High thermal conductivity aluminum nitride ceramic body

Claim 2

A polycrystalline aluminum nitride body having a density greater than 85% of the theoretical density for aluminum nitride and a thermal conductivity greater than 0.5 W/cm·K at 22° C., said body consisting essentially of aluminum nitride phase, said body containing oxygen in an amount ranging from greater than about 0.35% by weight up to about 1.1% by weight of said body as determined by neutron activation analysis, said body containing carbon in an amount ranging from a detectable amount to less than about 0.2% by weight of said body, said body being produced by the process which consists essentially of providing at least a substantially uniform particulate mixture comprised of aluminum nitride having a predetermined oxygen content greater than about 0.8% by weight of said particulate aluminum nitride and a carbonaceous additive selected from the group consisting of free carbon, carbonaceous organic material and mixtures thereof, said aluminum nitride having a specific surface area greater than about 4.7 m 2 /g, said carbonaceous organic material pyrolyzing at a temperature ranging from about 50° C. to 1000° C. to free carbon and gaseous product of decomposition which vaporizes away, said free carbon having a specific surface area greater than about 40 m 2 /g, deoxidizing said particulate mixture by heating said mixture in a nonoxidizing atmosphere selected from the group consisting of argon, nitrogen and mixtures thereof to a temperature ranging from about 1350° C. to about 1750° C. pyrolyzing any organic material therein to produce free carbon and reacting the free carbon therein with the oxygen content of said aluminum nitride producing deoxidized powder and gaseous product which vaporizes away, said free carbon being in an amount which produces a deoxidized powder having an oxygen content ranging from greater than about 0.35% by weight to about 1.1% by weight of said deoxidized powder and which is at least about 20% by weight lower than said predetermined oxygen content, shaping the deoxidized powder into a compact and sintering the compact at ambient pressure in a nonoxidizing atmosphere selected from the group consisting of argon, nitrogen and mixtures thereof at a temperature ranging from about 1900° C. to about 2200° C. producing said sintered body, said compact retaining its oxygen content in an amount greater than about 0.35% by weight of said compact during said sintering, said oxygen content being determinable by neutron activation analysis.

Claim 3

A polycrystalline aluminum nitride body having a density greater than 85% of the theoretical density for aluminum nitride and a thermal conductivity greater than 0.5 W/cm·K at 22° C., said body consisting essentially of aluminum nitride phase, said body containing oxygen ranging from greater than about 0.35% by weight up to about 1.1% by weight of said body as determined by neutron activation analysis, said body containing carbon in an amount ranging from a detectable amount to less than about 0.2% by weight of said body, said body being produced by the process which consists essentially of providing at least a substantially uniform particulate mixture comprised of aluminum nitride having a predetermined oxygen content greater than about 0.8% by weight of said particulate aluminum nitride and a carbonaceous additive selected from the group consisting of free carbon, a carbonaceous organic material and mixtures thereof, said aluminum nitride having a specific surface area greater than about 4.7 m 2 /g, said carbonaceous organic material pyrolyzing at a temperature ranging from about 50° C. to 1000° C. to free carbon and gaseous product of decomposition which vaporizes away, said free carbon having a specific surface area greater than about 40 m 2 /g, shaping said mixture into a compact, deoxidizing said compact by heating said compact in a nonoxidizing atmosphere selected from the group consisting of argon, nitrogen and mixtures thereof to a temperature ranging from about 1350° C. up to a temperature at which the pores of the compact remain open pyrolyzing any organic material therein to produce free carbon and reacting the free carbon therein with the oxygen content of said aluminum nitride producing said deoxidized compact and gaseous product which vaporizes away, said free carbon being in an amount which produces a deoxidized compact having an oxygen content ranging from greater than about 0.35% by weight to about 1.1% by weight of said deoxidized compact and which is at least about 20% by weight lower than said predetermined oxygen content, and sintering said deoxidized compact at ambient pressure in a nonoxidizing atmosphere selected from the group consisting of argon, nitrogen and mixtures thereof at a temperature ranging from about 1900° C. to about 2200° C. producing said sintered body, said compact retaining the oxygen content during said sintering in an amount greater than about 0.35% by weight of said compact, said oxygen content being determinable by neutron activation analysis.

