dependent Claim
33 words
A method as set forth in claim 2 wherein the layer of titanium metal is deposited onto the silicon oxide layer of controlled thickness to a thickness of the order of 250-3000 Angstroms.
References Cited (Backward Citations)
US3201667A
Cited
US3409429A
Cited
US3533850A
Cited
US3615947A
Cited
US3470609A
Cited
US3686544A
Cited
US3690945A
Cited
US3615873A
Cited
US3663279A
Cited
US3646665A
Cited
US3731163A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-04-29 | 1983-10-29 | 1984-04-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-04-29 | 1987-10-29 | 1988-04-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-04-29 | 1991-10-29 | 1992-04-29 | $7700.00 | Window Closed / Lapsed |