Process for the preparation of polyurea elastomers

Claim 2

In a process for the preparation of a high flexural modulus elastomer containing polyurea linkages by the reaction injection molding of (i) an organic polyisocyanate, (ii) an organic compound having at least two active hydrogen containing groups and a molecular weight of from about 1500 to about 12,000, and (iii) an aromatic diamine extender wherein at least one of the positions ortho to each amine group of said diamine is substituted by a lower alkyl group, the improvement which comprises injecting the above ingredients into a mold said mold being at a temperature of from about 110° to about 190° and holding thereat for a time sufficient to achieve an improvement in the brittle properties on demold of said molded elastomer.

Claim 3

A process according to claim 1 wherein said polyisocyanate (i) comprises an aromatic polyisocyanate.

Claim 4

A process according to claim 2 wherein said polyisocyanate comprises methylenebis(phenyl isocyanate).

Claim 5

A process according to claim 2 wherein said polyisocyanate is selected from the group consisting of (a) an isocyanate terminated prepolymer having an isocyanate content of about 9 to about 20 percent by weight and prepared from methylenebis(phenyl isocyanate), (b) a liquefied form of 4,4'-methylenebis(phenyl isocyanate), and mixtures of (a) and (b).

Claim 6

A process according to claim 1 wherein said organic compound (ii) comprises a polyol having a primary hydroxyl functionality of from about 2 to about 4.

Claim 7

A process according to claim 1 wherein said organic compound (ii) comprises a primary or secondary amine terminated polyether having an amine functionality of about 2 to about 4.

Claim 8

A process according to claim 1 wherein said aromatic diamine extender is selected from the group consisting of 1-methyl-3,5-diethyl-2,4-diaminobenzene, 1-methyl-3,5-diethyl,2,6-diaminobenzene, and mixtures thereof.

Claim 9

A process according to claim 1 wherein said aromatic diamine extender (iii) is present in an amount of from about 25 to about 60 percent by weight based on the combined weight of (ii) and (iii) and the ratio of isocyanate equivalents to the total active hydrogen equivalents of (ii) and (iii) is from about 0.95 to about 1.15.

Claim 10

A process according to claim 1 including a minor amount of an aliphatic chain extender diol having a MW of 60 to 400.

Claim 11

A process according to claim 1 wherein the demold time falls within the range of from about 3 seconds to about 5 minutes.

Claim 12

A process for the preparation of a high flexural modulus elastomer containing polyurea linkages said process comprising the reaction injection molding into a mold at a temperature of from about to about 110° to about 190° C. and holding thereat in said mold for a period of from about 3 seconds to about 5 minutes the following ingredients: (i) an aromatic polyisocyanate selected from the group consisting of (a) isocyanate terminated prepolymers having an isocyanate content of about 9 to about 20 percent by weight and prepared from methylenebis(phenyl isocyanate), (b) a liquefied form of 4,4'-methylenebis-(pheynl isocyanate), and mixtures of (a) and (b); (ii) an organic polyol or polyamine having a molecular weight of from about 1500 to about 12,000 and selected from the group consisting of polyols having a primary hydroxyl functionality of from about 2 to about 4, a primary or secondary amine terminated polyether having an amine functionality of about 2 to about 4, and mixtures of said polyol and polyamine; (iii) a diamine extender selected from the group consisting of 1-methyl-3,5-diethyl-2,4-diaminobenzene, 1-methyl-3,5-diethyl-2,6-diaminobenzene, and mixtures thereof; and (iv) optionally a catalyst for the reaction of isocyanate groups with the reactive hydrogen containing compounds wherein said diamine extender is present in an amount of from about 25 to about 60 percent by weight based on the combined weight of (ii) and (iii) and the ratio of isocyanate equivalents to the total active hydrogen equivalents of (ii) and (iii) is from about 0.95 to about 1.15.

Claim 13

A process for the preparation of a high flexural modulus elastomer containing polyurea linkages said process comprising the reaction injection molding into a mold at a temperature of from about to about 110° to about 190° C. and holding thereat in said mold for a period of from about 3 seconds to about 5 minutes the following ingredients: (i) an aromatic polyisocyanate selected from the group consisting of (a) isocyanate terminated prepolymers having an isocyanate content of about 9 to about 20 percent by weight and prepared from methylenebis(phenyl isocyanate), (b) a liquefied form of 4,4'-methylenebis-(pheynl isocyanate), and mixtures of (a) and (b); (ii) an organic polyol or polyamine having a molecular weight of from about 1500 to about 12,000 and selected from the group consisting of polyols having a primary hydroxyl functionality of from about 2 to about 4, a primary or secondary amine terminated polyether having an amine functionality of about 2 to about 4, and mixtures of said polyol and polyamine; (iii) a diamine extender selected from the group consisting of 1-methyl-3,5-diethyl-2,4-diaminobenzene, 1-methyl-3,5-diethyl-2,6-diaminobenzene, and mixtures thereof; and (iv) optionally a catalyst for the reaction of isocyanate groups with the reactive hydrogen containing compounds wherein said diamine extender is present in an amount of from about 25 to about 60 percent by weight based on the combined weight of (ii) and (iii) and the ratio of isocyanate equivalents to the total active hydrogen equivalents of (ii) and (iii) is from about 0.95 to about 1.15.

Claim 14

A process according to claim 11 wherein said polyisocyanate comprises a liquefied form of 4,4'-methylenebis(phenyl isocyanate).

Claim 15

A process according to claim 11 wherein said polyisocyanate comprises a mixture of said liquefied form of 4,4'-methylenebis(phenyl isocyanate) and an isocyanate terminated prepolymer having an isocyanate content of about 9 to about 20 percent by weight and prepared from methylenebis(phenyl isocyanate).

Claim 16

A process according to claim 11 wherein component (ii) comprises a polyol having a primary hydroxyl functionality of about 2 to about 3.

Claim 17

A process according to claim 11 wherein said component (ii) comprises a primary amine terminated polyether having an amine functionality of about 2 to about 3.

Claim 18

A process according to claim 11 wherein said polyisocyanate (i) comprises a liquefied form of 4,4-methylenebis(phenyl isocyanate) which has been reacted previously with from about 0.04 to about 0.2 equivalent per isocyanate equivalent of a diol selected from dipropylene glycol, tripropylene glycol and mixtures thereof; and (ii) comprises a polyoxyethylene-polyoxypropylene triol of MW of about 4000 to about 7000.

Claim 19

A process according to claim 11 wherein said polyisocyanate (i) comprises a mixture of (1) a liquefied form of 4,4'-methylenebis(phenyl isocyanate) which has been reacted previously with from about 0.04 to about 0.2 equivalent per isocyanate equivalent of a diol selected from dipropylene glycol, tripropylene glycol and mixtures thereof, (2) a liquefied form of 4,4'-methylenebis(phenyl isocyanate) obtained by heating the latter with a carbodiimide forming catalyst to convert a portion of said 4,4'-methylenebis(phenyl isocyanate) to carbodiimide, and (3) an isocyanate terminated prepolymer prepared from 4,4'-methylenebis(phenyl isocyanate) and a polyoxyethylene-polyoxypropylene triol (MW of about 4500 to about 5500)said triol and said 4,4'-methylenebis(phenyl isocyanate) having been reacted in the proportions of about 0.01 to about 0.5 equivalent of the former per equivalent of the latter; and (ii) comprises a primary amine terminated polyether having an amine functionality of about 3 and MW about 4000 to 6000.

Claim 20

A high flexural modulus elastomer containing polyrea linkages prepared in accordance with claim 1.