Abstract A process for preparing a particulate ceramic material comprising the steps of: (a) adding carbon dioxide or an aqueous solution of a soluble carbonate to first aqueous solution of a nitrate or chloride of Ba, Sr, Ca or Mg in a first vessel to adjust the pH of said first aqueous solution to between 7 and 10 thereby forming a carbonate precipitate; (b) adding an aqueous solution of a soluble hydroxide to a second aqueous solution of a nitrate or chloride of Ti, Zr, Sn or Pb in a second vessel to adjust the pH of said second aqueous solution to between 7 and 10 thereby forming a hydroxide precipitate; (c) combining slurries containing the precipitates formed in said first and second vessels; (d) mixing the combined slurries; (e) passing the slurries through a filter; (f) washing the filter cake with water; (g) drying the filter cake to form a powder; (h) calcining the dried powder; and (i) grinding the calcined powder.
A process for preparing a particulate ceramic material comprising the steps of: (a) adding carbon dioxide or an aqueous solution of a soluble carbonate to first aqueous solution of a nitrate or chloride of Ba, Sr, Ca or Mg in a first vessel to adjust the pH of said first aqueous solution to between 7 and 10 thereby forming a carbonate precipitate; (b) adding an aqueous solution of a soluble hydroxide to a second aqueous solution of a nitrate or chloride of Ti, Zr, Sn or Pb in a second vessel to adjust the pH of said second aqueous solution to between 7 and 10 thereby forming a hydroxide precipitate; (c) combining slurries containing the precipitates formed in said first and second vessels; (d) mixing the combined slurries; (e) passing the slurries through a filter; (f) washing the filter cake with water; (g) drying the filter cake to form a powder; (h) calcining the dried powder; and (i) grinding the calcined powder.
Claim 2
Dependent Claim
162 words
A process for preparing a particulate ceramic material comprising the steps of: (a) adding carbon dioxide or an aqueous solution of a soluble carbonate to first aqueous solution of a nitrate or chloride of Ba, Sr, Ca or Mg in a first vessel to adjust the pH of said first aqueous solution to between 7 and 10 thereby forming a carbonate precipitate; (b) adding an aqueous solution of a soluble hydroxide to a second aqueous solution of a nitrate or chloride of Ti, Zr, Sn or Pb in a second vessel to adjust the pH of said second aqueous solution to between 7 and 10 thereby forming a hydroxide precipitate; (c) combining slurries containing the precipitates formed in said first and second vessels; (d) mixing the combined slurries; (e) passing the slurries through a filter; (f) washing the filter cake with water; (g) drying the filter cake to form a powder; (h) calcining the dried powder; and (i) grinding the calcined powder.
Claim 3
Dependent Claim
37 words
The process according to claim 1, wherein the aqueous solution of nitrate or chloride used in said second vessel further contains at least one element selected from the group consisting of Nb, Y and rare earth metal.
Claim 4
Dependent Claim
37 words
The process according to claim 1, wherein the aqueous solution of nitrate or chloride used in said second vessel further contains at least one element selected from the group consisting of Mn, Al, Si, Bi and Zn.
Claim 5
Dependent Claim
23 words
The process according to claim 1, wherein the powder is calcined at a temperature in the range of from 700° to 1,200° C.