Flame retardant thermoplastic molding compositions of high electroconductivity
Assignee: MITech Corp
•
Filing: 1982-11-22
•
Granted: 1986-06-24
•
Expires: 2002-11-22
Abstract
Abstract Flame retardant, thermoplastic molding compositions of high electroconductivity comprising between about 2% and about 45% by weight of finely divided conductive carbon black particles substantially uniformly dispersed within a cementitious matrix having a chlorine content of at least about 24% by weight and composed predominantly of substantially thermoplastic resins not substantially less than half of which by weight are vinyl chloride polymers which have a vinyl chloride content of at least about 70% by weight and K-values between about 45 and about 70, and wherein said cementitious matrix also contains from about 1% to about 15% by weight of a well balanced lubricant/stabilizer combination comprising lubricants which are solid at temperatures up to at least about 50 DEG C., together with effective stabilizers, are disclosed.
Inventors
- 👤 Lothar W. Kleiner
- 👤 Andrew S. Pazur
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 11:28
CPC Classifications
C; C08; C08L; C08L27/00; C08L27/02; C08L27/04; C08L27/06
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
193 words
A flame retardant, thermoplastic composition of high electroconductivity for manufacture of static electricity dissipating devices comprising between about 2% and about 45% by weight of finely divided conductive carbon black substantially uniformly dispersed within a cementitious matrix having a chlorine content of at least about 24% by weight and composed predominantly of substantially thermoplastic resins not substantially less than half of which by weight are vinyl chloride polymers which have a vinyl chloride content of at least about 80% by weight and K-values between about 45 and about 70, said cementitious matrix also containing a stabilizer/lubricant system comprising at least three different classes of additive, said classes of additive consist of (1) waxy lubricants which are solid at temperatures up to at least 50° C. under normal pressure, (2) fatty acid salts of magnesium, lithium or alkaline earth metals , and (3) stabilizing compounds containing metal ions selected from the group consisting of lead, tin and antimony, each said classes of additive being present in the composition in an amount of at least 1% by weight of the cementitious matrix and in total not exceed 15% by weight of the total cementitious matrix.
Claim 2
Dependent Claim
193 words
A flame retardant, thermoplastic composition of high electroconductivity for manufacture of static electricity dissipating devices comprising between about 2% and about 45% by weight of finely divided conductive carbon black substantially uniformly dispersed within a cementitious matrix having a chlorine content of at least about 24% by weight and composed predominantly of substantially thermoplastic resins not substantially less than half of which by weight are vinyl chloride polymers which have a vinyl chloride content of at least about 80% by weight and K-values between about 45 and about 70, said cementitious matrix also containing a stabilizer/lubricant system comprising at least three different classes of additive, said classes of additive consist of (1) waxy lubricants which are solid at temperatures up to at least 50° C. under normal pressure, (2) fatty acid salts of magnesium, lithium or alkaline earth metals , and (3) stabilizing compounds containing metal ions selected from the group consisting of lead, tin and antimony, each said classes of additive being present in the composition in an amount of at least 1% by weight of the cementitious matrix and in total not exceed 15% by weight of the total cementitious matrix.
Claim 3
Dependent Claim
46 words
A composition as claimed in claim 1 wherein said cementitious matrix includes up to about 50% by weight of polymeric adjuvants melt blended with said vinyl chloride polymers, said polymeric adjuvants are selected from the group consisting of impact strength additives and high temperature processing aids.
Claim 4
Dependent Claim
31 words
A composition as claimed in claim 2 wherein said polymeric adjuvants include at least one partly elastomeric polymer in amounts of at least about 1% by weight of said cementitious matrix.
Claim 5
Dependent Claim
54 words
A composition as claimed in claim 3 wherein said partly elastomeric polymer is either a graft copolymer formed by graft polymerizing one or more of vinyl aromatics, acrylate monomers and acrylonitriles on a preformed rubbery backbone polymer or on a chlorinated linear polyethylene containing between about 25% and about 50% by weight combined chlorine.
Claim 6
Dependent Claim
32 words
A composition as claimed in claim 2 wherein said polymeric adjuvants include at least one nongrafted polymeric impact modifier in amounts of at least about 1% by weight of said cementitious matrix.
Claim 7
Dependent Claim
37 words
A composition as claimed in claim 1 wherein said cementitious matrix includes various minor additives including pigments, inert fillers, liquid plasticizers, liquid lubricants, synergists and mixtures thereof in an amount of about 10% by weight or less.
