Production method of a high magnetic permeability film
Assignee: Sharp Corp
•
Filing: 1984-10-24
•
Granted: 1986-06-03
•
Expires: 2004-10-24
Abstract
Abstract A method for producing a high magnetic permeability alloy film, wherein an alloy material composed of 1-6 wt % Al, 20-35 wt % Si and the remainder of iron is irradiated with an electron beam in a vacuum deposition apparatus equipped with an electron gun, and the vapor of the alloy material is deposited on a substrate for a predetermined time to form a high magnetic permeability alloy film, comprising further a step of preventing the irregular deposition caused if the concentration of aluminum in the vapor to be deposited increases.
Inventors
- 👤 Masaru Kadono
- 👤 Kumio Nago
- 👤 Shuuhei Tsuchimoto
- 👤 Mitsuhiko Yoshikawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 14:26
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/06; C23C14/14
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
103 words
A method for producing a high permeability alloy film comprising steps as follows: irradiating an alloy material composed of 1-6 wt % Al, 20-35 wt % Si and the remainder of Fe with an electron beam in order to evaporate said material under vacuum, depositing the vapor on a substrate for a predetermined time to form a high magnetic permeability alloy film thereon, and preventing the irregular deposition which takes place if the concentration of aluminum in the vapor begins to increase before said predetermined time has passed, and resuming the deposition after the concentration of aluminum in the vapor begins to decrease.
Claim 2
Independent Claim
103 words
A method for producing a high permeability alloy film comprising steps as follows: irradiating an alloy material composed of 1-6 wt % Al, 20-35 wt % Si and the remainder of Fe with an electron beam in order to evaporate said material under vacuum, depositing the vapor on a substrate for a predetermined time to form a high magnetic permeability alloy film thereon, and preventing the irregular deposition which takes place if the concentration of aluminum in the vapor begins to increase before said predetermined time has passed, and resuming the deposition after the concentration of aluminum in the vapor begins to decrease.
Claim 3
Dependent Claim
41 words
A method according to claim 1, wherein said step to prevent irregular deposition is a step of decreasing the input power of an electron gun to a predetermined value if the concentration of aluminum in the vapor to be deposited increases.
Claim 4
Dependent Claim
36 words
A method according to claim 1, wherein said step to prevent irregular deposition is a step of intercepting the deposition with a shutter means when the concentration of aluminum in the vapor to be deposited increases.
Claim 5
Dependent Claim
46 words
A method according to claim 1, comprising further a step that the vapor deposition on said substrate is intercepted by a shutter means until the concentration of aluminum in the vapor to be deposited has decreased to a value between 20 and about 4 wt %.
Claim 6
Dependent Claim
33 words
A method according to claim 1, comprising further a step that said film of a high magnetic permeability alloy is kept at a temperature between 100° and 800° C. for the heat treatment.
Claim 7
Independent Claim
110 words
A method for producing a high magnetic permeability alloy film comprising steps as follows: putting iron, silcon and aluminum deposition source materials at a predetermined position in a deposition apparatus in such a manner that said silicon and aluminum materials are covered with said iron material, melting said materials with the electron beam to form an alloy material during the process of raising the input powder to be applied to the electron gun, and successively evaporating said alloy material by heating it with an electron beam, and depositing the vapor of said alloy material on a substrate for a predetermined time to form a high magnetic permeability alloy film thereon.
Claim 8
Independent Claim
110 words
A method for producing a high magnetic permeability alloy film comprising steps as follows: putting iron, silcon and aluminum deposition source materials at a predetermined position in a deposition apparatus in such a manner that said silicon and aluminum materials are covered with said iron material, melting said materials with the electron beam to form an alloy material during the process of raising the input powder to be applied to the electron gun, and successively evaporating said alloy material by heating it with an electron beam, and depositing the vapor of said alloy material on a substrate for a predetermined time to form a high magnetic permeability alloy film thereon.
Claim 9
Dependent Claim
31 words
A method according to claim 6, wherein the weight ratios of aluminum, silicon and iron of said deposition source materials are 1-6 wt %, 20-35 wt %, and the remainder, respectively.
Claim 10
Dependent Claim
33 words
A method according to claim 6, wherein in the step of placing said deposition source materials, said iron deposition source material is positioned as a covering layer over said other deposition source materials.
Claim 11
Dependent Claim
33 words
A method according to claim 6, comprising further a step that said film of a high magnetic permeability alloy is kept at a temperature between 100° and 800° C. for the best treatment.
Claim 12
Independent Claim
181 words
A method for producing a multilayer film composed of high magnetic permeability alloy layers having a nonmagnetic layer therebetween, comprising steps as follows: placing an alloy material composed of 1-6 wt % Al, 20-35 wt % Si and the remainder of iron at a predetermined position and a nonmagnetic material at another predetermined position in a vacuum deposition apparatus equipped with an electron gun, evaporating said alloy material by heating it with an electron beam and depositing the vapor generated by heating said alloy material with an electron beam on a substrate in order to form a layer, and evaporating said nonmagnetic material by heating it with an electron beam and depositing the vapor generated on said layer, wherein said two deposition steps are repeated alternatively and successively to form a multilayer film, and preventing the irregular deposition which takes place at the depositing process of said alloy material if the concentration of aluminum in the vapor begins to increase before said predetermined time has passed, and resuming the deposition after the concentration of alumimum in the vapor begins to decrease.
