Preparation of interpolymers of alpha-olefins and nonconjugated alpha, omega-dienes
Assignee: Goodyear Tire and Rubber Co
•
Filing: 1982-01-25
•
Granted: 1985-11-05
•
Expires: 2002-01-25
Abstract
Abstract Interpolymers of alpha-olefins and nonconjugated alpha,omega-dienes are prepared by organoaluminum compound-transition metal compound catalysts modified with hexaalkylphosphoric triamides or organophosphate esters.
Inventors
- 👤 Joginder Lal
- 👤 Michael L. Senyek
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 18:41
CPC Classifications
C; C08; C08F; C08F210/00
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
182 words
Vulcanizates of sulfur-vulcanizable interpolymers having improved properties including tensile strength greater than 2000 psi, elongation at break in the range of 400 to 650%, and crosslink density was measured by swelling ratio value, Q of less than 4.0, said interpolymers being obtained by copolymerization of from 95 to 75 mole percent of at least one α-olefin containing from 4 to 12 carbon atoms and 5 to 25 mole percent of at least one α,ω-diene containing at least 8 carbon atoms in the presence of a coordination catalyst prepared from Components (A) an organoaluminum compound, (B) a transition metal compound selected from Group IVB of the Periodic Table, and (C) at least one compound of the general formula: Q=P(XY n ) 3 wherein Q is oxygen or sulfur, P is phosphorous, Y is a hydrocarbyl radical containing from 1 to 20 carbon atoms, and X is oxygen, sulfur or nitrogen, and n is an integer having values of 1 or 2, with the proviso that when X is oxygen or sulfur, then n is 1 and when X is nitrogen, then is 2.
Claim 2
Dependent Claim
182 words
Vulcanizates of sulfur-vulcanizable interpolymers having improved properties including tensile strength greater than 2000 psi, elongation at break in the range of 400 to 650%, and crosslink density was measured by swelling ratio value, Q of less than 4.0, said interpolymers being obtained by copolymerization of from 95 to 75 mole percent of at least one α-olefin containing from 4 to 12 carbon atoms and 5 to 25 mole percent of at least one α,ω-diene containing at least 8 carbon atoms in the presence of a coordination catalyst prepared from Components (A) an organoaluminum compound, (B) a transition metal compound selected from Group IVB of the Periodic Table, and (C) at least one compound of the general formula: Q=P(XY n ) 3 wherein Q is oxygen or sulfur, P is phosphorous, Y is a hydrocarbyl radical containing from 1 to 20 carbon atoms, and X is oxygen, sulfur or nitrogen, and n is an integer having values of 1 or 2, with the proviso that when X is oxygen or sulfur, then n is 1 and when X is nitrogen, then is 2.
Claim 3
Dependent Claim
47 words
The vulcanizates of interpolymers of α-olefins and α,ω-dienes according to claim 1 wherein the α-olefin is chosen from the group consisting of 1-butene, 1-pentene, 1-hexene, 1-heptene, 1-octene, 1-nonene, 1-decene, 1-undecene, and 1-dodecene and the α,ω-diene is chosen from the group consisting of 1,7-octadiene, 1,9-decadiene, 1,11-dodecadiene, and 1,13-tetradecadiene.
Claim 4
Dependent Claim
38 words
The vulcanizates of interpolymers of α-olefins and α,ω-dienes according to claim 1 wherein the Component (C) of the coordination catalyst is selected from the group consisting of hexamethylphosphoric triamide, hexaethylphosphoric triamide, hexamethylthiophosphoric triamide, triethylphosphate, tri-n-butyl phosphate, and S,S,S-trimethylphosphorotrithioate.
Claim 5
Dependent Claim
44 words
The vulcanizates of interpolymers of α-olefins and α,ω-dienes according to claim 1 wherein the molar ratio of Component (A) to Component (B) of the coordination catalyst is 0.5 to 15 and the molar ratio of Component (C) to Component (A) is 0.1 to 2.
Claim 6
Dependent Claim
32 words
The vulcanizates of interpolymers of α-olefins and α,ω-dienes according to claim 1 wherein the α,ω-diene is 1,7-octadiene, Component (B) of the coordination catalyst is titanium trichloride, and Component (C) is hexamethylphosphoric triamide.
Claim 7
Dependent Claim
44 words
The vulcanizates of interpolymers of α-olefins and α, ω-dienes according to claim 1 wherein the α,ω-diene is 1,7-octadiene, Component (B) of the coordination catalyst is titanium trichloride, and Component (C) is selected from the class consisting of triethyl phosphate, tri-n-butyl phosphate, and S,S,S-trimethyl phosphorotrithioate.
Claim 8
Dependent Claim
22 words
The vulcanizates of interpolymers of α-olefins and α,ω-dienes according to claim 1 wherein Component (B) of the coordination catalyst is titanium trichloride.
References Cited (Backward Citations)
GB836790A
Cited
US2933480A
Cited
GB1089333A
Cited
US3900452A
Cited
US3574176A
Cited
US3595842A
Cited
US3746694A
Cited
US3975336A
Cited
US4020250A
Cited
US3933769A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-11-04 | 1989-05-06 | 1989-11-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-11-04 | 1993-05-06 | 1993-11-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-11-04 | 1997-05-06 | 1997-11-05 | $7700.00 | Window Closed / Lapsed |