Abstract There is disclosed a method of producing a photochromic glass having a reduced transmittance for ultraviolet radiation while having substantially unimpaired photochromic properties. The method comprises providing a combination of 0.1-1.0% CeO 2 and 0.1-1.5% Sb 2 O 3 and/or As 2 O 3 as part of the glass composition. In an embodiment utilizing minimal silver content, the glass article in thicknesses of 1.3 to 2.0 mm. can be chemically strengthened to surpass the impact specification imposed by the Federal Food and Drug Administration for eyewear, will transmit less than 0.2% of radiation having wavelengths between 290-315 nm, and will demonstrate a darkened luminous transmittance at 20°-25° C. below 35% and a fading rate such that after five minutes the luminous transmittance will be at least 1.75 times that of the darkened transmittance. These glasses consist essentially of: ______________________________________ SiO 2 55-61 Ag >0.1-<0.2
B 2 O 3 18-21 Cl 0.2-0.6
Al 2 O 3 5-11 Br 0.05-0.2
Li 2 O
1.5-3 CuO 0.003-0.015
Na 2 O
2-5 CeO 2 0.1-1.0
K 2 O
4.5-8 Sb 2 O 3 0.1-1.5
______________________________________
A method for producing a photochromic glass article that, in cross section of < 2 mm but >1.3 mm, will transmit less than 0.2% of radiations having wavelengths between 290-315 nm, can be chemically strengthened to pass the strength standards mandated by the FDA, and at 20°-25° C. will exhibit a darkened luminous transmittance below 35% and a fading rate such that after five minutes the luminous transmittance will be at least 1.75 times that of the darkened transmittance, which method comprises the steps of: (a) melting a batch for a glass consisting essentially, expressed in terms of weight percent on the oxide basis, of ______________________________________
SiO.sub.2
55-61 CeO.sub.2 0.1-1
B.sub.2 O.sub.3
18-21 Ag >0.1-<0.2
Al.sub.2 O.sub.3
5-11 CuO 0.003-0.015
Li.sub.2 O
1.5-3 Cl 0.2-0.6
Na.sub.2 O
2-5 Br 0.05-0.2
K.sub.2 O
4.5-8 Sb.sub.2 O.sub.3 and/or As.sub.2 O.sub.3
0.1-1.5
______________________________________ wherein the amount of Sb 2 O 3 and/or As 2 O 3 is at least 75% of the amount of CeO 2 present; (b) cooling said melt and simultaneously forming a glass article of a desired geometry therefrom; and thereafter (c) heating said glass article to a temperature between about 650°-675° C. for a sufficient period of time to cause the growth of silver halide crystallites therein whereby said photochromic glass article is provided which, at 20°-25° C., will exhibit a darkened luminous transmittance below 35% and a fading rate such that after five minutes the luminous transmittance will be at least 1.75 times that of the darkened transmittance.
Claim 2
Independent Claim
250 words
A method for producing a photochromic glass article that, in cross section of < 2 mm but >1.3 mm, will transmit less than 0.2% of radiations having wavelengths between 290-315 nm, can be chemically strengthened to pass the strength standards mandated by the FDA, and at 20°-25° C. will exhibit a darkened luminous transmittance below 35% and a fading rate such that after five minutes the luminous transmittance will be at least 1.75 times that of the darkened transmittance, which method comprises the steps of: (a) melting a batch for a glass consisting essentially, expressed in terms of weight percent on the oxide basis, of ______________________________________
SiO.sub.2
55-61 CeO.sub.2 0.1-1
B.sub.2 O.sub.3
18-21 Ag >0.1-<0.2
Al.sub.2 O.sub.3
5-11 CuO 0.003-0.015
Li.sub.2 O
1.5-3 Cl 0.2-0.6
Na.sub.2 O
2-5 Br 0.05-0.2
K.sub.2 O
4.5-8 Sb.sub.2 O.sub.3 and/or As.sub.2 O.sub.3
0.1-1.5
______________________________________ wherein the amount of Sb 2 O 3 and/or As 2 O 3 is at least 75% of the amount of CeO 2 present; (b) cooling said melt and simultaneously forming a glass article of a desired geometry therefrom; and thereafter (c) heating said glass article to a temperature between about 650°-675° C. for a sufficient period of time to cause the growth of silver halide crystallites therein whereby said photochromic glass article is provided which, at 20°-25° C., will exhibit a darkened luminous transmittance below 35% and a fading rate such that after five minutes the luminous transmittance will be at least 1.75 times that of the darkened transmittance.
Claim 3
Dependent Claim
27 words
A method according to claim 1 wherein said CeO 2 ranges about 0.1-0.4% and said Sb 2 O 3 and/or As 2 O 3 ranges about 0.15-0.5%.
Claim 4
Dependent Claim
15 words
A method according to claim 1 wherein said glass also contains up to 0.25% PbO.
Claim 5
Dependent Claim
49 words
A method according to claim 1 wherein said glass also contains up to 10% total of at least one of the following oxides in the indicated proportions of up to 5% La 2 O 3 , up to 5% ZrO 2 , and up to 3% TiO 2 .