Method for the formation of calcium silicate and the resulting structure
Assignee: Ceramic Design International Holding Bv
•
Filing: 1981-10-28
•
Granted: 1985-10-08
•
Expires: 2001-10-28
Abstract
Abstract Calcium silicate is formed by a process wherein the viscosity of the calcium silicate produced in an autoclave is lowered by adding an acetate to the reaction constituents prior to the reaction of these constituents to form the calcium silicate crystals. In one embodiment, manganese acetate is added to comprise between approximately 1% and 3% by weight of the solids contents of the reaction constituents. The result is to lower the viscosity of the reaction product and thus to allow a higher solids content in the autoclave than heretofore commonly used. In one embodiment, water is added in-line to the reaction products as they are transferred from the autoclave to a holding vessel or from a holding vessel to a storage tank. In a further embodiment, fibrous material is added to the holding vessel prior to the transfer of the reaction product into the holding vessel, thus to reduce the amount of energy required to bring the pressure in the holding vessel up to a selected pressure beneath that of the autoclave.
Inventors
- 👤 Pieter Krijgsman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 10:11
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/18; B; B01; B01J; B01J3/00; B01J3/04; C01; C01B; C01B33/00; C01B33/20; C01B33/24; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/91
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
55 words
In a process for the formation of calcium silicate from calcium hydroxide and silicon dioxide, the improvement comprising: adding an acetate to the reaction constituents prior to the reaction of these constituents to form the calcium silicate crystals wherein said acetate is selected from the group consisting of magnesium acetate, manganese acetate and nickel acetate.
Claim 2
Dependent Claim
55 words
In a process for the formation of calcium silicate from calcium hydroxide and silicon dioxide, the improvement comprising: adding an acetate to the reaction constituents prior to the reaction of these constituents to form the calcium silicate crystals wherein said acetate is selected from the group consisting of magnesium acetate, manganese acetate and nickel acetate.
Claim 3
Dependent Claim
16 words
The method of claim 1 wherein the material added to said reaction constituents is manganese acetate.
Claim 4
Dependent Claim
33 words
The method of claim 2 wherein said manganese acetate is added to said reaction constituents in a range between approximately 1 and 3% by weight of the solid contents of said reaction constituents.
Claim 5
Independent Claim
120 words
The method of forming calcium silicate insulation in which reaction constituents comprising calcium hydroxide, silicon dioxide, water and an acetate selected from the group consisting of magnesium acetate, manganese acetate and nickel acetate, are reacted in an autoclave for a selected time, and transferred to a receiving vessel held in a controlled manner at a pressure beneath that of the autoclave during the transfer process characterized by adding fibrous material and chemically unreacted silica dust to the receiving vessel prior to the transfer of the reaction products from the autoclave to the receiving vessel, thereby to reduce the amount of energy required to bring the pressure in said receiving vessel up to a selected pressure beneath that in the autoclave.
Claim 6
Independent Claim
120 words
The method of forming calcium silicate insulation in which reaction constituents comprising calcium hydroxide, silicon dioxide, water and an acetate selected from the group consisting of magnesium acetate, manganese acetate and nickel acetate, are reacted in an autoclave for a selected time, and transferred to a receiving vessel held in a controlled manner at a pressure beneath that of the autoclave during the transfer process characterized by adding fibrous material and chemically unreacted silica dust to the receiving vessel prior to the transfer of the reaction products from the autoclave to the receiving vessel, thereby to reduce the amount of energy required to bring the pressure in said receiving vessel up to a selected pressure beneath that in the autoclave.
Claim 7
Dependent Claim
28 words
The method of claim 4 wherein said fibrous material comprises a mixture of mineral wool and cellulose fibers, and free silica comprises high surface area dust or powder.
Claim 8
Dependent Claim
43 words
The method of claim 5 wherein said mineral wool comprises approximately 2.5% by weight of the calcium hydroxide and silicon dioxide in the autoclave and the cellulose fibers comprise approximately 2.5% by weight of the calcium hydroxide and silicon dioxide in the autoclave.
Claim 9
Dependent Claim
12 words
The method of claim 4 wherein said fibrous material comprises cellulose fibers.
Claim 10
Dependent Claim
27 words
The method claim 7 wherein said cellulose fibers comprise approximately 5% by weight of the solids content of the calcium hydroxide and silicon dioxide in the autoclave.
References Cited (Backward Citations)
BE624441A
Cited
US3679446A
Cited
US3816149A
Cited
US4131638A
Cited
US4179303A
Cited
US4238240A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-07 | 1989-04-08 | 1989-10-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-07 | 1993-04-08 | 1993-10-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-07 | 1997-04-08 | 1997-10-08 | $7700.00 | Window Closed / Lapsed |