Method for sealing porous metals
Assignee: Mazda Motor Corp
•
Filing: 1985-02-19
•
Granted: 1986-05-27
•
Expires: 2005-02-19
Abstract
Abstract A method for sealing porous metals, which comprises applying powder of a eutectic alloy containing an element having a good diffusibility in a porous metal or powder of a mixture of metals capable of forming the eutectic alloy, to the surface of a porous metal member and heating the surface applied with the powder at a temperature higher than the eutectic temperature of the eutectic alloy to thereby cause the molten eutectic alloy to intrude into pores from the surface of the porous metal member, whereby the melting point of the molten alloy in the pores is promptly increased by diffusion of the element in the porous metal member to solidify the molten metal in the pores, sealing only pores present in the vicinity of the surface of the porous metal member.
Inventors
- 👤 Tsuyoshi Morishita
- 👤 Sigemi Osaki
- 👤 Noriyuki Sakai
- 👤 Yasuhumi Kawado
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 05:51
CPC Classifications
B; B22; B22F; B22F3/00; B22F3/24; B22F3/26; C; C22; C22C; C22C33/00; C22C33/02; C22C33/0242; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12042; Y10T428/12493; Y10T428/12771; Y10T428/12861; Y10T428/12951; Y10T428/12958
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
124 words
A method for sealing porous metals comprised of an iron-based sintered alloy, said method comprising applying powder of a eutectic alloy of one of Fe-P, Fe-P-C, Fe-Mo-C and Fe-B-C type, to the surface of said porous metal member and heating said surface applied with the powder to a temperature higher than the eutectic temperature of said eutectic alloy to allow said molten eutectic alloy to intrude into pores from the surface of the porous metal member so that the melting point of said molten alloy in the pores is promptly increased by diffusion of said element in said porous metal member to solidify said molten metal in the pores, sealing only pores present in the vicinity of the surface of the porous metal member.
Claim 2
Independent Claim
124 words
A method for sealing porous metals comprised of an iron-based sintered alloy, said method comprising applying powder of a eutectic alloy of one of Fe-P, Fe-P-C, Fe-Mo-C and Fe-B-C type, to the surface of said porous metal member and heating said surface applied with the powder to a temperature higher than the eutectic temperature of said eutectic alloy to allow said molten eutectic alloy to intrude into pores from the surface of the porous metal member so that the melting point of said molten alloy in the pores is promptly increased by diffusion of said element in said porous metal member to solidify said molten metal in the pores, sealing only pores present in the vicinity of the surface of the porous metal member.
Claim 3
Dependent Claim
40 words
A method in accordance with claim 1 in which said powder is mixed with 0.5 to 4.0 weight % of camphor and kneaded with an addition of acetone before it is applied to the surface of the porous metal member.
Claim 4
Dependent Claim
39 words
A method in accordance with claim 1 in which said powder is mixed with 1 to 7 weight % of acrylic resin and formed into a sheet before it is applied to the surface of the porous metal member.
Claim 5
Dependent Claim
18 words
A method in accordance with claim 1 in which the heating is carried out in a non-oxidating atmosphere.
Claim 6
Dependent Claim
24 words
A method in accordance with claim 6 in which the non-oxidating atmosphere is one of inactive gas atmospheres, a reducing gas atmosphere and vacuum.
Claim 7
Dependent Claim
61 words
A method in accordance with claim 1 in which said powder is applied to the surface by being mixed with an acrylic binder and a preheating step is carried out prior to the heating step, said preheating step comprising heating the surface applied with said powder to 150° to 380° C. and maintaining at the temperature for more than 5 minutes.
Claim 8
Dependent Claim
35 words
A method in accordance with claim 1 in which quantity of B, P or Mo in accordance with the temperature at which the surface applied with the powder so that sealing depths can be adjusted.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-05-26 | 1989-11-25 | 1990-05-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-05-26 | 1993-11-25 | 1994-05-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-05-26 | 1997-11-25 | 1998-05-27 | $7700.00 | Window Closed / Lapsed |