Method of increasing field inversion threshold voltage and reducing leakage current and electrical noise in semiconductor devices
Assignee: Texas Instruments Tucson Corp
•
Filing: 1977-11-10
•
Granted: 1979-05-15
•
Expires: 1997-11-10
Abstract
Abstract A method for processing a semiconductor wafer to reduce electrical noise, to reduce the surface component of junction leakage current, to increase junction reverse breakdown voltage, and to increase field inversion voltage. Subsequent to last high temperature processing to which the semiconductor wafer is exposed in course of its manufacture, the semiconductor wafer is subjected to an annealing cycle in an inert ambient at a temperature in the range of 600 to 950 degrees Centigrade. At this point the semiconductor wafer has a field oxide thereon produced by prior processing operations. The annealing cycle stabilizes the semiconductor device by allowing an oxide-semiconductor interface region of the wafer to attain a minimum energy configuration, thereby reducing the surface-state charge density. The semiconductor wafer is then exposed to an oxidizing ambient for a short time to increase the oxide charge. At the end of the oxidizing procedure, the wafer is quenched to prevent reduction of the oxide charge by diffusion of the oxidizing species which create the oxide charge. The increased oxide charge increases the field inversion voltage. The semiconductor wafer is thus again subjected to an inert ambient, for restabilization. The semiconductor wafer is then subjected to a low temperature annealing cycle in a hydrogen ambient at a temperature in the range from 300 to 500 degrees Centigrade. The low temperature annealing step reduces the surface-state charge density without substantially decreasing the density of the oxide charge trapped in the field oxide, and therefore does not substantially lower the field inversion voltage.
Inventors
- 👤 Robert E. Hickox
- 👤 Heber J. Bresee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 10:45
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6302; H10P14/6304; H10P14/6306; H10P14/6308; H10P14/6309; H10D; H10D64/00; H10D64/01; H10D64/011; H10P14/6322; H10P14/65; H10P14/6516; H10P14/6529; H10P95/00; H10P95/90; Y; Y10; Y10S; Y10S148/00; Y10S148/003; Y10S438/00; Y10S438/91
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
182 words
A method for making a semiconductor device having an increased field inversion threshold voltage and also have improved electrical parameters including reduced PN junction reverse leakage current and reduced electrical noise, wherein said semiconductor device has been subjected to at least one high temperature step including forming an oxide on a layer of semiconductor, said method comprising the further steps of: (a) causing an inert gas to flow past said semiconductor device; (b) ramping the temperature of said semiconductor device from the temperature of said high temperature step to a temperature in the range from 600 to 950 degrees Centigrade; (c) maintaining said semiconductor device at said temperature in the range from 600 to 950 degrees Centigrade; (d) causing an oxidizing gas to flow past said semiconductor device; (e) causing said oxidizing gas to stop flowing past said semiconductor device; (f) reducing the temperature of said semiconductor device; (g) causing hydrogen to flow past said semiconductor device; (h) maintaining said semiconductor device at a temperature in the range from 300 to 500 degrees Centigrade; and (i) stopping the flow of said hydrogen.
Claim 2
Independent Claim
182 words
A method for making a semiconductor device having an increased field inversion threshold voltage and also have improved electrical parameters including reduced PN junction reverse leakage current and reduced electrical noise, wherein said semiconductor device has been subjected to at least one high temperature step including forming an oxide on a layer of semiconductor, said method comprising the further steps of: (a) causing an inert gas to flow past said semiconductor device; (b) ramping the temperature of said semiconductor device from the temperature of said high temperature step to a temperature in the range from 600 to 950 degrees Centigrade; (c) maintaining said semiconductor device at said temperature in the range from 600 to 950 degrees Centigrade; (d) causing an oxidizing gas to flow past said semiconductor device; (e) causing said oxidizing gas to stop flowing past said semiconductor device; (f) reducing the temperature of said semiconductor device; (g) causing hydrogen to flow past said semiconductor device; (h) maintaining said semiconductor device at a temperature in the range from 300 to 500 degrees Centigrade; and (i) stopping the flow of said hydrogen.
Claim 3
Dependent Claim
22 words
The method of claim 1 wherein said temperature in the range from 600 to 950 degrees Centigrade is approximately 860 degrees Centigrade.
Claim 4
Dependent Claim
14 words
The method of claim 1 wherein said inert gas of step (a) is nitrogen.