Claim 4

A polycrystalline aluminum nitride body having a density greater than 85% of the theoretical density for aluminum nitride and a thermal conductivity greater than 0.5 W/cm·K at 22° C., said body consisting essentially of aluminum nitride phase, said body containing oxygen ranging from greater than about 0.35% by weight up to about 1.1% by weight of said body as determined by neutron activation analysis, said body containing carbon in an amount ranging from a detectable amount to less than about 0.2% by weight of said body, said body being produced by the process which consists essentially of providing at least a substantially uniform particulate mixture comprised of aluminum nitride having a predetermined oxygen content greater than about 0.8% by weight of said particulate aluminum nitride and a carbonaceous additive selected from the group consisting of free carbon, a carbonaceous organic material and mixtures thereof, said aluminum nitride having a specific surface area greater than about 4.7 m 2 /g, said carbonaceous organic material pyrolyzing at a temperature ranging from about 50° C. to 1000° C. to free carbon and gaseous product of decomposition which vaporizes away, said free carbon having a specific surface area greater than about 40 m 2 /g, shaping said mixture into a compact, deoxidizing said compact by heating said compact in a nonoxidizing atmosphere selected from the group consisting of argon, nitrogen and mixtures thereof to a temperature ranging from about 1350° C. up to a temperature at which the pores of the compact remain open pyrolyzing any organic material therein to produce free carbon and reacting the free carbon therein with the oxygen content of said aluminum nitride producing said deoxidized compact and gaseous product which vaporizes away, said free carbon being in an amount which produces a deoxidized compact having an oxygen content ranging from greater than about 0.35% by weight to about 1.1% by weight of said deoxidized compact and which is at least about 20% by weight lower than said predetermined oxygen content, and sintering said deoxidized compact at ambient pressure in a nonoxidizing atmosphere selected from the group consisting of argon, nitrogen and mixtures thereof at a temperature ranging from about 1900° C. to about 2200° C. producing said sintered body, said compact retaining the oxygen content during said sintering in an amount greater than about 0.35% by weight of said compact, said oxygen content being determinable by neutron activation analysis.

Claim 5

A polycrystalline aluminum nitride body having a density greater than 85% of the theoretical density for aluminum nitride and a thermal conductivity greater than 0.5 W/cm·K at 22° C., said body consisting essentially of aluminum nitride phase, said body containing oxygen ranging from greater than about 0.40% by weight up to about 0.9% by weight of said body as determined by neutron analysis, said body containing carbon in an amount ranging from a detectable amount to less than about 0.2% by weight of said body, said body being produced by the process which consists essentially of providing at least a substantially uniform particulate mixture comprised of aluminum nitride having a predetermined oxygen content greater than about 0.8% by weight of said particulate aluminum nitride and a carbonaceous additive selected from the group consisting of free carbon, carbonaceous organic material and mixtures thereof, said aluminum nitride having a specific surface area greater than about 4.7 m 2 /g, said carbonaceous organic material pyrolyzing at a temperature ranging from about 50° C. to 1000° C. to free carbon and gaseous product of decomposition which vaporizes away, said free carbon having a specific surface area greater than about 40 m 2 /g, deoxidizing said particulate mixture by heating said mixture in a nonoxidizing atmosphere selected from the group consisting of argon, nitrogen and mixtures thereof to a temperature ranging from about 1350° C. to about 1750° C. pyrolyzing any organic material therein to produce free carbon and reacting the free carbon therein with the oxygen content of said aluminum nitride producing deoxidized powder and gaseous product which vaporizes away, said free carbon being in an amount which produces a deoxidized powder having an oxygen content ranging from greater than about 0.8% by weight to about 1.1% by weight of said deoxidized powder and which is at least about 20% by weight lower than said predetermined oxygen content, shaping the deoxidized powder into a compact and sintering the compact at ambient pressure in a nonoxidizing atmosphere selected from the group consisting of argon, nitrogen and mixtures thereof at a temperature ranging from about 1900° C. to about 2200° C. producing said sintered body, said compact retaining its oxygen content in an amount greater than about 0.4% by weight of said compact during said sintering, said oxygen content being determinable by neutron activation analysis.

