Uniformly pigmented, low shrinking polyester molding compositions

Claim 2

A curable molding composition containing: (a) a polyester resin that is suitable for use in molding and which comprises the reaction product of an olefinically unsaturated dicarboxylic acid or anhydride and a polyol; (b) an olefinically unsaturated monomer that is copolymerizable with said polyester resin; (c) a thickening agent comprising an oxide or hydroxide of a metal or Group I, II, or III of the Periodic Table; (d) a pigment; (e) a carboxylated vinyl acetate polymer low profile additive having a molecular weight within the range of from about 10,000 to about 250,000; and (f) a surface active compound that is employed in an amount sufficient to enhance the uniformity of the pigmentation of the cured composite produced from said curable molding composition.

Claim 3

The curable molding composition of claim 1 wherein the olefinically unsaturated monomer is styrene.

Claim 4

The curable molding composition of claim 2 wherein the thickening agent is magnesium oxide or magnesium hydroxide.

Claim 5

The curable molding composition of claim 1 wherein the surface active compound is a member selected from the group consisting of: (a) a sulfonic acid or an alkali metal, alkaline earth metal, or ammonium salt thereof; (b) an ethylene oxide adduct of a long chain aliphatic alcohol; (c) a polyoxyethylene-polyoxypropylene block copolymer; (d) polyglycerol oleate; (e) ethoxylated sorbitan monooleate; (f) sodium 2-caprylic (ethyl beta oxipropanoic acid)imidazoline; (g) ethoxylated alkylguanidine amine complex; (h) sodium and methyl-N-long chain aliphatic taurate; (i) sodium isethionate coconut ester; (j) ethoxylated long chain alkylphenol; (k) N-long chain aliphatic quaternary ammonium halide; and (l) polydimethylsiloxane oil.

Claim 6

The curable molding composition of claim 1 wherein the surface active compound is sodium dodecylbenzene sulfonate.

Claim 7

The curable molding composition of claim 1 wherein the surface active compound is a sulfonic acid or an alkali metal, alkaline earth metal, or ammonium salt thereof.

Claim 8

The curable molding composition of claim 5 wherein the carboxylated vinyl acetate polymer low profile additive is a vinyl acetate/maleic acid copolymer.

Claim 9

The curable molding composition of claim 6 wherein the carboxylated vinyl acetate polymer low profile additive is a vinyl acetate/maleic acid copolymer.

Claim 10

The curable molding composition of claim 7 wherein the olefinically unsaturated monomer is styrene and wherein the thickening agent is magnesium oxide or magnesium hydroxide.

Claim 11

The curable molding composition of claim 8 wherein the olefinically unsaturated monomer is styrene and wherein the thickening agent is magnesium oxide or magnesium hydroxide.

Claim 12

A curable molding composition containing: (a) a polyester resin that is suitable for use in molding and which comprises the reaction product of an olefinically unsaturated dicarboxylic acid or anhydride and a polyol; (b) an olefinically unsaturated monomer that is copolymerizable with said polyester resin; (c) a thickening agent comprising an oxide or hydroxide of a metal of Group I, II, or III of the Periodic Table; (d) a pigment; (e) a low profile additive consisting essentially of a vinyl acetate/maleic acid copolymer.

Claim 13

A curable molding composition containing: (a) a polyester resin that is suitable for use in molding and which comprises the reaction product of an olefinically unsaturated dicarboxylic acid or anhydride and a polyol; (b) an olefinically unsaturated monomer that is copolymerizable with said polyester resin; (c) a thickening agent comprising an oxide or hydroxide of a metal of Group I, II, or III of the Periodic Table; (d) a pigment; (e) a low profile additive consisting essentially of a vinyl acetate/maleic acid copolymer.

Claim 14

The cured composite produced by curing the composition of claim 1.

Claim 15

The cured composite produced by curing the composition of claim 11.

Claim 16

A process for the preparation of a pigmented curable molding composition comprising effecting the mixture of a polyester resin that is suitable for use in molding and which comprises the reaction product of an olefinically unsaturated dicarboxylic acid or anhydride and a polyol, an olefinically unsaturated monomer that is copolymerizable with said polyester resin, a thickening agent comprising an oxide or hydroxide of a metal of Group I, II or III of the Periodic Table, a pigment, a carboxylated vinyl acetate polymer low profile additive having a molecular weight within the range of from about 10,000 to about 250,000, and a surface active compound that is employed in an amount sufficient to enhance the uniformity of the pigmentation of the cured composite produced from said curable molding composition.

