US3983077A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for making ceramic resistor materials
Assignee: Texas Instruments Inc
•
Filing: 1975-05-02
•
Granted: 1976-09-28
•
Expires: 1995-05-02
Abstract
Abstract A process for making barium titanate based materials and the like of positive temperature coefficient of resistivity having desirable and precisely predetermined thermal and electrical properties utilizes low cost starting materials and convenient and economical processing steps. Titanium dioxide powder is placed in suspension in an aqueous medium with dissolved compounds of barium and other selected materials while the pH of the medium is regulated within selected limits, whereby barium and other selected ions are adsorbed in predetermined ratio by suspended titanium dioxide particles and whereby water-soluble contaminants in the starting materials are placed in solution. An aqueous carbonate solution is then commingled with the titanium dioxide suspension in a controlled manner to form a precipitate which incorporates titanium dioxide and desired relative proportions of carbonates of barium and other selected materials in a homogenous mixture. The precipitate is filtered from the aqueous medium for effecting separation of the water soluble contaminants from the precipitate. The precipitate is subsequently dried and calcined and is preferably combined with a binder and fired for forming ceramic resistor elements.
Inventors
- 👤 Peter G. Fuller
- 👤 Hans A. Stoeckler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 18:18
CPC Classifications
H; H01; H01C; H01C7/00; H01C7/02; H01C7/022; H01C7/023; H01C7/025; C; C01; C01B; C01B13/00; C01B13/14; C01G; C01G23/00; C01G23/003; C01G23/006; C01P; C01P2006/00; C01P2006/40
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
139 words
A method for producing a mixed metal oxide material incorporating at least one element selected from the group consisting of barium, strontium, calcium and lead and at least one metal selected from the group consisting of titanium, tin and zirconium, said method comprising the steps of combining an aqueous solution of a water soluble compound of at least said one element with an oxide of at least said one metal suspended in an aqueous medium and regulating the pH of said combined solution-suspension to obtain desired stability thereof, thereby to place any water soluble contaminants of said compound in metal oxide in solution in said aqueous medium, removing said aqueous medium with said contaminants to leave a homogeneous mixture of a material incorporating said one element and said metal oxide, and pyrolyzing said mixture for forming said mixed metal
Claim 2
Independent Claim
139 words
A method for producing a mixed metal oxide material incorporating at least one element selected from the group consisting of barium, strontium, calcium and lead and at least one metal selected from the group consisting of titanium, tin and zirconium, said method comprising the steps of combining an aqueous solution of a water soluble compound of at least said one element with an oxide of at least said one metal suspended in an aqueous medium and regulating the pH of said combined solution-suspension to obtain desired stability thereof, thereby to place any water soluble contaminants of said compound in metal oxide in solution in said aqueous medium, removing said aqueous medium with said contaminants to leave a homogeneous mixture of a material incorporating said one element and said metal oxide, and pyrolyzing said mixture for forming said mixed metal
Claim 3
Independent Claim
136 words
A method for producing a mixed metal oxide material incorporating at least one element selected from the group consisting of barium, strontium, calcium and lead and at least one metal selected from the group consisting of titanium, tin and zirconium, said method comprising the steps of combining an aqueous solution of a water soluble compound of at least said one element with an aqueous suspension of an oxide of at least said one metal and regulating the pH of said combined solution-suspension to obtain desired stability thereof, commingling said combined solution-suspension with an aqueous carbonate solution for forming a precipitate incorporating a homogeneous mixture of said one metal oxide and a carbonate of said one element in an aqueous medium, filtering said precipitate from aqueous medium, and pyrolyzing said precipitate for forming said mixed metal oxide
Claim 4
Independent Claim
136 words
