Method for selective deposition of tungsten on silicon
Assignee: Intersil Corp
•
Filing: 1984-11-09
•
Granted: 1986-06-17
•
Expires: 2004-11-09
Abstract
Abstract A metal is selectively chemically vapor deposited on a substrate through openings in a moisture adsorbing mask layer by maintaining moisture in the mask layer. Thick metal layers are formed by precharging the mask with moisture. Also a cleaned tube is prepared for selective deposition by operating the process with a bare substrate until the tube is coated. The selective deposition is then performed.
Inventors
- 👤 Edward M. King
- 👤 Kurt E. Gsteiger
- 👤 Joseph S. Raby
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 06:39
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/056; H10W20/057; C; C23; C23C; C23C16/00; C23C16/04; H10P; H10P14/00; H10P14/40; H10P14/42; H10P14/43; H10P14/432
Claims Analysis
Total Claims: 38
Claim 1
Independent Claim
94 words
A method of applying a tungsten layer to selected portions of a substrate comprising: applying moisture to at least first surface areas of said substrate which comprise moisture adsorbing material where tungsten is not desired such that said moisture is adsorbed by said moisture adsorbing material of said first surface areas for the purpose of preventing tungsten deposition on said first surface areas; and disposing said substrate in a vapor deposition environment containing a tungsten gas such that tungsten metal is deposited on said selected portions of said substrate not having adsorbed moisture thereon.
Claim 2
Independent Claim
94 words
A method of applying a tungsten layer to selected portions of a substrate comprising: applying moisture to at least first surface areas of said substrate which comprise moisture adsorbing material where tungsten is not desired such that said moisture is adsorbed by said moisture adsorbing material of said first surface areas for the purpose of preventing tungsten deposition on said first surface areas; and disposing said substrate in a vapor deposition environment containing a tungsten gas such that tungsten metal is deposited on said selected portions of said substrate not having adsorbed moisture thereon.
Claim 3
Dependent Claim
24 words
The method according to claim 1 wherein said selected portions one comprised of silicon and said first surface areas are comprised of glass materials.
Claim 4
Dependent Claim
13 words
The method according to claim 2 wherein said glass materials comprise silicon oxides.
Claim 5
Dependent Claim
13 words
The method according to claim 2 wherein said glass materials comprise silicon nitrides.
Claim 6
Dependent Claim
44 words
The method according to claim 1 wherein said substrate is removed from said vapor deposition environment periodically, prior to complete release of moisture from said first surface areas, and moisture is reapplied to said first surface areas such that moisture is again adsorbed thereby.
Claim 7
Dependent Claim
18 words
The method according to claim 1 wherein said vapor deposition environment comprises tungsten hexafluoride and hydrogen gas flows.
Claim 8
Dependent Claim
28 words
The method according to claim 6 wherein said tungsten hexafluoride gas flow rate is between 5 and 60 SCCM and hydrogen gas flow rate is about 1000 SCCM.
Claim 9
Dependent Claim
26 words
The method according to claim 6 wherein said vapor deposition environment temperature is less than 300° C. and the pressure is between 0.2 and 0.5 Torr.
Claim 10
Dependent Claim
35 words
The method according to claim 1 wherein the surface of said substrate is subject first to a hydrofluoric pretreatment to remove native oxide growth and then to an ammonium hydroxide dip to remove residual fluorine.
Claim 11
Dependent Claim
43 words
The method according to claim 1 wherein said moisture is applied to said substrate by disposing said substrate in an evacuated chamber and back filling with an atmosphere of more than 50% humidity and in a temperature range between 250° and 400° C.
Claim 12
Independent Claim
120 words
A method of selectively applying tungsten to a substrate having silicon and glass surface areas wherein tungsten is selectively deposited over said silicon surface areas but not over said glass areas comprising: applying water to said glass surface areas such that the water is adsorbed thereby; applying tungsten to said substrate by vapor deposition from a gas flow containing a tungsten gas until said adsorbed water is about to be depleted from said glass surfaces; reapplying water to said glass surfaces such that the water is adsorbed thereby; and continuing to apply tungsten to said substrate by vapor deposition from a gas flow containing tungsten gas as along as said reapplied and adsorbed water is present in said glass surfaces.