Claim 6

A polycrystalline aluminum nitride body having a density greater than 85% of the theoretical density for aluminum nitride and a thermal conductivity greater than 0.5 W/cm·K at 22° C., said body consisting essentially of aluminum nitride phase, said body containing oxygen ranging from greater than about 0.40% by weight up to about 0.9% by weight of said body as determined by neutron analysis, said body containing carbon in an amount ranging from a detectable amount to less than about 0.2% by weight of said body, said body being produced by the process which consists essentially of providing at least a substantially uniform particulate mixture comprised of aluminum nitride having a predetermined oxygen content greater than about 0.8% by weight of said particulate aluminum nitride and a carbonaceous additive selected from the group consisting of free carbon, carbonaceous organic material and mixtures thereof, said aluminum nitride having a specific surface area greater than about 4.7 m 2 /g, said carbonaceous organic material pyrolyzing at a temperature ranging from about 50° C. to 1000° C. to free carbon and gaseous product of decomposition which vaporizes away, said free carbon having a specific surface area greater than about 40 m 2 /g, deoxidizing said particulate mixture by heating said mixture in a nonoxidizing atmosphere selected from the group consisting of argon, nitrogen and mixtures thereof to a temperature ranging from about 1350° C. to about 1750° C. pyrolyzing any organic material therein to produce free carbon and reacting the free carbon therein with the oxygen content of said aluminum nitride producing deoxidized powder and gaseous product which vaporizes away, said free carbon being in an amount which produces a deoxidized powder having an oxygen content ranging from greater than about 0.8% by weight to about 1.1% by weight of said deoxidized powder and which is at least about 20% by weight lower than said predetermined oxygen content, shaping the deoxidized powder into a compact and sintering the compact at ambient pressure in a nonoxidizing atmosphere selected from the group consisting of argon, nitrogen and mixtures thereof at a temperature ranging from about 1900° C. to about 2200° C. producing said sintered body, said compact retaining its oxygen content in an amount greater than about 0.4% by weight of said compact during said sintering, said oxygen content being determinable by neutron activation analysis.

Claim 7

A polycrystalline aluminum nitride body having a density greater than 85% of the theoretical density for aluminum nitride and a thermal conductivity greater than 0.5 W/cm·K at 22° C., said body consisting essentially of aluminum nitride phase, said body containing oxygen ranging from greater than about 0.40% by weight up to about 0.9% by weight of said body as determined by neutron activation analysis, said body containing carbon in an amount ranging from a detectable amount to less than about 0.2% by weight of said body, said body being produced by the process which consists essentially of providing at least a substantially uniform particulate mixture comprised of aluminum nitride having a predetermined oxygen content greater than about 0.8% by weight of said particulate aluminum nitride and a carbonaceous additive selected from the group consisting of free carbon, a carbonaceous organic material and mixtures thereof, said aluminum nitride having a specific surface area greater than about 4.7 m 2 /g, said carbonaceous organic material pyrolyzing at a temperature ranging from about 50° C. to 1000° C. to free carbon and gaseous product of decomposition which vaporizes away, said free carbon having a specific surface area greater than about 40 m 2 /g, shaping said mixture into a compact, deoxidizing said compact by heating said compact in a nonoxidizing atmosphere selected from the group consisting of argon, nitrogen and mixtures thereof to a temperature ranging from about 1350° C. up to a temperature at which the pores of the compact remain open pyrolyzing any organic material therein to produce free carbon and reacting the free carbon therein with the oxygen content of said aluminum nitride producing said deoxidized compact and gaseous product which vaporizes away, said free carbon being in an amount which produces a deoxidized compact having an oxygen content ranging from greater than about 0.50% by weight up to about 0.9% by weight of said deoxidized compact and which is at least about 20% by weight lower than said predetermined oxygen content, and sintering said deoxidized compact at ambient pressure in a nonoxidizing atmosphere selected from the group consisting of argon, nitrogen and mixtures thereof at a temperature ranging from about 1900° C. to about 2200° C. producing said sintered body, said compact retaining the oxygen content during said sintering in an amount greater than about 0.4% by weight of said compact, said oxygen content being determinable by neutron activation analysis.

