Color-neutral, solar-selective, heat-reflecting coating for glass panes

Claim 2

An insulating glass pane consisting essentially of a glass substrate and a selective coating with high color neutrality, high solar transmissivity, low K-value and high stability on an outer surface of said substrate, said coating comprising a pigment component and a carrier component and consisting of an electrically conductive layer having very small, transparent, non-conductive discrete dielectric zones embedded therein.

Claim 3

An insulating glass pane of claim 1, where the absorption coefficient of the carrier component is equal to the refractive index of the pigment component over a broad wavelength range of the solar spectrum including 0.5 μm.

Claim 4

An insulating glass pane of claim 1, where the diameters of the dielectric zones embedded in the conductive layer are smaller than the electrically conductive layer thickness and smaller than the shortest light wavelength.

Claim 5

An insulating glass pane of claim 1, where the volume fraction of the dielectric zones is at least 50% of the coating volume.

Claim 6

An insulating glass pane of claim 1, where the dielectric zones are spherical.

Claim 7

An insulating glass pane of claim 1, where the dielectric zones are needle-shaped and their longitudinal axes are perpendicular to the surface of the electrically conductive layer.

Claim 8

An insulating glass pane of claim 1, where the carrier component has an absorption coefficient between 1 and 2.5 in the solar system at substantially λ=0.5 μm, and the refractive index of the carrier component is not greater than 1.

Claim 9

An insulating glass pane of claim 1, where the pigment component is also transmissive in the infrared range at about λ=10 μm; K p =0.

Claim 10

An insulating glass pane of claim 1, where the refractive index of the coating is between 1 and 1.5.

Claim 11

An insulating glass pane of claim 1, where a metal with a relatively small refractive index in the solar range selected from the group consisting of gold, silver, copper, aluminum, magnesium, yttrium and zirconium, is used as the carrier component.

Claim 12

An insulating glass pane of claim 1, where an intermetallic compound of the alkali or alkaline earth metals is used as the carrier component.

Claim 13

An insulating glass pane of claim 1, where the pigment component is a semiconductor which is transparent in the visible and in the infrared range selected from the group consisting of SnO 2 and In 2 O 3 .

Claim 14

An insulating glass pane of claim 1, where the pigment component is selected from the group consisting of air, plastic, alkali metal halides and alkaline earth metal halides which are transparent in the visible and in the infrared range.

Claim 15

A process for the production of an insulating glass pane of claim 1, which comprises coating a surface of a glass substrate with a thin layer of a mixture of two metals, and selectively oxidizing one metal component.

Claim 16

A process of claim 14, where said metal component is oxidized by exposure to the air.

Claim 17

A process of claim 14, where said metal component is oxidized by a heat treatment.

Claim 18

A process of claim 14, where said mixture of metals is a metal alloy and said one metal component is oxidized by exposure to the air.

Claim 19

A process of claim 17, where said one metal component is oxidized by a heat treatment.

Claim 20

A process of claim 14, where said glass substrate is coated by cathode sputtering, and said coating is subjected to a selective reaction of one metal component by plasma conversion in a gaseous compound selected from the group consisting of fluorine, nitrogen and boron compounds, whereby discrete transparent dielectric zones are formed.

Claim 21

A process of claim 14, which comprises coating a glass substrate with a thin layer of a mixture of two metal compounds of different thermal stability and different particle size, and subsequently selectively reducing one mixture component to the free metal by a reducing heat treatment.

Claim 22

A process of claim 14, which comprises coating a glass substrate with a thin layer of a mixture of discrete particles of a first metal and a suboxide of a second metal and subjecting said coating to partial disproportioning of its components by a subsequent heat treatment, whereby said suboxide is converted into a stable, high-valenced, non-conductive and transparent oxide, and at the same time a conductive compound of said first metal with said second metal is formed which joins the previously separate metal particles conductively with each other.