Cermet varistors
Assignee: Allen Bradley Co LLC
•
Filing: 1975-10-24
•
Granted: 1977-08-09
•
Expires: 1995-10-24
Abstract
Abstract The cermet varistors have electrodes applied to an improved varistor composition which includes a semi-conductive material having zinc oxide in admixture with at least one metal oxide selected from the group consisting of chromium oxide, cobalt oxide and manganese oxide and includes a glass matrix. The glass matrix is a borosilicate glass with at least one metal oxide selected from the group consisting of cobalt oxide and manganese oxide. The improved compositions are used in varistors of both the thick film and bulk types, the resulting varistors having enhanced device characteristics, particularly high exponents of nonlinearity.
Inventors
- 👤 Allan Kouchich
- 👤 George W. Taylor
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 21:53
CPC Classifications
H; H01; H01C; H01C7/00; H01C7/10; H01C7/1006; C; C03; C03C; C03C3/00; C03C3/04; C03C3/062; C03C3/064; C03C8/00; C03C8/14; C03C2207/00; C03C2207/08
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
180 words
A varistor having a nonlinear current-voltage characteristic defined by the relation I = (V/C).sup.α where I is the current flowing through the varistor, V is the voltage across the varistor, C is a constant proportional to the varistor, and α is a constant > 1 and is a measure of the nonlinearity of the varistor, said varistor having an α value in excess of 10, comprising: an inert substrate; a thick film associated with said inert substrate comprising a varistor composition consisting essentially of from about 75.0 to about 92.0 weight percent of a semi-conductive material and from about 25.0 to about 8.0 weight percent of glass matrix; said semi-conductive material consisting predominantly of zinc oxide in admixture with a small amount of at least one metal oxide selected from the group consisting of chromium oxide, cobalt oxide and manganese oxide; said glass matrix consisting primarily of a borosilcate glass with, as an additive, at least one metal oxide selected from the group consisting of cobalt oxide and manganese oxide; and a pair of electrodes applied to said thick film.
Claim 2
Dependent Claim
180 words
A varistor having a nonlinear current-voltage characteristic defined by the relation I = (V/C).sup.α where I is the current flowing through the varistor, V is the voltage across the varistor, C is a constant proportional to the varistor, and α is a constant > 1 and is a measure of the nonlinearity of the varistor, said varistor having an α value in excess of 10, comprising: an inert substrate; a thick film associated with said inert substrate comprising a varistor composition consisting essentially of from about 75.0 to about 92.0 weight percent of a semi-conductive material and from about 25.0 to about 8.0 weight percent of glass matrix; said semi-conductive material consisting predominantly of zinc oxide in admixture with a small amount of at least one metal oxide selected from the group consisting of chromium oxide, cobalt oxide and manganese oxide; said glass matrix consisting primarily of a borosilcate glass with, as an additive, at least one metal oxide selected from the group consisting of cobalt oxide and manganese oxide; and a pair of electrodes applied to said thick film.
Claim 3
Dependent Claim
29 words
The varistor as recited in claim 1, wherein said borosilicate glass consists essentially of one member selected from the group consisting of bismuth borosilicate glass and lead borosilicate glass.
Claim 4
Dependent Claim
33 words
The varistor as recited in claim 1, wherein said varistor composition is disposed on said inert substrate and said electrodes are applied to said varistor composition on its surface opposite said inert substrate.
Claim 5
Dependent Claim
26 words
The varistor as recited in claim 1, wherein said varistor composition is interposed between said electrodes, one of said electrodes being disposed on said inert substrate.
Claim 6
Dependent Claim
66 words
A varistor as recited in claim 1, wherein said semi-conductive material approximately comprises 98.8 weight percent zinc oxide, 0.5 weight percent chromium oxide, 0.2 weight percent cobalt oxide, and 0.5 weight percent manganese oxide; and said glass matrix approximately comprises 23.4 mole percent boron trioxide, 19.8 mole percent bismuth oxide, 27.2 mole percent silicon dioxide, 15.9 mole percent cobalt oxide, and 13.7 mole percent manganese oxide.
Claim 7
Dependent Claim
28 words
The varistor as recited in claim 1, wherein said semi-conductive material comprises particles having a size within the range of from about 0.1 microns to about 10 microns.
Claim 8
Dependent Claim
175 words
A varistor having a nonlinear current-voltage characteristic defined by the relation I = (V/C).sup.α where I is the current flowing through the varistor, V is the voltage across the varistor, C is a constant proportional to the varistor, and α is a constant > 1 and is a measure of the nonlinearity of the varistor, said varistor having an α value in excess of 10, comprising: a bonded mass of particles comprising a varistor composition consisting essentially of from about 90.0 to about 99.0 weight percent of a semi-conductive material and from about 10.0 to about 1.0 weight percent of a glass matrix; said semi-conductive material consisting predominantly of zinc oxide in admixture with a small amount of at least one metal oxide selected from the group consisting of chromium oxide, cobalt oxide and manganese oxide; said glass matrix consisting primarily of a borosilicate glass with, as an additive, at least one metal oxide selected from the group consisting of cobalt oxide and manganese oxide; and a pair of electrodes applied to said bonded mass.
Claim 9
Dependent Claim
175 words
A varistor having a nonlinear current-voltage characteristic defined by the relation I = (V/C).sup.α where I is the current flowing through the varistor, V is the voltage across the varistor, C is a constant proportional to the varistor, and α is a constant > 1 and is a measure of the nonlinearity of the varistor, said varistor having an α value in excess of 10, comprising: a bonded mass of particles comprising a varistor composition consisting essentially of from about 90.0 to about 99.0 weight percent of a semi-conductive material and from about 10.0 to about 1.0 weight percent of a glass matrix; said semi-conductive material consisting predominantly of zinc oxide in admixture with a small amount of at least one metal oxide selected from the group consisting of chromium oxide, cobalt oxide and manganese oxide; said glass matrix consisting primarily of a borosilicate glass with, as an additive, at least one metal oxide selected from the group consisting of cobalt oxide and manganese oxide; and a pair of electrodes applied to said bonded mass.
Claim 10
Dependent Claim
66 words
A varistor as recited in claim 7, wherein said semi-conductive material approximately comprises 98.8 weight percent zinc oxide, 0.5 weight percent chromium oxide, 0.2 weight percent cobalt oxide, and 0.5 weight percent manganese oxide; and said glass matrix approximately comprises 23.4 mole percent boron trioxide, 19.8 mole percent bismuth oxide, 27.2 mole percent silicon dioxide, 15.9 mole percent cobalt oxide, and 13.7 mole percent manganese oxide.
Claim 11
Dependent Claim
29 words
The varistor as recited in claim 7, wherein said borosilicate glass consists essentially of one member selected from the group consisting of bismuth borosilicate glass and lead borosilicate glass.
Claim 12
Dependent Claim
28 words
The varistor as recited in claim 7, wherein said semi-conductive material comprises particles having a size within the range of from about 0.1 microns to about 10 microns.
References Cited (Backward Citations)
US3669907A
Cited
US3477055A
Cited
US3598763A
Cited
US3868334A
Cited
US3725836A
Cited
US3928242A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-08 | 1981-02-07 | 1981-08-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-08 | 1985-02-07 | 1985-08-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-08 | 1989-02-07 | 1989-08-09 | $7700.00 | Window Closed / Lapsed |