Thick crystalline films on foreign substrates
Assignee: Massachusetts Institute of Technology
•
Filing: 1983-05-24
•
Granted: 1986-03-18
•
Expires: 2003-05-24
Abstract
Abstract To achieve a uniform texture, large crystalline grains or, in some cases, a single crystalline orientation in a thick (>1 μm) film on a foreign substrate, the film is formed so as to be thin (<1 μm) in a certain section. Zone-melting recrystallization is initiated in the thin section and then extended into the thick section. The method may employ planar constriction patterns of orientation filter patterns.
Inventors
- 👤 Henry I. Smith
- 👤 Harry A. Atwater
- 👤 Michael W. Geis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 03:48
CPC Classifications
C; C30; C30B; C30B13/00; C30B13/34; C30B29/00; C30B29/60; C30B29/64; Y; Y10; Y10S; Y10S438/00; Y10S438/973
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
110 words
A method of forming a thick crystalline film with large, uniform-textured, grains and aligned crystallographic orientations upon a substrate, the method comprising: (a) depositing a film to be processed upon the surface of the substrate; (b) establishing a pattern of vertical constriction in a portion of the film; the pattern being characterized by a thin section and a section of graduated thickness connecting the thin section to the rest of the deposited film; and (c) heating the film sequentially from the thin section to the rest of the film to induce recrystallization, whereby the orientation of the thin section will be passed on to the bulk of the deposited film.
Claim 2
Independent Claim
110 words
A method of forming a thick crystalline film with large, uniform-textured, grains and aligned crystallographic orientations upon a substrate, the method comprising: (a) depositing a film to be processed upon the surface of the substrate; (b) establishing a pattern of vertical constriction in a portion of the film; the pattern being characterized by a thin section and a section of graduated thickness connecting the thin section to the rest of the deposited film; and (c) heating the film sequentially from the thin section to the rest of the film to induce recrystallization, whereby the orientation of the thin section will be passed on to the bulk of the deposited film.
Claim 3
Dependent Claim
21 words
The method of claim 1 wherein the step of depositing the film further comprises depositing the film by chemical vapor deposition.
Claim 4
Dependent Claim
24 words
The method of claim 1 wheren the step of establishing the pattern in the film further comprises photolithographically etching a pattern in the film.
Claim 5
Dependent Claim
22 words
The method of claim 1 wherein the step of heating the film sequentially further comprises passing a heated zone through the film.
Claim 6
Dependent Claim
24 words
The method of claim 1 wherein the method further comprises covering the film with an encapsulation layer after the vertical constriction pattern is established.
Claim 7
Dependent Claim
29 words
The method of claim 1 wherein the method further comprises establishing a planar constriction pattern, as well as a vertical constriction pattern, in the thin section prior to heating.
References Cited (Backward Citations)
US4196041A
Cited
US4323417A
Cited
JPS571225A
Cited
US4383883A
Cited
US4473433A
Cited
US4479846A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-03-17 | 1989-09-16 | 1990-03-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-03-17 | 1993-09-16 | 1994-03-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-03-17 | 1997-09-16 | 1998-03-18 | $7700.00 | Window Closed / Lapsed |