Claim 8
Dependent Claim
162 words
A flame retardant, thermoplastic composition of high electroconductivity for manufacture of static electricity dissipating devices by extrusion comprising about 10% by weight of the final composition, of finely divided conductive carbon black particles, substantially uniformly dispersed within a cementitious matrix having a chlorine content of at least about 24% by weight and composed predominantly of about 70% by weight of a vinyl chloride rigid homopolymer thermoplastic resin having a K-value of about 50 to 60, said cementitious matrix also containing about 10% to 20% by weight of a chlorinated polyethylene modifier having a chlorine content of about 30% to 40% by weight and a well balanced lubricant/stabilizer system comprising a balanced stabilizer system of about 1% to 3% by weight of tin mercaptide stabilizer, about 2% to 4% by weight of a balanced lubricant system consisting of a paraffinic wax, calcium stearate and magnesium stearate, and a polyethylene wax as well as about 1% to 5% by weight of a processing aid.
Claim 9
Dependent Claim
162 words
A flame retardant, thermoplastic composition of high electroconductivity for manufacture of static electricity dissipating devices by extrusion comprising about 10% by weight of the final composition, of finely divided conductive carbon black particles, substantially uniformly dispersed within a cementitious matrix having a chlorine content of at least about 24% by weight and composed predominantly of about 70% by weight of a vinyl chloride rigid homopolymer thermoplastic resin having a K-value of about 50 to 60, said cementitious matrix also containing about 10% to 20% by weight of a chlorinated polyethylene modifier having a chlorine content of about 30% to 40% by weight and a well balanced lubricant/stabilizer system comprising a balanced stabilizer system of about 1% to 3% by weight of tin mercaptide stabilizer, about 2% to 4% by weight of a balanced lubricant system consisting of a paraffinic wax, calcium stearate and magnesium stearate, and a polyethylene wax as well as about 1% to 5% by weight of a processing aid.
Claim 10
Dependent Claim
42 words
A composition as claimed in claims 7 or 1 wherein said finely divided conductive carbon black has a bulk density of from about 125 g/l to about 300 g/l and a nitrogen surface area from about 200 to 1,500 m 2 /g.
Claim 11
Dependent Claim
29 words
A flame retardant thermoplastic composition as claimed in claims 7 or 1 wherein said vinyl chloride polymers have number average molecular weights of from about 25,000 to about 110,000.
Claim 12
Dependent Claim
29 words
A flame retardant, thermoplastic composition as claimed in claims 7 or 1 wherein said vinyl chloride polymers have number average molecular weights of from about 40,000 to about 85,000.
Claim 13
Dependent Claim
21 words
A flame retardant, thermoplastic extrusion composition as claimed in claim 1 wherein said vinyl chloride has K-values between 50 and 60.
Claim 14
Dependent Claim
37 words
A process for producing a composition as claimed in claims 7 or 1 wherein said conductive carbon black is added to the other ingredients by utilizing a starve-fed hopper system to an extruder, continuous mixer or kneader.
Claim 15
Dependent Claim
36 words
A process for producing a composition as claimed in claims 7 or 1 wherein said conductive carbon black is added to the other ingredients before introduction to a hopper of an extruder, continuous mixer or kneader.
Claim 16
Dependent Claim
39 words
A process for producing a composition as claimed in claims 7 or 1 wherein said conductive carbon black is added to said cementitious matrix by introduction into one of the final zones of an extruder, continuous mixer or kneader.
Claim 17
Dependent Claim
32 words
A process for producing a composition as claimed in claims 7 or 1 wherein said conductive carbon black and the other ingredients are simultaneously introduced to the hopper of a batch mixer.
Claim 18
Dependent Claim
39 words
A process for producing an extruded article from the composition as claimed in claims 7 or 1 wherein said article is produced by profile extrusion or sheet extrusion which may be followed by vacuum molding or other reshaping operation.
Claim 19
Dependent Claim
14 words
An extruded article produced using the compositions as claimed in claims 7 or 1.
References Cited (Backward Citations)
GB1578447A
Cited
US4151132A
Cited
US4233191A
Cited
US4241120A
Cited
US4228050A
Cited
US4288352A
Cited
US4293452A
Cited
US4288568A
Cited
US4399061A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-23 | 1989-12-23 | 1990-06-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-23 | 1993-12-23 | 1994-06-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-23 | 1997-12-23 | 1998-06-24 | $7700.00 | Window Closed / Lapsed |