Abstract
Abstract A novel process for placing a thin film of a metal nitride, e.g. titanium nitride, on a glass substrate by mixing a metal halide with a reducing gas like ammonia, preferably within a range of from about 250° C. to 320° C., and then reacting the gases at the surface of a glass substrate heated to, e.g., about 400° C. to about 700° C. to form the film on the glass.
Inventors
- 👤 Roy G. Gordon
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 13:48
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/34; C03; C03C; C03C17/00; C03C17/22; C03C17/225; C03C2217/00; C03C2217/20; C03C2217/28; C03C2217/281; C03C2218/00; C03C2218/10; C03C2218/15; C03C2218/152
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
138 words
A process for depositing a transparent, solar control film composed mainly of titanium nitride on a transparent heated glass ribbon substrate, by the steps of (a) preparing a first preheated gaseous mixture of titanium tetrahalide vapor reactant in an inert carrier gas, (b) preparing a second preheated gaseous mixture of ammonia reactant, as a nitrogen donor and a reducing gas, and inert carrier gas, said first and second gaseous mixtures containing at least 0.1 mole percent of said tetrahalide based on the gas in both mixtures and, (c) mixing the two said gas mixtures at a temperature below 500° C. in the immediate proximity of said substrate which is at a temperature of at least about 500° C. such that a substantially haze free film is formed on by reaction products of said reactants on said glass substrate.
Claim 2
Dependent Claim
138 words
A process for depositing a transparent, solar control film composed mainly of titanium nitride on a transparent heated glass ribbon substrate, by the steps of (a) preparing a first preheated gaseous mixture of titanium tetrahalide vapor reactant in an inert carrier gas, (b) preparing a second preheated gaseous mixture of ammonia reactant, as a nitrogen donor and a reducing gas, and inert carrier gas, said first and second gaseous mixtures containing at least 0.1 mole percent of said tetrahalide based on the gas in both mixtures and, (c) mixing the two said gas mixtures at a temperature below 500° C. in the immediate proximity of said substrate which is at a temperature of at least about 500° C. such that a substantially haze free film is formed on by reaction products of said reactants on said glass substrate.
Claim 3
Dependent Claim
12 words
A process as defined in claim 1 wherein said tetrahalide is tetrachloride.
Claim 4
Dependent Claim
28 words
A process as in claim 1, in which the preheating of said tetrahalide and said ammonia is within the range of about 200° C. to about 400° C.
Claim 5
Dependent Claim
21 words
A process as in claim 2, wherein 1 to 50 moles of ammonia are mixed with every mole of titanium tetrachloride.
Claim 6
Dependent Claim
16 words
A process as in claim 1, wherein said titanium tetrahalide is titanium tetrabromide or titanium tetraiodide.
Claim 7
Dependent Claim
16 words
A process as in claim 3, wherein said titanium tetrahalide is titanium tetrabromide or titanium tetraiodide.
Claim 8
Dependent Claim
33 words
A process as in claim 2, in which the final mixing of said tetrachloride and said ammonia takes place at a temperature within the range of about 200° C. to about 400° C.
Claim 9
Dependent Claim
37 words
A process as defined in claim 3 wherein said mixing of said first and second gas mixtures takes place with said gas mixtures preheated to within a temperature range of from about 250° C. to 320° C.
Claim 10
Dependent Claim
18 words
A process as in claim 8, wherein the substrate is heated to a temperature of above 500° C.
Claim 11
Dependent Claim
96 words
A process for depositing a solar control film of titanium nitride on a transparent, heated glass ribbon substrate, said process including the steps of (a) preparing a gaseous mixture of titanium tetrahalide vapor reactant and an inert carrier gas, (b) preparing a second gas mixture of ammonia reactant, as a nitrogen donor and a reducing gas, and an inert carrier gas, (c) mixing said gas mixtures at a temperature range of from about 200° C. to 400° C. to provide a reaction product; and (d) depositing said reaction product on a said transparent, heated glass substrate.
Claim 12
Dependent Claim
96 words
A process for depositing a solar control film of titanium nitride on a transparent, heated glass ribbon substrate, said process including the steps of (a) preparing a gaseous mixture of titanium tetrahalide vapor reactant and an inert carrier gas, (b) preparing a second gas mixture of ammonia reactant, as a nitrogen donor and a reducing gas, and an inert carrier gas, (c) mixing said gas mixtures at a temperature range of from about 200° C. to 400° C. to provide a reaction product; and (d) depositing said reaction product on a said transparent, heated glass substrate.
Claim 13
Dependent Claim
18 words
A process as in claim 10, wherein the substrate is heated to a temperature of above 500° C.
Claim 14
Dependent Claim
16 words
A process as in claim 10, wherein said titanium tetrahalide is titanium tetrabromide or titanium tetraiodide.
Claim 15
Dependent Claim
12 words
A process as defined in claim 10 wherein said tetrahalide is tetrachloride.
Claim 16
Dependent Claim
37 words
A process as defined in claim 10 wherein said mixing of said first and second gas mixtures takes place with said gas mixtures preheated to within a temperature range of from about 250° C. to 320° C.
Claim 17
Dependent Claim
37 words
A process as defined in claim 13 wherein said mixing of said first and second gas mixtures takes place with said gas mixtures preheated to within a temperature range of from about 250° C. to 320° C.
Claim 18
Dependent Claim
37 words
A process as defined in claim 11 wherein said mixing of said first and second gas mixtures takes place with said gas mixtures preheated to within a temperature range of from about 250° C. to 320° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-08-12 | 1989-02-11 | 1989-08-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-08-12 | 1993-02-11 | 1993-08-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-08-12 | 1997-02-11 | 1997-08-13 | $7700.00 | Window Closed / Lapsed |