Method of preparing a foreproduct for the production of an optical lightconductor
Assignee: Heraeus Quarzschmelze GmbH
•
Filing: 1976-08-24
•
Granted: 1977-08-30
•
Expires: 1996-08-24
Abstract
Abstract There is disclosed a process for preparing a foreproduct useful in the production of an optical self-focusing lightconductor in which the index of refraction of the lightconductor diminishes with increasing distance from the conductor axis such that, when plotted against the conductor diameter, the refractive index curve is parabolic and the apex of the parabola lies over the center of the conductor diameter wherein a plurality of layers of doped silica are deposited on a cylindrical support, the layers being formed of a mixture of a vaporous silicon compound and a vaporous doping agent at elevated temperature. The invention involves depositing at least one layer of undoped silica between layers of doped silica and following each deposition of each doped or undoped silica layer by heating step in which the material is heated to a temperature of at least 900° C to vitrify the same. Each layer is deposited in a thickness ranging from 0.1 to 20 μm.
Inventors
- 👤 Karlheinz Rau
- 👤 Albert Muhlich
- 👤 Fritz Simmat
- 👤 Norbert Treber
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 22:56
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/018; C03B37/01853; C03B2203/00; C03B2203/10; C03B2203/22; Y; Y10; Y10S; Y10S65/00; Y10S65/15; Y10S65/16
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
232 words
In a process for preparing a foreproduct useful in the production of an optical, self-focusing lightconductor in which the index of refraction of the lightconductor material diminishes with increasing distance from the conductor axis such that, when plotted against the conductor diameter, the refractive index curve is parabolic and the apex of the parabola lies over the center of the conductor diameter wherein a plurality of layers of doped silica are deposited on a cylindrical support, said layers being formed of a mixture of a vaporous silicon compound and a vaporous doping agent at elevated temperature, the improvement which comprises depositing at least one layer of undoped silica between layers of doped silica and following each deposition of each doped or undoped silica layer heating the deposited silica to a temperature of at least 900° C. to vitrify the same, each layer being deposited in a thickness ranging from 0.1 to 20 μm, such that the number of layers of undoped silica which are to be deposited on a layer of doped silica before another layer of doped silica is deposited increases with increasing distance from the lightconductor axis if a doping agent is used which produces an increase in the refractive index of vitreous silica and decreases with increasing distance from the lightconductor axis if a doping agent is used which produces a decrease in the refractive index of vitreous silica.
Claim 2
Dependent Claim
232 words
In a process for preparing a foreproduct useful in the production of an optical, self-focusing lightconductor in which the index of refraction of the lightconductor material diminishes with increasing distance from the conductor axis such that, when plotted against the conductor diameter, the refractive index curve is parabolic and the apex of the parabola lies over the center of the conductor diameter wherein a plurality of layers of doped silica are deposited on a cylindrical support, said layers being formed of a mixture of a vaporous silicon compound and a vaporous doping agent at elevated temperature, the improvement which comprises depositing at least one layer of undoped silica between layers of doped silica and following each deposition of each doped or undoped silica layer heating the deposited silica to a temperature of at least 900° C. to vitrify the same, each layer being deposited in a thickness ranging from 0.1 to 20 μm, such that the number of layers of undoped silica which are to be deposited on a layer of doped silica before another layer of doped silica is deposited increases with increasing distance from the lightconductor axis if a doping agent is used which produces an increase in the refractive index of vitreous silica and decreases with increasing distance from the lightconductor axis if a doping agent is used which produces a decrease in the refractive index of vitreous silica.
Claim 3
Dependent Claim
21 words
A process as claimed in claim 1 wherein initially upon said cylindrical support there is deposited a layer of undoped silica.
Claim 4
Dependent Claim
17 words
A process as claimed in claim 1 wherein said cylindrical support is one of a vitreous material.
Claim 5
Dependent Claim
32 words
A process as claimed in claim 1 wherein following the deposition of each doped or undoped layer the deposited material is heated to a vitrifying temperature within 3600 seconds following the deposition.
Claim 6
Dependent Claim
22 words
A process as claimed in claim 1 wherein the composition of the doped silica layer is maintained constant for all doped layers.
Claim 7
Dependent Claim
41 words
A process as claimed in claim 1 wherein the deposition conditions are maintained constant from the deposition of one layer of doped silica through the deposition of a layer of undoped silica to the deposition of another layer of doped silica.
Claim 8
Dependent Claim
25 words
A process as claimed in claim 1 wherein the layers are deposited on the inside wall of a tubular support maintained at the depositing temperature.
Claim 9
Dependent Claim
28 words
A process as claimed in claim 7 wherein said tubular support is rotated during deposition of the silica layers or during the heat treatment at over 900° C.
Claim 10
Dependent Claim
26 words
A process as claimed in claim 4 wherein the heat treatment of the deposited silica layers following deposition is effected at a temperature above 1500° C.
Claim 11
Dependent Claim
74 words
A process as claimed in claim 7 wherein on the inside wall of the tubular support, prior to the depositing of the series of layers consisting of doped and undoped silica, a layer of vitreous material is deposited whose refractive index is only high enough for it to be usable as the jacket of an optical photoconductor where core material is produced by the deposition of a sequence of layers followed by heat treatment.
Claim 12
Dependent Claim
29 words
A process as claimed in claim 10 wherein at least one layer of doped silica in its vitreous state has a refractive index greater or less than quartz glass.
Claim 13
Dependent Claim
22 words
A process as claimed in claim 10 wherein the doped silica layer is doped with an agent which reduces the refractive index.
Claim 14
Dependent Claim
16 words
A process as claimed in claim 12 wherein said agent is a boron or fluorine compound.
Claim 15
Dependent Claim
22 words
A process as claimed in claim 1 wherein the doped silica layer is doped with an agent which increases the refractive index.
Claim 16
Dependent Claim
19 words
A process as claimed in claim 14 wherein said agent is a phosphorus, germanium, aluminum, gallium or titanium compound.
References Cited (Backward Citations)
US3843229A
Cited
US3823995A
Cited
US3847585A
Cited
US3877912A
Cited
US4000416A
Cited
US3980459A
Cited
US3982916A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-29 | 1981-02-28 | 1981-08-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-29 | 1985-02-28 | 1985-08-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-29 | 1989-02-28 | 1989-08-30 | $7700.00 | Window Closed / Lapsed |