Method for surface treating copper foil
Assignee: Individual
•
Filing: 1985-03-08
•
Granted: 1985-10-29
•
Expires: 2005-03-08
Abstract
Abstract A method is and its resulting product are disclosed relating to the surface treatment of copper stock such as copper foil to improve its bondability to nonmetallic substrates. The method comprises immersing the copper in a bath having a composition consisting essentially of an aqueous solution of copper sulfate and sulfuric acid. While immersed in the bath, the copper is subjected to a plurality of pulsing treatment cycles, with each treatment cycle comprising a first application of peak current of a magnitude and duration sufficient to form a first layer coating on the surface of the copper but insufficient to cause the formation of a nodular coating exhibiting treatment transfer; and a second application of base current of a magnitude less than that of the peak current and sufficient to interrupt the formation of the first nodular layer but insufficient to serve to anchor the same to the foil surface. Preferably, the second application of current is longer than the first current application, with each treatment cycle milliseconds in duration, and all treatment cycles may be performed continuously. The resulting copper product is inexpensively prepared and exhibits uniformly superior bond strengths rendering it particularly well suited for printed circuit applications.
Inventors
- 👤 Steven J. Karwan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 20:56
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/38; H05K3/382; H05K3/384; C; C25; C25D; C25D5/00; C25D5/60; C25D5/605; C25D5/611; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0355; H05K2203/00; H05K2203/03; H05K2203/0307; H05K2203/07; H05K2203/0703; H05K2203/0723
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
257 words
A method for treating the surface of copper foil to improve the bond strength thereof, consisting essentially of: A. immersing said copper foil in a bath consisting essentially of an aqueous solution of copper sulfate and sulfuric acid; B. applying to the bath with said copper foil immersed therein, a continuous treatment of electric current, said treatment consisting essentially of a plurality of pulsing treatment cycles to cause the deposition on the surface of said copper foil of an adherent, irregular surface of improved bonding capability, each of said pulsing treatment cycles consisting essentially of a first peak current phase and a second base current phase; (i) said peak current phase performed at a current density and for a duration sufficient to form on at least one surface of said foil a fully adherent nodular layer on said surface, said nodular layer consisting essentially of copper, such current density and duration insufficient however, to form a nodular layer that exhibits treatment transfer and requires further treatment to anchor said nodular layer to the surface of said foil; (ii) said base current phase performed at a current density of a magnitude less than those of said peak current phase, and at a current density and for a duration sufficient to dispose over said nodular layer a thin, tightly adherent layer of smooth copper to interrupt the formation of said nodular layer, but insufficient to anchor said nodular layer to said foil surface; and (iii) wherein said pulsing treatment cycles are each as short as milliseconds in total duration.
Claim 2
Independent Claim
257 words
A method for treating the surface of copper foil to improve the bond strength thereof, consisting essentially of: A. immersing said copper foil in a bath consisting essentially of an aqueous solution of copper sulfate and sulfuric acid; B. applying to the bath with said copper foil immersed therein, a continuous treatment of electric current, said treatment consisting essentially of a plurality of pulsing treatment cycles to cause the deposition on the surface of said copper foil of an adherent, irregular surface of improved bonding capability, each of said pulsing treatment cycles consisting essentially of a first peak current phase and a second base current phase; (i) said peak current phase performed at a current density and for a duration sufficient to form on at least one surface of said foil a fully adherent nodular layer on said surface, said nodular layer consisting essentially of copper, such current density and duration insufficient however, to form a nodular layer that exhibits treatment transfer and requires further treatment to anchor said nodular layer to the surface of said foil; (ii) said base current phase performed at a current density of a magnitude less than those of said peak current phase, and at a current density and for a duration sufficient to dispose over said nodular layer a thin, tightly adherent layer of smooth copper to interrupt the formation of said nodular layer, but insufficient to anchor said nodular layer to said foil surface; and (iii) wherein said pulsing treatment cycles are each as short as milliseconds in total duration.
Claim 3
Dependent Claim
19 words
The method of claim 1 wherein said base current phase is longer in duration than said peak current phase.
Claim 4
Dependent Claim
20 words
The method of claim 1 wherein each succeeding base current phase is conducted for a longer duration than the previous.
Claim 5
Dependent Claim
26 words
The method of claim 1 wherein each of the respective of said peak and said base current phases is performed at the same magnitude of current.
Claim 6
Dependent Claim
54 words
The method of claim 4 wherein the magnitude of said peak current phase varies in current density, from about 56 amps per square foot to about 80 amps per square foot, and said base current phase varies in current density from about 40 amps per square foot to about 70 amps per square foot.
Claim 7
Dependent Claim
24 words
The method of claim 1 wherein said bath consists essentially of an aqueous solution of CuSO 4 .5H2O and H 2 SO 4 .
Claim 8
Dependent Claim
35 words
The method of claim 6 wherein said bath contains copper in an amount measured as the metal of about 39 grams per liter, and sulfuric acid in an amount of about 63 grams per liter.
Claim 9
Dependent Claim
24 words
The method of claim 1 wherein the total time for the performance of each of said treatment cycles is up to about 100 milliseconds.
Claim 10
Dependent Claim
37 words
The method of claim 1 wherein the duration of said peak current phase ranges from about 8 to about 10 milliseconds, and the duration of said base current phase ranges from about 10 to about 60 milliseconds.
Claim 11
Dependent Claim
22 words
The method of claim 1 wherein said pulsing treatment cycles have a total duration of from about 3 to about 3.5 minutes.
Claim 12
Dependent Claim
14 words
The method of claim 1 wherein at least two pulsing treatment cycles are performed.
Claim 13
Dependent Claim
14 words
The method of claim 1 wherein at least 60 pulsing treatment cycles are performed.
Claim 14
Dependent Claim
38 words
A copper product selected from copper foil, copper rod, copper wire and copper bar stock having a tightly adherent surface electrodeposit offering improved bondability to nonmetallic substrates, said electrodeposit prepared in accordance with the method of claim 1.
References Cited (Backward Citations)
US3293109A
Cited
US3585010A
Cited
US3857681A
Cited
US3918926A
Cited
US3799847A
Cited
US4049481A
Cited
WO1982002991A1
Cited
GB2116213A
Cited
US4468293A
Cited
GB2118973A
Cited
EP0112635A2
Cited
US4515671A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-28 | 1989-04-29 | 1989-10-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-28 | 1993-04-29 | 1993-10-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-28 | 1997-04-29 | 1997-10-29 | $7700.00 | Window Closed / Lapsed |