Method for growing an oxide layer on a silicon surface
Assignee: Signetics
•
Filing: 1984-07-02
•
Granted: 1986-04-22
•
Expires: 2004-07-02
Abstract
Abstract In an improved method for growing an oxide layer on a silicon surface of a semiconductor body, the semiconductor body is first provided with a silicon surface. A first oxide layer portion is then grown over the silicon surface in a first thermal oxidation process at a temperature of less than about 1000° C. The semiconductor device is then annealed in a nonoxidizing ambient at a temperature above about 1000° C., and finally a second oxide layer portion is then grown over the first oxide layer portion in a second thermal oxidation process to complete the growth of the oxide layer. The silicon surface may be of either polycrystalline or monocrystalline material. This method avoids both the dopant outdiffusion problems associated with present high-temperature oxidation processes and the stress-related irregularities associated with known low-temperature oxidation processes.
Inventors
- 👤 Teh-Yi J. Chen
- 👤 Anjan Bhattacharyya
- 👤 William T. Stacy
- 👤 Charles J. Vorst
- 👤 Albert Schmitz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 16:46
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6302; H10P14/6304; H10P14/6306; H10P14/6308; H10P14/6309; H10P95/00; H10P14/6322
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
108 words
A method for growing an oxide layer on a silicon surface of a semiconductor body, which comprises: providing said semiconductor body with said silicon surface; growing a first oxide layer portion over at least a portion of said silicon surface in a first thermal oxidation process at a temperature of less than or equal to about 950° C.; then annealing said semiconductor body in a nonoxidizing ambient at a temperature greater than or equal to about 1050° C.; and then growing a second oxide layer portion at least over said first oxide layer portion in a second thermal oxidation process to complete the growth of said oxide layer.
Claim 2
Independent Claim
108 words
A method for growing an oxide layer on a silicon surface of a semiconductor body, which comprises: providing said semiconductor body with said silicon surface; growing a first oxide layer portion over at least a portion of said silicon surface in a first thermal oxidation process at a temperature of less than or equal to about 950° C.; then annealing said semiconductor body in a nonoxidizing ambient at a temperature greater than or equal to about 1050° C.; and then growing a second oxide layer portion at least over said first oxide layer portion in a second thermal oxidation process to complete the growth of said oxide layer.
Claim 3
Dependent Claim
20 words
A method for growing an oxide layer as in claim 1, wherein said silicon surface comprises a patterned polysilicon surface.
Claim 4
Dependent Claim
58 words
A method for growing an oxide layer as in claim 2, wherein said first oxide layer portion is grown at a temperature of about 900° C. for about 70 minutes in a dry oxygen ambient and said annealing step is conducted at a temperature of at least about 1100° C. for about 3 minutes in a nitrogen ambient.
Claim 5
Dependent Claim
35 words
A method for growing an oxide layer as in claim 3, wherein said second oxide layer portion is grown at a temperature of about 900° C. for about 60 minutes in a dry oxygen ambient.
Claim 6
Dependent Claim
30 words
A method for growing an oxide layer as in claim 3, wherein said second oxide layer portion is grown at a temperature of about 1150° C. for about 3.5 minutes.
Claim 7
Dependent Claim
29 words
A method for growing an oxide layer as in claim 3, wherein said annealing step comprises heatpulse annealing at a temperature of about 1100° C. for about 30 seconds.
Claim 8
Dependent Claim
19 words
A method for growing an oxide layer as in claim 1, wherein said silicon surface comprises a monocrystalline surface.
Claim 9
Dependent Claim
76 words
A method for growing an oxide layer as in claim 7, wherein said first oxide layer portion is grown to a thickness of about 30 angstroms at a temperature of about 950° C., said annealing step is conducted in an argon ambient at a temperature of about 1050° C. for 1 hour, and said second oxide layer portion is grown at a temperature of 950° C. to achieve a total oxide thickness of about 80 angstroms.
Claim 10
Dependent Claim
27 words
A method for growing an oxide layer as in claim 1, wherein said first and second oxide layer portions are grown by a High Pressure Oxidation process.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-04-21 | 1989-10-21 | 1990-04-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-04-21 | 1993-10-21 | 1994-04-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-04-21 | 1997-10-21 | 1998-04-22 | $7700.00 | Window Closed / Lapsed |