Claim 8

A polycrystalline aluminum nitride body having a density greater than 85% of the theoretical density for aluminum nitride and a thermal conductivity greater than 0.5 W/cm·K at 22° C., said body consisting essentially of aluminum nitride phase, said body containing oxygen ranging from greater than about 0.40% by weight up to about 0.9% by weight of said body as determined by neutron activation analysis, said body containing carbon in an amount ranging from a detectable amount to less than about 0.2% by weight of said body, said body being produced by the process which consists essentially of providing at least a substantially uniform particulate mixture comprised of aluminum nitride having a predetermined oxygen content greater than about 0.8% by weight of said particulate aluminum nitride and a carbonaceous additive selected from the group consisting of free carbon, a carbonaceous organic material and mixtures thereof, said aluminum nitride having a specific surface area greater than about 4.7 m 2 /g, said carbonaceous organic material pyrolyzing at a temperature ranging from about 50° C. to 1000° C. to free carbon and gaseous product of decomposition which vaporizes away, said free carbon having a specific surface area greater than about 40 m 2 /g, shaping said mixture into a compact, deoxidizing said compact by heating said compact in a nonoxidizing atmosphere selected from the group consisting of argon, nitrogen and mixtures thereof to a temperature ranging from about 1350° C. up to a temperature at which the pores of the compact remain open pyrolyzing any organic material therein to produce free carbon and reacting the free carbon therein with the oxygen content of said aluminum nitride producing said deoxidized compact and gaseous product which vaporizes away, said free carbon being in an amount which produces a deoxidized compact having an oxygen content ranging from greater than about 0.50% by weight up to about 0.9% by weight of said deoxidized compact and which is at least about 20% by weight lower than said predetermined oxygen content, and sintering said deoxidized compact at ambient pressure in a nonoxidizing atmosphere selected from the group consisting of argon, nitrogen and mixtures thereof at a temperature ranging from about 1900° C. to about 2200° C. producing said sintered body, said compact retaining the oxygen content during said sintering in an amount greater than about 0.4% by weight of said compact, said oxygen content being determinable by neutron activation analysis.

Claim 9

The polycrystalline aluminum nitride body according to claim 1 wherein said atmosphere is nitrogen.

Claim 10

The polycrystalline aluminum nitride body according to claim 1 wherein said density is greater than 90% of the theoretical density for aluminum nitride.

Claim 11

The polycrystalline aluminum nitride body according to claim 1 wherein said density is greater than 95% of the theoretical density for aluminum nitride.

Claim 12

The polycrystalline aluminum nitride body according to claim 2 wherein said atmosphere is nitrogen.

Claim 13

The polycrystalline aluminum nitride body according to claim 2 wherein said density is greater than 90% of the theoretical density for aluminum nitride.

Claim 14

The polycrystalline aluminum nitride body according to claim 2 wherein said density is greater than 95% of the theoretical density for aluminum nitride.

Claim 15

The polycrystalline aluminum nitride body according to claim 3 wherein said atmosphere is nitrogen.

Claim 16

The polycrystalline aluminum nitride body according to claim 3 wherein said density is greater than 90% of the theoretical density for aluminum nitride.

Claim 17

The polycrystalline aluminum nitride body according to claim 3 wherein said density is greater than 95% of the theoretical density for aluminum nitride.

Claim 18

The polycrystalline aluminum nitride body according to claim 4 wherein said atmosphere is nitrogen.

Claim 19

The polycrystalline aluminum nitride body according to claim 4 wherein said density is greater than 90% of the theoretical density for aluminum nitride.

Claim 20

The polycrystalline aluminum nitride body according to claim 4 wherein said density is greater than 95% of the theoretical density for aluminum nitride.