Claim 13
Independent Claim
120 words
A method of selectively applying tungsten to a substrate having silicon and glass surface areas wherein tungsten is selectively deposited over said silicon surface areas but not over said glass areas comprising: applying water to said glass surface areas such that the water is adsorbed thereby; applying tungsten to said substrate by vapor deposition from a gas flow containing a tungsten gas until said adsorbed water is about to be depleted from said glass surfaces; reapplying water to said glass surfaces such that the water is adsorbed thereby; and continuing to apply tungsten to said substrate by vapor deposition from a gas flow containing tungsten gas as along as said reapplied and adsorbed water is present in said glass surfaces.
Claim 14
Independent Claim
91 words
A method of selective deposition of tungsten on a substrate by vapor deposition techniques comprising: applying moisture to areas of said substrate where tungsten deposition is not desired, such that water is adsorbed by said areas and released during said vapor deposition techniques; disposing said substrate in a vapor deposition environment containing a tungsten gas such that tungsten deposition results on said substrate where water is not being released; and maintaining the water content of at least a portion of said areas throughout said vapor deposition of tungsten on said substrate.
Claim 15
Independent Claim
91 words
A method of selective deposition of tungsten on a substrate by vapor deposition techniques comprising: applying moisture to areas of said substrate where tungsten deposition is not desired, such that water is adsorbed by said areas and released during said vapor deposition techniques; disposing said substrate in a vapor deposition environment containing a tungsten gas such that tungsten deposition results on said substrate where water is not being released; and maintaining the water content of at least a portion of said areas throughout said vapor deposition of tungsten on said substrate.
Claim 16
Independent Claim
90 words
A method of chemical vapor deposition onto a substrate containing silicon and glass film surface areas, comprising: applying moisture to said substrate such that water is adsorbed by said glass film surface area; and applying a tungsten gas to said substrate during chemical vapor deposition as long as water is present in said glass film surface areas, said tungsten gas reacting with said silicon surface area to apply a tungsten metal layer thereto and not reacting with said glass film surface area to not apply a tungsten metal layer thereto.
Claim 17
Independent Claim
90 words
A method of chemical vapor deposition onto a substrate containing silicon and glass film surface areas, comprising: applying moisture to said substrate such that water is adsorbed by said glass film surface area; and applying a tungsten gas to said substrate during chemical vapor deposition as long as water is present in said glass film surface areas, said tungsten gas reacting with said silicon surface area to apply a tungsten metal layer thereto and not reacting with said glass film surface area to not apply a tungsten metal layer thereto.
Claim 18
Independent Claim
106 words
A method of selective deposition of a first material capable of being selectively chemically vapor deposited onto a moisture free surface by exposing to a chemical vapor deposition environment a substrate having a layer of water adsorbent material with openings exposing a second material through said openings comprising: applying moisture to said water absorbent material to be adsorbed therein; heating said substrate in a gas flow of said first material in a deposition furnace to deposit said first material on said exposed second material and not on said water adsorbent material; and terminating said gas flow before said water is depleted from said water adsorbent material.
Claim 19
Independent Claim
106 words
A method of selective deposition of a first material capable of being selectively chemically vapor deposited onto a moisture free surface by exposing to a chemical vapor deposition environment a substrate having a layer of water adsorbent material with openings exposing a second material through said openings comprising: applying moisture to said water absorbent material to be adsorbed therein; heating said substrate in a gas flow of said first material in a deposition furnace to deposit said first material on said exposed second material and not on said water adsorbent material; and terminating said gas flow before said water is depleted from said water adsorbent material.
Claim 20
Dependent Claim
19 words
The method according to claim 14 including removing all non-adsorbed water prior to gas flow of said first material.
Claim 21
Dependent Claim
37 words
The method according to claim 14 including interrupting said gas flow before said water is depleted from said water adsorbent material, reapplying water to said water adsorbent material and restarting said gas flow of said first material.
Claim 22
Dependent Claim
33 words
The method according to claim 16 wherein reapplying water includes subjecting said substrate to a humid atmosphere in said deposition furnace, evacuating said furnace of said humid atmosphere before restarting said gas flow.
Claim 23
Dependent Claim
20 words
The method according to claim 14 wherein said gas flow of said first material is sufficiently high to prevent etching.