Claim 17

A process for the preparation of a pigmented curable molding composition comprising effecting the mixture of a polyester resin that is suitable for use in molding and which comprises the reaction product of an olefinically unsaturated dicarboxylic acid or anhydride and a polyol, an olefinically unsaturated monomer that is copolymerizable with said polyester resin, a thickening agent comprising an oxide or hydroxide of a metal of Group I, II or III of the Periodic Table, a pigment, a carboxylated vinyl acetate polymer low profile additive having a molecular weight within the range of from about 10,000 to about 250,000, and a surface active compound that is employed in an amount sufficient to enhance the uniformity of the pigmentation of the cured composite produced from said curable molding composition.

Claim 18

A process as claimed in claim 14 wherein the carboxylated vinyl acetate polymer low profile additive is a vinyl acetate/maleic acid copolymer.

Claim 19

A process for making a pigmented molded article having a smooth surface which comprises molding at an elevated temperature a pigmented curable molding composition comprising a polyester resin that is suitable for use in molding and which comprises the reaction product of an olefinically unsaturated dicarboxylic acid or anhydride and a polyol, an olefinically unsaturated monomer that is copolymerizable with said polyester resin, a thickening agent comprising an oxide or hydroxide of a metal of Group I, II or III of the Periodic Table, a pigment, a carboxylated vinyl acetate polymer low profile additive having a molecular weight within the range of from about 10,000 to about 250,000, and a surface active compound that is employed in an amount sufficient to enhance the uniformity of the pigmentation of the cured composite produced from said curable molding composition.

Claim 20

A process for making a pigmented molded article having a smooth surface which comprises molding at an elevated temperature a pigmented curable molding composition comprising a polyester resin that is suitable for use in molding and which comprises the reaction product of an olefinically unsaturated dicarboxylic acid or anhydride and a polyol, an olefinically unsaturated monomer that is copolymerizable with said polyester resin, a thickening agent comprising an oxide or hydroxide of a metal of Group I, II or III of the Periodic Table, a pigment, a carboxylated vinyl acetate polymer low profile additive having a molecular weight within the range of from about 10,000 to about 250,000, and a surface active compound that is employed in an amount sufficient to enhance the uniformity of the pigmentation of the cured composite produced from said curable molding composition.

Claim 21

A process as claimed in claim 16 wherein the carboxylated vinyl acetate polymer low profile additive is a vinyl acetate/maleic acid copolymer.

Claim 22

A pigmented molded article having a smooth surface prepared by the process of claim 16.

Claim 23

A pigmented molded article having a smooth surface prepared by the process of claim 17.

Claim 24

A process for the preparation of a pigmented curable molding composition comprising effecting the mixture of a polyester resin that is suitable for use in molding and which comprises the reaction product of an olefinically unsaturated dicarboxylic acid or anhydride and a polyol, an olefinically unsaturated monomer that is copolymerizable with said polyester resin, a thickening agent comprising an oxide or hydroxide of a metal of Group I, II or III of the Periodic Table, a pigment, and a low profile additive comprising a vinyl acetate/maleic acid copolymer.

Claim 25

A process for the preparation of a pigmented curable molding composition comprising effecting the mixture of a polyester resin that is suitable for use in molding and which comprises the reaction product of an olefinically unsaturated dicarboxylic acid or anhydride and a polyol, an olefinically unsaturated monomer that is copolymerizable with said polyester resin, a thickening agent comprising an oxide or hydroxide of a metal of Group I, II or III of the Periodic Table, a pigment, and a low profile additive comprising a vinyl acetate/maleic acid copolymer.

Claim 26

A process for making a pigmented molded article having a smooth surface which comprises molding at an elevated temperature a pigmented curable molding composition comprising a polyester resin that is suitable for use in molding and which comprises the reaction product of an olefinically unsaturated dicarboxylic acid or anhydride and a polyol, an olefinically unsaturated monomer that is copolymerizable with said polyester resin, a thickening agent comprising an oxide or hydroxide of a metal of Group I, II or III of the Periodic Table, a pigment, and a low profile additive comprising a vinyl acetate/maleic acid copolymer.

Claim 27

A process for making a pigmented molded article having a smooth surface which comprises molding at an elevated temperature a pigmented curable molding composition comprising a polyester resin that is suitable for use in molding and which comprises the reaction product of an olefinically unsaturated dicarboxylic acid or anhydride and a polyol, an olefinically unsaturated monomer that is copolymerizable with said polyester resin, a thickening agent comprising an oxide or hydroxide of a metal of Group I, II or III of the Periodic Table, a pigment, and a low profile additive comprising a vinyl acetate/maleic acid copolymer.

Claim 28

A pigmented molded article having a smooth surface prepared by the process of claim 21.