A method for producing a mixed metal oxide material incorporating at least one element selected from the group consisting of barium, strontium, calcium and lead and at least one metal selected from the group consisting of titanium, tin and zirconium, said method comprising the steps of combining an aqueous solution of a water soluble compound of at least said one element with an aqueous suspension of an oxide of at least said one metal and regulating the pH of said combined solution-suspension to obtain desired stability thereof, commingling said combined solution-suspension with an aqueous carbonate solution for forming a precipitate incorporating a homogeneous mixture of said one metal oxide and a carbonate of said one element in an aqueous medium, filtering said precipitate from aqueous medium, and pyrolyzing said precipitate for forming said mixed metal oxide
Claim 5
Independent Claim
151 words
A method for producing a ceramic resistor material of positive temperature coefficient of resistivity comprising the steps of combining an aqueous solution of a water soluble compound of at least on element selected from the group consisting of barium, strontium, calcium and lead and a water soluble compound of at least one dopant selected from the group consisting of yttrium, lanthanum, cerium, dysprosium and praesodymium with an aqueous suspension of an oxide of at least one metal selected from the group consisting of titanium, tin and zirconium and regulating the pH of said combined solution-suspension to obtain desired stability thereof, commingling said combined solution-suspension with an aqueous carbonate solution for forming a precipitate incorporating a homogeneous mixture of at least said one metal oxide and carbonate of at least said one element and said one dopant in an aqueous medium, filtering said precipitate from said aqueous medium, and calcining said precipitate
Claim 6
Independent Claim
151 words
A method for producing a ceramic resistor material of positive temperature coefficient of resistivity comprising the steps of combining an aqueous solution of a water soluble compound of at least on element selected from the group consisting of barium, strontium, calcium and lead and a water soluble compound of at least one dopant selected from the group consisting of yttrium, lanthanum, cerium, dysprosium and praesodymium with an aqueous suspension of an oxide of at least one metal selected from the group consisting of titanium, tin and zirconium and regulating the pH of said combined solution-suspension to obtain desired stability thereof, commingling said combined solution-suspension with an aqueous carbonate solution for forming a precipitate incorporating a homogeneous mixture of at least said one metal oxide and carbonate of at least said one element and said one dopant in an aqueous medium, filtering said precipitate from said aqueous medium, and calcining said precipitate
Claim 7
Dependent Claim
22 words
A method as set forth in claim 3 wherein manganese nitrate is dissolved in said combined solution-suspension so that said precipitate incorporates
Claim 8
Dependent Claim
48 words
A method as set forth in claim 3 wherein at least one additional oxide selected from the group consisting of the oxides of manganese and silicon is placed in suspension in said aqueous medium so that said precipitate incorporates at least said one additional metal oxide homogeneously mixed
Claim 9
Dependent Claim
88 words
A method as set forth in claim 3 wherein a sufficient quantity of water soluble barium, strontium, yttrium and manganese salts are placed in said aqueous solution and wherein a sufficient quantity of titanium and silicon dioxides are placed in suspension in said aqueous medium so that the combined solution-suspension embodies 0.77 moles barium, 0.23 moles strontium, 0.035 moles silicon and 0.006 moles yttrium for each 1.01 moles titanium and embodies sufficient manganese to comprise about 170 ppm. of the resulting ceramic resistor material, whereby said calcined precipitate
Claim 10
Dependent Claim
88 words
A method as set forth in claim 3 wherein a sufficient quantity of water soluble barium, lead, yttrium and manganese salts are placed in said aqueous solution and wherein a sufficient quantity of titanium and silicon dioxides are placed in suspension in said aqueous medium so that the combined solution-suspension embodies 0.98 moles barium, 0.02 moles lead, 0.035 moles silicon and 0.007 moles yttrium for each 1.01 moles titanium and embodies sufficient manganese to comprise about 150 ppm. of the resulting ceramic resistor material, whereby said calcined precipitate
