Method of selectively exposing the sidewalls of a trench and its use to the forming of a metal silicide substrate contact for dielectric filled deep trench isolated devices
Assignee: International Business Machines Corp
•
Filing: 1984-06-29
•
Granted: 1985-10-29
•
Expires: 2004-06-29
Abstract
Abstract Deep trenches (14,15) are formed according to the desired pattern through the N epitaxial layer (13) and N+ subcollector region (12) into the P- substrate (11) of a silicon structure (10). Where a substrate contact is needed, the trenches delineate a central stud (16) or mesa of silicon material. Channel stop regions (18) are formed e.g. by ion implantation of boron atoms at the bottom of trenches, SiO2 and Si3N4 layers (17,19) are then deposited on the whole structure. A substrate contact mask is applied and patterned to selectively expose one side of the trench sidewalls, the bottom of the trenches adjacent thereto and others areas if desired such as the top surface of the stud. The composite SiO2/Si3N4 layer is then etched to leave exposed only the sidewalls of the stud, at least partially the bottom of the trenches adjacent thereto and the top surface of the stud. Platinum is deposited preferably via sputter deposition, conformally coating all regions of the structure. After sintering, the unreacted platinum is removed using wet chemical etch (aqua regia). Platinum silicide is left in all opened contacts and on the stud sidewalls where its defines a metal silicide lining (25) or cap, covering the stud. This lining connects the top surface (25a) of the stud, with the channel stop implanted regions (18) and then forms the desired substrate contact.
Inventors
- 👤 George R. Goth
- 👤 Thomas A. Hansen
- 👤 James S. Makris
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 20:33
CPC Classifications
H; H10; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/014; H10W10/10; H10W10/17; H10W20/00; H10W20/01; H10W20/021
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
119 words
In a process of forming semiconductor devices in a semiconductor structure according to which a passivated trench is produced in the structure, the improvement comprising the steps of: depositing an underlay material to form an underlay layer to coat the structure and fill the trench; depositing a barrier layer above said underlay layer; patterning said barrier layer to form at least one opening which overlaps only partially the structure and the trench area, delineating the desired portions of the sidewalls, of the bottom of the trench and of the top surface of the structure, adjacent thereto, to be exposed; anisotropically etching the underlay material which is exposed through said opening, thereby selectively exposing said desired portions for further processing.
Claim 2
Dependent Claim
119 words
In a process of forming semiconductor devices in a semiconductor structure according to which a passivated trench is produced in the structure, the improvement comprising the steps of: depositing an underlay material to form an underlay layer to coat the structure and fill the trench; depositing a barrier layer above said underlay layer; patterning said barrier layer to form at least one opening which overlaps only partially the structure and the trench area, delineating the desired portions of the sidewalls, of the bottom of the trench and of the top surface of the structure, adjacent thereto, to be exposed; anisotropically etching the underlay material which is exposed through said opening, thereby selectively exposing said desired portions for further processing.
Claim 3
Dependent Claim
13 words
The process of claim 1 wherein said underlay material is an organic material.
Claim 4
Dependent Claim
18 words
The process of claim 2 wherein said barrier layer is an inorganic material such as SiO x .
Claim 5
Dependent Claim
31 words
The process of claim 3 wherein said step of patterning includes a conventional photolithographic step with an overetching of the barrier layer to ensure its complete removal in the exposed region.
Claim 6
Dependent Claim
29 words
The process of claim 4 wherein said step of completely etching the underlay material is effected in a parallel plate reactive ion etch tool in an O 2 plasma.
Claim 7
Dependent Claim
53 words
The process of claim 5 wherein said step is a two step process, comprised of a first anisotropic etch, to remove the underlay material to the bottom of the trench, then a cleaning step to remove retained underlay material where sidewalls have negative slopes, the latter step is accomplished at a higher pressure.
Claim 8
Dependent Claim
54 words
The process of claim 6 wherein said two-step process operating condition read as follows: ______________________________________
(1) Power density 0.17 watts/cm.sup.2
Pressure 3 μm
Flow 100 Scc/min.
Etch rate SiO.sub.x
.7 nm/min.
Etch rate polyimide
75 nm/min.
(2) Power density 0.23 watts/cm.sup.2
Pressure 50 μm
Flow (O.sub.2) 30 Scc/min.
Etch rate polyimide
200 nm/min.
______________________________________
Claim 9
Dependent Claim
20 words
The process of claim 1 wherein said trench is passivated by a composite SiO 2 /Si 3 N 4 layer.
Claim 10
Dependent Claim
32 words
The process of claim 8 wherein the exposed areas of the Si 3 N 4 layer forming part of said composite masking layer are removed to expose the underlying SiO 2 layer.
Claim 11
Dependent Claim
21 words
The process of claim 9 wherein said removal is accomplished in a CF4+10% O 2 plasma, in semi isotropic etching conditions.
Claim 12
Dependent Claim
43 words
The process of claim 10 wherein said conditions reads as follows: ______________________________________
Power density 0.23 watts/cm.sup.2
Pressure 200 μm
Flow (CF.sub.4 + 10% O.sub.2)
150 Scc/min.
Etch rate Si.sub.3 N.sub.4
70 nm/min.
Etch rate SiO.sub.2 40 nm/min.
Etch rate polyimide 45 nm/min.
______________________________________
Claim 13
Dependent Claim
21 words
The process of claim 11 wherein the remaining portions of the barrier layer are removed in a 10:1H 2 O:HF solution.
Claim 14
Dependent Claim
25 words
The process of claim 12 wherein the remaining portions of the underlay layer are removed using conventional ash processes in a barrel type barrel etcher.
Claim 15
Dependent Claim
21 words
The process of claim 13 wherein the exposed portions of the SiO 2 layer are removed in a buffer HF solution.
Claim 16
Dependent Claim
23 words
The process of claim 14 wherein said trench is part of a pattern of isolation trenches to isolate devices or part of devices.
Claim 17
Dependent Claim
40 words
The process of claim 15 wherein said structure is comprised of a P - silicon substrate having a N + subcollector and N epitaxial layer thereon, and said trenches are formed through said subcollector and epitaxial layer into said substrate.
Claim 18
Dependent Claim
17 words
The process of claim 15 wherein the bottom of said trenches is provided with channel stopper region.
Claim 19
Dependent Claim
31 words
The process of claim 17 wherein said pattern of trenches defines a central stud of silicon having all its sidewalls, the bottoms of trenches adjacent thereto and its top surface exposed.
Claim 20
Dependent Claim
63 words
The process of claim 18 further comprising the steps of: blanket depositing a layer of a silicide forming metal; sintering the structure to produce metal silicide wherever said metal contacts silicon; and, removing the unreacted metal, leaving a metal silicide cap covering the stud and channel stopper regions, therefore providing an electrical contact between the top side of the structure and the substrate.
Claim 21
Dependent Claim
13 words
The process of claim 19 wherein said depositing step is accomplished by sputtering.
Claim 22
Dependent Claim
18 words
The process of claim 20 wherein said metal is selected in the group comprised of platinum and palladium.
Claim 23
Dependent Claim
46 words
The process of claim 21 further comprising the step of filling the trenches with polyimide and reactively ion etching in an O 2 plasma the polyimide in excess to let exposed the top part of said metal silicide cap to be used as a substrate contact.
Claim 24
Dependent Claim
21 words
The process of any of the preceding claims wherein said underlay material is an organic material selected from the polyimide group.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-28 | 1989-04-29 | 1989-10-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-28 | 1993-04-29 | 1993-10-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-28 | 1997-04-29 | 1997-10-29 | $7700.00 | Window Closed / Lapsed |