USRE30883E
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of producing synthetic quartz glass
Assignee: Heraeus Quarzglas GmbH and Co KG
•
Filing: 1980-02-13
•
Granted: 1982-03-16
•
Expires: 2000-02-13
Abstract
Abstract An improvement in a method for producing a synthetic hydroxyl ion-free quartz glass wherein a hydrogen free silicon compound is heated in a hydrogen-free gas stream while the gas stream is passed through an induction coupled plasma burner, the gas stream containing elemental and/or bound oxygen and the oxidation product is deposited on a refractory support as a vitreous mass, the improvement lying in including in the gas stream a gaseous hydrogen-free, thermally decomposable compound which yields fluorine in an amount of at least 500 gms. per kilogram of silica to be produced; an apparatus for producing a synthetic OH ion-free quartz glass comprising an induction coupled plasma burner which burner has disposed thereabout 3 concentric quartz glass tubes disposed in stepped configuration of which the outermost tube is the longest and the innermost tube is the shortest. The apparatus includes means for passing through the innermost tube a hydrogen-free gas stream containing elemental oxygen and/or bound oxygen together with a gaseous hydrogen free thermally decomposable compound which yields fluorine. The apparatus further contains means for passing a separating gas such as oxygen through the space defined by the innermost tube and the middle tube and the middle tube and the outermost tube.
Inventors
- 👤 Karlheinz Rau
- 👤 Fritz Simmat
- 👤 Albert Muhlich
- 👤 Norbert Treber
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 18:34
CPC Classifications
C; C03; C03C; C03C3/00; C03C3/04; C03C3/06; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/01413; C03B37/0142; C03B37/01426; C03B37/018; C03B37/01807; C03B37/01815; C03B37/01823; C03B2201/00; C03B2201/06; C03B2201/07; C03B2201/075; C03B2201/08; C03B2201/12; C03B2207/00; C03B2207/80; C03B2207/85; C03C2201/00; C03C2201/06; C03C2201/08; C03C2201/12; C03C2203/00; C03C2203/40
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
140 words
A method for forming a coating of a fluorine containing synthetic OH ion-free quartz glass on a refractory support which comprises passing a hydrogen-free silicon compound, gaseous oxygen and vaporous CCl 2 F 2 , CClF 3 or CF 4 in a hydrogen free gas stream through an induction coupled plasma burner whereby said hydrogen-free silicon compound reacts with said oxygen to form synthetic OH ion-free quartz glass, the amount of said CCl 2 F 2 , CClF 3 or CF 4 , passed through said burner, being sufficient to yield .[.a.]. fluorine .[.content in the quartz glass.]. in an amount of at least 500 grams per kg of quartz to be produced whereby there is formed a fluorine-doped synthetic OH ion-free quartz glass and depositing said fluorine-doped synthetic OH ion-free quartz glass as a coating on a refractory support.
Claim 2
Independent Claim
140 words
A method for forming a coating of a fluorine containing synthetic OH ion-free quartz glass on a refractory support which comprises passing a hydrogen-free silicon compound, gaseous oxygen and vaporous CCl 2 F 2 , CClF 3 or CF 4 in a hydrogen free gas stream through an induction coupled plasma burner whereby said hydrogen-free silicon compound reacts with said oxygen to form synthetic OH ion-free quartz glass, the amount of said CCl 2 F 2 , CClF 3 or CF 4 , passed through said burner, being sufficient to yield .[.a.]. fluorine .[.content in the quartz glass.]. in an amount of at least 500 grams per kg of quartz to be produced whereby there is formed a fluorine-doped synthetic OH ion-free quartz glass and depositing said fluorine-doped synthetic OH ion-free quartz glass as a coating on a refractory support.
Claim 3
Dependent Claim
66 words
A method according to claim 1 wherein said refractory support is quartz glass having a rod shape and said synthetic OH ion-free quartz glass formed by reaction of said hydrogen-free silicon compound and said oxygen is deposited thereon, the refractive index of the refractory support being increased by refractive index raising metal ions, the refractive index of said support decreasing with the distance from its axes.
Claim 4
Dependent Claim
48 words
A process according to claim 1 wherein a sufficient amount of fluorine is passed through said plasma burner together with said hydrogen-free silicon compound and elemental and/or bound oxygen, that the fluorine containing synthetic OH ion-free quartz glass has a refractory index n D of 1.457 to 1.435.
Claim 5
Dependent Claim
38 words
A method according to claim 1 wherein said refractory support is in the form of a rod shape and the resultant synthetic OH ion-free quartz glass is deposited in the form of a sleeve on said rod-shaped support.
Claim 6
Dependent Claim
19 words
A method according to claim 1 wherein CCl 2 F 2 is admixed in vapor form with said oxygen.
Claim 7
Dependent Claim
18 words
A method according to claim 1 wherein said CClF 3 is admixed in vapor form with said oxygen.
Claim 8
Dependent Claim
18 words
A method according to claim 1 wherein said CF 4 is admixed in vapor form with said oxygen.
Claim 9
Dependent Claim
33 words
A method according to claim 1 wherein the amount of said CCl 2 F 2 , CClF 3 or CF 4 is increased as the synthetic OH ion-free quartz glass increases in thickness.
Claim 10
Dependent Claim
32 words
A method according to claim 1 wherein said hydrogen-free silicon compound is selected from the group consisting of SiCl 4 , SiCl 3 F, SiCl 2 F 2 and SiClF 3 .
Claim 11
Dependent Claim
37 words
A method according to claim 9 wherein said vaporous CCl 2 F 2 , CClF 3 or CF 4 is thermally decomposed in said plasma burner at a temperature in the range of 1800° to 2600° C.
Claim 12
Dependent Claim
33 words
A method according to claim 10 wherein said CCl 2 F 2 , CClF 3 or CF 4 is thermally decomposed in said plasma burner at a temperature between 1850° and 2000° C.
Claim 13
Dependent Claim
45 words
A method according to claim 9 wherein the weight relationship of the fluorine in said vapor CClF 2 , CClF 3 or CF 4 to silicon in said hydrogen-free silicon compound is in the range of 50 to 800 grams fluorine per kg of silicon.
References Cited (Backward Citations)
US3275408A
Cited
US3659915A
Cited
US3843229A
Cited
DE2247307A1
Cited
US3778132A
Cited
FR2253723A1
Cited
JPS5156641A
Cited
US3981707A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-03-15 | 1985-09-14 | 1986-03-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-03-15 | 1989-09-14 | 1990-03-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-03-15 | 1993-09-14 | 1994-03-16 | $7700.00 | Window Closed / Lapsed |