Claim 11
Dependent Claim
88 words
A method as set forth in claim 3 wherein a sufficient quantity of water soluble barium, lead, yttrium and manganese salts are placed in said aqueous solution and wherein a sufficient quantity of titanium and silicon dioxides are placed in suspension in said aqueous medium so that the combined solution-suspension embodies 0.89 moles barium, 0.11 moles lead, 0.035 moles silicon and 0.006 moles yttrium for each 1.01 moles titanium and embodies sufficient manganese to comprise about 100 ppm. of the resulting ceramic resistor material, whereby said calcined precipitate
Claim 12
Dependent Claim
77 words
A method as set forth in claim 3 wherein a sufficient quantity of water soluble barium, lead and yttrium salts are placed in said aqueous solution and wherein a sufficient quantity of titanium and silicon dioxides are placed in suspension in said aqueous medium so that the combined solution-suspension embodies 0.95 moles barium, 0.05 moles lead, 0.03 moles silicon and 0.006 moles yttrium for each 1.01 moles titanium, whereby said calcined precipitate displays a Curie temperature of
Claim 13
Dependent Claim
88 words
A method as set forth in claim 3 wherein a sufficient quantity of water soluble barium, lead, yttrium and manganese salts are placed in said aqueous solution and wherein a sufficient quantity of titanium and silicon dioxides are placed in suspension in said aqueous medium so that the combined solution-suspension embodies 0.84 moles barium, 0.16 moles lead, 0.03 moles silicon and 0.006 moles yttrium for each 1.02 moles titanium and embodies sufficient manganese to comprise about 50 ppm. of the resulting ceramic resistor material, whereby said calcined precipitate
Claim 14
Dependent Claim
75 words
A method as set forth in claim 3 wherein a sufficient quantity of water soluble barium, strontium and yttrium salts are placed in said aqueous solution and wherein a sufficient quantity of titanium and silicon dioxides are placed in suspension is said aqueous medium so that the combined solution-suspension embodies 0.95 moles barium, 0.05 moles strontium, 0.035 moles silicon, and 0.004 moles yttrium for each 1.01 moles titanium, whereby said calcined precipitate displays a Curie
Claim 15
Dependent Claim
88 words
A method as set forth in claim 3 wherein a sufficient quantity of water soluble barium, lead, yttrium and manganese salts are placed in said aqueous solution and wherein a sufficient quantity of titanium and silicon dioxides are placed in suspension in said aqueous medium so that the combined solution-suspension embodies 0.91 moles barium, 0.09 moles lead, 0.035 moles silicon and 0.006 moles yttrium for each 1.01 moles titanium and embodies sufficient manganese to comprise about 150 ppm. of the resulting ceramic resistor material, whereby said calcined precipitate
Claim 16
Dependent Claim
87 words
A method as set forth in claim 3 wherein a sufficient quantity of water soluble barium, strontium and yttrium salts are placed in said aqueous solution and wherein a sufficient quantity of titanium and silicon dioxides are placed in suspension in said aqueous medium so that the combined solution-suspension embodies 0.86 moles barium, 0.14 moles strontium, 0.035 moles silicon and 0.006 moles yttrium for each 1.02 moles titanium and embodies sufficient manganese to comprise about 226 ppm. of the resulting ceramic resistor material, whereby said calcined precipitate
Claim 17
Dependent Claim
95 words
A method as set forth in claim 3 wherein a sufficient quantity of water soluble barium, strontium and yttrium salts are placed in said aqueous solution and wherein a sufficient quantity of titanium and silicon dioxides are placed in suspension in said aqueous medium so that the combined solution-suspension embodies 0.93 moles barium, 0.07 moles strontium, 0.035 moles silicon and 0.006 moles yttrium for each 1.01 moles titanium and embodies sufficient manganese to comprise about 230 ppm. of the resulting ceramic resistor material, whereby said calcined precipitate displays a Curie temperature of approximately 105° C.
References Cited (Backward Citations)
US3351568A
Cited
US3586642A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-28 | 1980-03-29 | 1980-09-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-28 | 1984-03-29 | 1984-09-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-28 | 1988-03-29 | 1988-09-28 | $7700.00 | Window Closed / Lapsed |