Claim 24
Dependent Claim
34 words
The method according to claim 14 including applying said water adsorbent material and forming the openings in said layer of water adsorbent material of said substrate to minimize the amount of second material exposed.
Claim 25
Dependent Claim
18 words
The method according to claim 14 wherein said second material is silicon and said first material is tungsten.
Claim 26
Dependent Claim
20 words
The method according to claim 20 wherein said gas of said first material is tungsten hexaflouride and a reducing gas.
Claim 27
Dependent Claim
15 words
The method according to claim 20 wherein said water adsorbing material is a silicon compound.
Claim 28
Dependent Claim
36 words
The method according to claim 14 further comprising including a plurality of said substrates in said furnace and forming a coating on one side of said substrates to minimize the amount of substrate that is exposed.
Claim 29
Dependent Claim
19 words
The method according to claim 14 wherein said furnace is heated in the range of 250° to 400° C.
Claim 30
Independent Claim
125 words
A method of selective deposition of a first material capable of being selectively chemically vapor deposited onto a moisture free surface by exposing to a chemical vapor deposition environment a substrate having a layer of water adsorbent material with openings exposing a second material through said openings comprising: positioning a localized source of water adjacent said substrate in a deposition furnace; heating said furnace to cause said localized source of water to produce a deposition inhibiting barrier at the surface of said water adsorbent material; flowing a gas of said first material in said furnace to deposit said first material on said exposed second material and not on said water adsorbent material; and terminating said gas flow before said localized source of water is depleted.
Claim 31
Independent Claim
125 words
A method of selective deposition of a first material capable of being selectively chemically vapor deposited onto a moisture free surface by exposing to a chemical vapor deposition environment a substrate having a layer of water adsorbent material with openings exposing a second material through said openings comprising: positioning a localized source of water adjacent said substrate in a deposition furnace; heating said furnace to cause said localized source of water to produce a deposition inhibiting barrier at the surface of said water adsorbent material; flowing a gas of said first material in said furnace to deposit said first material on said exposed second material and not on said water adsorbent material; and terminating said gas flow before said localized source of water is depleted.
Claim 32
Dependent Claim
18 words
The method according to claim 25 wherein said gas includes a first material gas and a reduction gas.
Claim 33
Dependent Claim
21 words
The method according to claim 26 wherein said deposition inhibiting barrier is produced by said heat and reduction of said gases.
Claim 34
Dependent Claim
14 words
The method according to claim 25 wherein said furnace is heated below 300° C.
Claim 35
Independent Claim
113 words
A method of preparing a washed tube for selective chemical vapor deposition of a first material capable of being selectively chemically vapor deposited onto a moisture free surface by exposing a substrate having an exposed portion of a second material to a vapor deposition environment comprising: placing a quantity of said second material in said tube; heating said tube; flowing a gas of said first material in said heated tube to react with said second material and coat the interior of said tube; terminating said gas flow; removing the remaining portion of said quantity of said second material; inserting said substrate; and beginning said selective chemical vapor deposition process of said first material.
Claim 36
Independent Claim
113 words
A method of preparing a washed tube for selective chemical vapor deposition of a first material capable of being selectively chemically vapor deposited onto a moisture free surface by exposing a substrate having an exposed portion of a second material to a vapor deposition environment comprising: placing a quantity of said second material in said tube; heating said tube; flowing a gas of said first material in said heated tube to react with said second material and coat the interior of said tube; terminating said gas flow; removing the remaining portion of said quantity of said second material; inserting said substrate; and beginning said selective chemical vapor deposition process of said first material.
Claim 37
Dependent Claim
17 words
The method according to claim 29 wherein said tube is heated in the range of 250°-400° C.
Claim 38
Dependent Claim
36 words
The method according to claim 30 including preheating said tube at over 700° C. for an extended period of time and removing the atmosphere prior to placing said quantity of said second material in said tube.
References Cited (Backward Citations)
US3477872A
Cited
US3565676A
Cited
SU570658A1
Cited
JPS5238428A
Cited
US4404235A
Cited
US4349408A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-16 | 1989-12-16 | 1990-06-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-16 | 1993-12-16 | 1994-06-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-16 | 1997-12-16 | 1998-06-17 | $7700.00 | Window Closed / Lapsed |