Method for continuous coating of glass
Assignee: Individual
•
Filing: 1985-02-25
•
Granted: 1986-04-29
•
Expires: 2005-02-25
Abstract
Abstract A process for coating a wide moving web with the product of chemical reactants first brought into contact at a point proximate the glass surface. The process comprises a primary distribution of reactants (across the width of the substrate) through a row of small apertures, then a segregation through a secondary passage to a reaction zone at the surface of the substrate. Reactant distribution pipes are advantageously positioned and shaped to form only a gradual increase in width of the reactant flow path as they enter the reaction zone.
Inventors
- 👤 Roy G. Gordon
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 05:38
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/34; C03; C03C; C03C17/00; C03C17/22; C03C17/225; C03C2217/00; C03C2217/20; C03C2217/28; C03C2217/281; C03C2218/00; C03C2218/10; C03C2218/15; C03C2218/152
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
121 words
A process for forming a metal oxide coating by reacting a water vapor reactant and a metal halide reactant in close proximity to a moving glass substrate, comprising the steps of (a) primarily distributing said reactants through relatively small apertures spaced along tubes transverse to the direction of the glass substrate; (b) secondarily distributing said reactants through passages which are at least twice as wide as said aperture; (c) allowing said reactants to mix in a reaction zone at a position within a zone depth less than one inch from said substrate; and (d) depositing said coating onto said glass over a coating zone along said moving glass, the width of said coating zone being at least twice said zone depth.
Claim 2
Dependent Claim
121 words
A process for forming a metal oxide coating by reacting a water vapor reactant and a metal halide reactant in close proximity to a moving glass substrate, comprising the steps of (a) primarily distributing said reactants through relatively small apertures spaced along tubes transverse to the direction of the glass substrate; (b) secondarily distributing said reactants through passages which are at least twice as wide as said aperture; (c) allowing said reactants to mix in a reaction zone at a position within a zone depth less than one inch from said substrate; and (d) depositing said coating onto said glass over a coating zone along said moving glass, the width of said coating zone being at least twice said zone depth.
Claim 3
Dependent Claim
55 words
A process as defined in claim 1 wherein one said reactant is a tin chloride reactant carried in, an inert carrier gas containing about 0.2 to 0.3 mole percent of oxygen and the other said reactant is water vapor carried in an inert carrier gas, also containing about 0.2 to 0.3 mole percent of oxygen.
Claim 4
Dependent Claim
22 words
A process as defined in claim 1 wherein said reaction zone gradually increases in width as it approaches said moving glass substrate.
Claim 5
Dependent Claim
54 words
A process as defined in claim 1 wherein said apertures are from about 0.1 to about 0.3 centimeters in diameter, are spaced about 2 to 3 centimeters apart across said glass plate and wherein said secondary distribution takes place through passages which are about three times as wide as the diameter of said apertures.
Claim 6
Dependent Claim
28 words
A process as defined in claim 1 wherein said reactants emerge generally upwardly from said small apertures and then flow downwardly through said passages into said reaction zone.
Claim 7
Dependent Claim
28 words
A process as defined in claim 3 wherein said reactants emerge generally upwardly from said small apertures and then flow downwardly through said passages into said reaction zone.
Claim 8
Dependent Claim
28 words
A process as defined in claim 4 wherein said reactants emerge generally upwardly from said small apertures and then flow downwardly through said passages into said reaction zone.
Claim 9
Dependent Claim
55 words
A process as defined in claim 7 wherein one said reactant is a tin chloride reactant carried in, an inert carrier gas containing about 0.2 to 0.3 mole percent of oxygen and the other said reactant is water vapor carried in an inert carrier gas, also containing about 0.2 to 0.3 mole percent of oxygen.
References Cited (Backward Citations)
US2953483A
Cited
US3306768A
Cited
US4206252A
Cited
US4329379A
Cited
US4294868A
Cited
US4476158A
Cited
US4508054A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-04-28 | 1989-10-28 | 1990-04-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-04-28 | 1993-10-28 | 1994-04-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-04-28 | 1997-10-28 | 1998-04-29 | $7700.00 | Window Closed / Lapsed |