Claim 5
Dependent Claim
16 words
The method of claim 1 wherein said high temperature step occurs at approximately 1025 degrees Centigrade.
Claim 6
Dependent Claim
16 words
The method of claim 1 wherein the temperature of step (h) is approximately 450 degrees Centigrade.
Claim 7
Dependent Claim
23 words
The method of claim 1 wherein said oxidizing gas of step (d) is caused to flow for a time less than thirty minutes.
Claim 8
Dependent Claim
30 words
The method of claim 6 wherein the duration and the temperature of step (d) are selected to raise the field inversion voltage of said semiconductor device to a predetermined level.
Claim 9
Dependent Claim
20 words
The method of claim 1 wherein the oxidizing gas of step (d) is caused to flow for approximately five minutes.
Claim 10
Dependent Claim
22 words
The method of claim 1 wherein the semiconductor material of said semiconductor device is silicon and the oxide layer is silicon dioxide.
Claim 11
Dependent Claim
34 words
The method of claim 9 wherein the temperature in step (h) is maintained for a time selected to reduce the surface-state charge at the interface between the oxide and silicon to a predetermined level.
Claim 12
Dependent Claim
18 words
The method of claim 1 wherein said ramping is performed over a time period of approximately sixty minutes.
Claim 13
Dependent Claim
31 words
The method of claim 1 wherein the temperature reducing of step (f) is performed at a rate selected to prevent oxygen in the oxide from further diffusion to the oxide-semiconductor interface.
Claim 14
Dependent Claim
15 words
The method of claim 1 wherein the order of steps (f) and (g) is reversed.
Claim 15
Dependent Claim
37 words
The method of claim 1 wherein the duration of said ramping is selected to anneal out surface states induced by differences in thermal expansion coefficients of the oxide layer and the semiconductor material of said semiconductor device.
Claim 16
Dependent Claim
24 words
The method of claim 1 wherein the hydrogen of step (g) is in forming gas which is caused to flow past said semiconductor device.
Claim 17
Dependent Claim
37 words
The method of claim 1 wherein step (f) includes ramping the temperature from said temperature in the range from 600 to 900 degrees Centigrade to approximately 680 degrees Centigrade, to reduce cooling stresses in said semiconductor device.
Claim 18
Independent Claim
180 words
A method for making a semiconductor device having an increased field inversion threshold voltage and also have improved electrical parameters including reduced PN junction reverse leakage current and reduced electrical noise, wherein said semiconductor device has been subjected to at least one high temperature step including forming an oxide on a layer of semiconductor, said method comprising the further steps of: (a) causing an inert gas to flow past said semiconductor; (b) ramping the temperature of said semiconductor device from the temperature of said high temperature step to a temperature in the range from 600 to 950 degrees Centigrade; (c) maintaining said semiconductor device at said temperature in the range from 600 to 950 degrees Centigrade; (d) causing an oxidizing gas to flow past said semiconductor device; (e) causing said oxidizing gas to stop flowing past said semiconductor device; (f) reducing the temperature of said semiconductor device; (g) causing helium to flow past said semiconductor (h) maintaining said semiconductor device at a temperature in the range from 300 to 500 degrees Centigrade; and (i) stopping the flow of said helium.
Claim 19
Independent Claim
180 words
A method for making a semiconductor device having an increased field inversion threshold voltage and also have improved electrical parameters including reduced PN junction reverse leakage current and reduced electrical noise, wherein said semiconductor device has been subjected to at least one high temperature step including forming an oxide on a layer of semiconductor, said method comprising the further steps of: (a) causing an inert gas to flow past said semiconductor; (b) ramping the temperature of said semiconductor device from the temperature of said high temperature step to a temperature in the range from 600 to 950 degrees Centigrade; (c) maintaining said semiconductor device at said temperature in the range from 600 to 950 degrees Centigrade; (d) causing an oxidizing gas to flow past said semiconductor device; (e) causing said oxidizing gas to stop flowing past said semiconductor device; (f) reducing the temperature of said semiconductor device; (g) causing helium to flow past said semiconductor (h) maintaining said semiconductor device at a temperature in the range from 300 to 500 degrees Centigrade; and (i) stopping the flow of said helium.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-05-14 | 1982-11-13 | 1983-05-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-05-14 | 1986-11-13 | 1987-05-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-05-14 | 1990-11-13 | 1991-05-15 | $7700.00 | Window Closed / Lapsed |