Electrically conductive polymeric compositions
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1979-03-26
•
Granted: 1981-09-08
•
Expires: 1999-03-26
Abstract
Abstract This invention relates to the injection moldable and extrusion type electrically conductive polymeric blend compositions having a viscosity at 200 DEG C. at 0.73 sec-1 of less than about 8x105 poises. The compositions used for elastomeric articles include a neutralized sulfonated polymer; graphite fiber at a concentration of about 1 to about 50 parts by weight per 100 parts by weight of neutralized sulfonated polymer; and a preferential plasticizer at about less than 60 parts by weight based on 100 parts by weight of the neutralized sulfonated polymer. The composition may also optionally include fillers, oils and other additives. These blend compositions can be readily processed due to their superior rheological properties on conventional plastic fabrication equipment, especially on low and high pressure injection molding or extrusion equipment into electrically conductive articles having excellent physical and electrical properties.
Inventors
- 👤 Robert A. Weiss
- 👤 Robert D. Lundberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 21:43
CPC Classifications
H; H01; H01B; H01B1/00; H01B1/20; H01B1/24; C; C08; C08K; C08K7/00; C08K7/02; C08K7/04; C08K7/06
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
121 words
A polymeric composition produced by the high shear intensity mixing of a mixture of: (a) a neutralized sulfonated polymer having about 5 to about 100 meq. neutralized sulfonate groups per 100 grams of said neutralized sulfonate polymer, said neutralized sulfonated polymer being formed from a unsulfonated polymer having a Mooney viscosity (M.L. 1+8, 212° F.) of about 10 to about 60; (b) about 10 to 20 parts by weight of discontinuous and uniaxially oriented carbon or graphite fibers per 100 parts by weight of said neutralized sulfonated polymer, said fibers having a length of about 0.125 inches; and (c) at least about 3 parts by weight of a preferential ionic plasticizer based on 100 parts by weight of said neutralized polymer.
Claim 2
Dependent Claim
121 words
A polymeric composition produced by the high shear intensity mixing of a mixture of: (a) a neutralized sulfonated polymer having about 5 to about 100 meq. neutralized sulfonate groups per 100 grams of said neutralized sulfonate polymer, said neutralized sulfonated polymer being formed from a unsulfonated polymer having a Mooney viscosity (M.L. 1+8, 212° F.) of about 10 to about 60; (b) about 10 to 20 parts by weight of discontinuous and uniaxially oriented carbon or graphite fibers per 100 parts by weight of said neutralized sulfonated polymer, said fibers having a length of about 0.125 inches; and (c) at least about 3 parts by weight of a preferential ionic plasticizer based on 100 parts by weight of said neutralized polymer.
Claim 3
Dependent Claim
36 words
A composition according to claim 1, wherein said neutralized sulfonated polymer is formed from an elastomeric polymer selected from the group consisting of a copolymer of an isoolefin and a conjugated multiolefin, and an EPDM terpolymer.
Claim 4
Dependent Claim
42 words
A composition according to claim 1, wherein said neutralized sulfonated polymer is formed from a polyvinyl aromatic thermoplastic selected from the group consisting of polystyrene, poly-t-butyl styrene, polychlorostyrene, poly-methylstyrene, and terpolymers of the aforementioned with acrylonitrile or vinyl toluene and mixtures thereof.
Claim 5
Dependent Claim
46 words
A composition according to claim 1, wherein said neutralized sulfonate groups are neutralized with a counterion being selected from the group consisting of ammonium, antimony, aluminum, lead and metal ions from Groups IA, IIA, IB and IIB of the Periodic Table of Elements and mixtures thereof.
Claim 6
Dependent Claim
43 words
A composition according to claim 2, wherein said EPDM terpolymer consists of about 40 to about 80wt. % of ethylene, of about 10 to about 53 wt. % of propylene and of about 1 to about 10 wt. % of a non-conjugated diene.
Claim 7
Dependent Claim
23 words
A composition according to claim 5, wherein said non-conjugated diene is selected from the group consisting of 1,4-hexadiene, alkenyl substituted norbornenes, and tetrahydroindene.
Claim 8
Dependent Claim
12 words
A composition according to claim 6, wherein said non-conjugated diene is 5-ethylidene-2-norbornene.
Claim 9
Dependent Claim
35 words
A composition according to claim 1, wherein said preferential plasticizer is present at a concentration level of at least about 9 parts by weight based on 100 parts by weight of said neutralized sulfonated polymer.
Claim 10
Dependent Claim
40 words
A composition according to claim 8, wherein said preferential plasticizer is selected from the group consisting of carboxylic acids and metallic salts of said carboxylic acids and mixtures thereof, said carboxylic acid having about 5 to about 30 carbon atoms.
Claim 11
Dependent Claim
59 words
A composition according to claim 8, wherein said preferential plasticizer is a combination of stearic acid and a metallic salt of said stearic acid, the metal ion of said metallic salt being selected from the group consisting of lead, antimony, aluminum and metals from Groups IA, IIA, IB and IIB of the Periodic Table of Elements and mixtures thereof.
Claim 12
Dependent Claim
27 words
A composition according to claim 1, wherein said preferential plasticizer is a metallic salt of an aliphatic carboxylic acid having about 5 to about 30 carbon atoms.
Claim 13
Dependent Claim
40 words
A composition according to claim 1, wherein said preferential plasticizer is selected from the group consisting of an amide, an urea, a thiourea, and a metallic salt of an aliphatic carboxylic acid having about 5 to about 30 carbon atoms.
Claim 14
Dependent Claim
29 words
A composition according to claim 1, further including a non-polar process oil being selected from the group consisting of paraffinic oils, naphthenic oils, and aromatic oils and mixtures thereof.
Claim 15
Dependent Claim
32 words
A composition of claim 1, further including a crystalline hydrocarbon was having a melting point of about 135° F. to about 220° F. and an Mn of about 1000 to about 4000.
Claim 16
Dependent Claim
28 words
A composition according to claim 14, further including a filler selected from the group consisting of carbon black, calcium carbonate, amorphous silica, talc and clay and mixtures thereof.
Claim 17
Dependent Claim
28 words
The composition according to claim 1, further including a filler selected from the group consisting of carbon black, calcium carbonate, amorphous silica, talc and clay and mixtures thereof.
Claim 18
Dependent Claim
13 words
The composition according to claim 1, wherein said preferential plasticizer is zinc stearate.
References Cited (Backward Citations)
US3406126A
Cited
US3642728A
Cited
JPS4877395A
Cited
US3908061A
Cited
US3870841A
Cited
US4061827A
Cited
US4014831A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-09-07 | 1985-03-09 | 1985-09-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-09-07 | 1989-03-09 | 1989-09-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-09-07 | 1993-03-09 | 1993-09-08 | $7700.00 | Window Closed / Lapsed |