Doped glass and process for making

Claim 1

An improved method for making a solid phase rod from which glass fibers having a refractive index profile having a uniform paraboloid configuration for use as light waveguides in optical communicators technology are formable, said method comprising the sequential steps of: (A) heating an alkali-free silica glass tube which has been initially interiorly cleaned by a gas stream comprised of oxygen and sulfur hexafluoride with a narrow oxyhydrogen gas burner while simultaneously first passing at a flow rate of from about 200 to 2000 centimeters per minute through said tube a first gaseous composition comprised of silicon tetrachloride, oxygen, and at least one fluorine containing gaseous compound, said heating being conducted by moving said burner along the exterior of said tube in the direction of flow through said tube of said gaseous composition at a moving rate of from about 5 to 25 centimeters per minute, the interrelationship between said heating, said moving, said first passing, and said first gaseous composition being such that in front of the zone of heating produced by said burner a precipitation of silica glass powder doped with fluorine occurs which powder is clear-melted onto the interior wall portions of said tube in such zone of heating, (B) repeating step (A) at least twice, (C) secondly, passing at a flow rate of from about 200 to 2000 centimeters per minute through said tube a second gaseous composition containing higher relative weight percentages of fluorine than were present in said first gaseous composition, said fluorine being in the initial form of at least one fluorine containing gaseous compound, said second gaseous composition further including silicon tetrachloride, oxygen, and at least one further chloride of elements selected of the group consisting of Ge, Al, Ti, Ta, Sn, Nb, Zr, Yb, La, P, B, and Sb, (D) repeating said step (C) at least twice, each such repeat being conducted with a gaseous composition having a higher fluorine content, (E) thirdly, passing at a flow rate of from about 200 to 2000 centimeters per minute through said, tube a final gaseous composition comprised of sulfur hexafluoride while said moving is continued at a moving rate of from about 2 to 45 centimeters per minute, the interrelationship between said heating, said moving, said third passing, and said final gaseous composition being such that a cleaning of said interior wall portions results, (F) repeating said step (E) at least once, (G) moving said burner along resulting tube at a temperature sufficient to melt said resulting tube into a solid rod.

Claim 4

A method for making a silica glass having a predetermined refractive index gradient profile said glass being comprised of a plurality of successive glass layers, said method comprising the steps of: successively depositing at glass forming temperatures each of said layers upon a substrate from a gas phase containing oxygen and at least one gaseous silicon compound from which silica glass is produced, introducing into said gas phase for each of said layers a gaseous dopant composition so as to produce in each said layer as so deposited a desired refractive index, said dopant composition being comprised of: a fluorine containing compound selected from the group consisting of sulfur fluorides, nitrogen fluorides, fluorohydrocarbons, fluorine containing halogenated hydrocarbons, and carbonyl fluoride, and at least one other dopant compound containing an element selected from the group consisting of Ga, Al, Ti, Ta, Sn, Nb, Zr, Yb, La, P, B, Sb, and mixtures thereof, and gradually increasing in said dopant composition as so introduced for each said layer the relative amount of said other dopant compound so that the refractive index profile of such successive glass layers changes from layer to layer in accordance with a desired refractive index gradient profile while holding constant the amount of said fluorine containing compound.

Claim 5

A method for making a silica glass having a predetermined refractive index gradient profile said glass being comprised of a plurality of successive glass layers, said method comprising the steps of: successively depositing at glass forming temperatures each of said layers upon a substrate from a gas phase containing oxygen and at least one gaseous silicon compound from which silica glass is produced, introducing into said gas phase for each of said layers a gaseous dopant composition so as to produce in each said layer as so deposited a desired refractive index, said dopant composition being comprised of: a fluorine containing compound selected from the group consisting of sulfur fluorides, nitrogen fluorides, fluorohydrocarbons, fluorine containing halogenated hydrocarbons, and carbonyl fluoride, and at least one other dopant compound containing an element selected from the group consisting of Ga, Al, Ti, Ta, Sn, Nb, Zr, Yb, La, P, B, Sb, and mixtures thereof, and gradually increasing in said dopant composition as so introduced for each said layer the relative amount of said other dopant compound so that the refractive index profile of such successive glass layers changes from layer to layer in accordance with a desired refractive index gradient profile while holding constant the amount of said fluorine containing compound.

Claim 15

A method for making a silica glass having a predetermined refractive index gradient profile said glass being comprised of a plurality of successive glass layers, said method comprising the steps of: successively depositing at glass forming temperatures each of said layers upon from a gas phase containing oxygen and at least one gaseous silicon compound from which silica glass is produced, introducing into said gas phase for each of said layers a gaseous dopant composition so as to produce in each said layer as so deposited a desired refractive index, said dopant composition being comprised of: a fluorine containing compound selected from the group consisting of sulfur fluorides, nitrogen fluorides, fluorohydrocarbons, fluorine containing halogenated hydrocarbons, and carbonyl fluoride, and at least one other dopant compound containing an element selected from the group consisting of Ga, Al, Ti, Ta, Sn, Nb, Zr, Yb, La, P, B, Sb, and mixtures thereof, and gradually decreasing in said dopant composition as so introduced for each said layer the relative amount of said other dopant compound so that the refractive index profile of such successive glass layers changes from layer to layer in accordance with a desired refractive index gradient profile while holding constant the amount of said fluorine containing compound.

Claim 16

A method for making a silica glass having a predetermined refractive index gradient profile said glass being comprised of a plurality of successive glass layers, said method comprising the steps of: successively depositing at glass forming temperatures each of said layers upon from a gas phase containing oxygen and at least one gaseous silicon compound from which silica glass is produced, introducing into said gas phase for each of said layers a gaseous dopant composition so as to produce in each said layer as so deposited a desired refractive index, said dopant composition being comprised of: a fluorine containing compound selected from the group consisting of sulfur fluorides, nitrogen fluorides, fluorohydrocarbons, fluorine containing halogenated hydrocarbons, and carbonyl fluoride, and at least one other dopant compound containing an element selected from the group consisting of Ga, Al, Ti, Ta, Sn, Nb, Zr, Yb, La, P, B, Sb, and mixtures thereof, and gradually decreasing in said dopant composition as so introduced for each said layer the relative amount of said other dopant compound so that the refractive index profile of such successive glass layers changes from layer to layer in accordance with a desired refractive index gradient profile while holding constant the amount of said fluorine containing compound.