Claim 13
Independent Claim
181 words
A method for producing a multilayer film composed of high magnetic permeability alloy layers having a nonmagnetic layer therebetween, comprising steps as follows: placing an alloy material composed of 1-6 wt % Al, 20-35 wt % Si and the remainder of iron at a predetermined position and a nonmagnetic material at another predetermined position in a vacuum deposition apparatus equipped with an electron gun, evaporating said alloy material by heating it with an electron beam and depositing the vapor generated by heating said alloy material with an electron beam on a substrate in order to form a layer, and evaporating said nonmagnetic material by heating it with an electron beam and depositing the vapor generated on said layer, wherein said two deposition steps are repeated alternatively and successively to form a multilayer film, and preventing the irregular deposition which takes place at the depositing process of said alloy material if the concentration of aluminum in the vapor begins to increase before said predetermined time has passed, and resuming the deposition after the concentration of alumimum in the vapor begins to decrease.
Claim 14
Dependent Claim
42 words
A method according to claim 10, wherein said step to prevent the irregular deposition is a step of decreasing the input power of an electron gun to a predetermined value if the concentration of aluminum in the vapor to be deposited increases.
Claim 15
Dependent Claim
44 words
A method according to claim 11, wherein, during the vapor deposition step of an alloy material, the deposition is intercepted with a shutter means until the concentration of aluminum in the vapor has decreased to a value between 20 and about 4 wt %.
Claim 16
Dependent Claim
28 words
A method according to claim 11, comprising further a step that said multilayer film is kept at a temperature between 100° and 800° C. for the heat treatment.
Claim 17
Dependent Claim
37 words
A method according to claim 10, wherein said step to prevent the irregular deposition is a step of intercepting the deposition with a shutter means when the concentration of aluminum in the vapor to be deposited increases.
Claim 18
Dependent Claim
44 words
A method according to claim 14, wherein, during the vapor deposition step of an alloy material, the deposition is intercepted with a shutter means until the concentration of aluminum in the vapor has decreased to a value between 20 and about 4 wt %.
Claim 19
Dependent Claim
50 words
A method according to claim 10, comprising further a step that the vapor deposition of an alloy material on said substrate is intercepted by a shutter means until the concentration of aluminum in the vapor to be deposited has decreased to a value between 20 and about 4 wt %.
Claim 20
Dependent Claim
28 words
A method according to claim 10, comprising further a step that said multilayer film is kept at a temperature between 100° and 800° C. for the heat treatment.
Claim 21
Independent Claim
164 words
A method for producing a multilayer film composed of high magnetic permeability alloy layers having an insulating layer therebetween, comprising steps as follows: placing first and second deposition source materials at a predetermined position respectively in a vacuum deposition apparatus with an electron gun, said first source materials being constituted by pure iron, pure aluminum and pure silicon each weight of which is predetermined so as to form an alloy material at a following melting step, and said second deposition source material being an insulating material, melting said first deposition source materials by heating with an electron beam to form an alloy material and, successively, depositing the vapor generated by heating said alloy material with an electron beam on a substrate in order to form a layer, and evaporating said second deposition source material by heating it with an electron beam and depositing the vapor generated on said layer, wherein said two deposition steps are repeated alternatively and successively to form a multilayer film.
Claim 22
Independent Claim
164 words
A method for producing a multilayer film composed of high magnetic permeability alloy layers having an insulating layer therebetween, comprising steps as follows: placing first and second deposition source materials at a predetermined position respectively in a vacuum deposition apparatus with an electron gun, said first source materials being constituted by pure iron, pure aluminum and pure silicon each weight of which is predetermined so as to form an alloy material at a following melting step, and said second deposition source material being an insulating material, melting said first deposition source materials by heating with an electron beam to form an alloy material and, successively, depositing the vapor generated by heating said alloy material with an electron beam on a substrate in order to form a layer, and evaporating said second deposition source material by heating it with an electron beam and depositing the vapor generated on said layer, wherein said two deposition steps are repeated alternatively and successively to form a multilayer film.
Claim 23
Dependent Claim
30 words
A method according to claim 18, wherein in the step of placing the first deposition source materials, said iron material is positioned as a covering layer over said other materials.
Claim 24
Dependent Claim
34 words
A method according to claim 18, comprising further a step that said multilayer film of a high magnetic permeability alloy is kept at a temperature between 100° and 800° C. for the heat treatment.
References Cited (Backward Citations)
US4168187A
Cited
US4450186A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-02 | 1989-12-02 | 1990-06-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-02 | 1993-12-02 | 1994-06-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-02 | 1997-12-02 | 1998-06-03 | $7700.00 | Window Closed / Lapsed |