Method for fabricating wrought components for high-temperature gas-cooled reactors and product
Assignee: United States, AS REPRESENTED BY DOE
•
Filing: 1982-02-24
•
Granted: 1985-07-23
•
Expires: 2002-02-24
Abstract
Abstract A method and alloys for fabricating wrought components of a high-temperature gas-cooled reactor are disclosed. These wrought, nickel-based alloys, which exhibit strength and excellent resistance to carburization at elevated temperatures, include aluminum and titanium in amounts and ratios to promote the growth of carburization resistant films while preserving the wrought character of the alloys. These alloys also include substantial amounts of molybdenum and/or tungsten as solid-solution strengtheners. Chromium may be included in concentrations less than 10% to assist in fabrication. Minor amounts of carbon and one or more carbide-forming metals also contribute to high-temperature strength.
Inventors
- 👤 Larry D. Thompson
- 👤 William R. Johnson, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:18
CPC Classifications
C; C22; C22C; C22C19/00; C22C19/03; Y; Y10; Y10S; Y10S376/00; Y10S376/90
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
293 words
A method of fabricating a high-temperature high-strength, carburization-resistant structural component of a high-temperature gas-cooled reactor, said component having a predetermined shape, comprising: forming an alloy consisting essentially of between 0 and about 10 percent by weight chromium, between about 0.02 and about 0.1 percent by weight carbon; between about 0 and 0.2 percent by weight zirconium; between 0 and about 0.2 percent by weight niobium; between 0 and about 0.2 percent by weight vanadium; between 0 and about 0.2 percent by weight tantalum; between 0 and about 0.2 percent by weight of hafnium, at least one of zirconium, niobium, vanadium, tantalum and hafnium being present for forming carbides, the sum of the contents of zirconium, niobium, vanadium, tantalum and hafnium totaling between about 0.02 and about 0.2 weight percent; between 0 and about 20 percent by weight of tungsten; between 0 and about 20 percent by weight of molybdenum, the sum of the tungsten and molybdenum contents totaling between about 6 and about 20 percent by weight; aluminum and titanium, the sum of the aluminum and titanium contents totaling between about 1 and about 5 percent by weight, the ratio of the percentage by weight of aluminum to the percentage by weight of titanium being between about 0.5 and about 2, balance nickel and incidental impurities not detrimental to malleability, strength and carburization resistance at temperatures up to 1050° C.; working the alloy into the predetermined shape; and exposing said worked alloy to an atmosphere having an oxidation potential of between about 10 -21 and about 10 -23 atmospheres at a temperature of between about 850° C. and about 1050° C., whereupon a titanium-stabilized aluminum oxide coating is formed on the surface of said worked alloy that protects said alloy from subsequent carburization.
Claim 2
Independent Claim
293 words
A method of fabricating a high-temperature high-strength, carburization-resistant structural component of a high-temperature gas-cooled reactor, said component having a predetermined shape, comprising: forming an alloy consisting essentially of between 0 and about 10 percent by weight chromium, between about 0.02 and about 0.1 percent by weight carbon; between about 0 and 0.2 percent by weight zirconium; between 0 and about 0.2 percent by weight niobium; between 0 and about 0.2 percent by weight vanadium; between 0 and about 0.2 percent by weight tantalum; between 0 and about 0.2 percent by weight of hafnium, at least one of zirconium, niobium, vanadium, tantalum and hafnium being present for forming carbides, the sum of the contents of zirconium, niobium, vanadium, tantalum and hafnium totaling between about 0.02 and about 0.2 weight percent; between 0 and about 20 percent by weight of tungsten; between 0 and about 20 percent by weight of molybdenum, the sum of the tungsten and molybdenum contents totaling between about 6 and about 20 percent by weight; aluminum and titanium, the sum of the aluminum and titanium contents totaling between about 1 and about 5 percent by weight, the ratio of the percentage by weight of aluminum to the percentage by weight of titanium being between about 0.5 and about 2, balance nickel and incidental impurities not detrimental to malleability, strength and carburization resistance at temperatures up to 1050° C.; working the alloy into the predetermined shape; and exposing said worked alloy to an atmosphere having an oxidation potential of between about 10 -21 and about 10 -23 atmospheres at a temperature of between about 850° C. and about 1050° C., whereupon a titanium-stabilized aluminum oxide coating is formed on the surface of said worked alloy that protects said alloy from subsequent carburization.
Claim 3
Dependent Claim
261 words
A structural component for use in contact with the coolant gas environment of a nuclear reactor, said component being formed of a nickel-based wrought alloy consisting essentially of between 0 and about 10 percent by weight chromium; between about 0.02 and about 0.1 percent by weight carbon; between 0 and about 0.2 percent by weight zirconium; between 0 and about 0.2 percent by weight niobium; between 0 and about 0.2 percent by weight vanadium; between 0 and about 0.2 percent by weight tantalum; between 0 and about 0.2 percent by weight of hafnium; at least one of zirconium, niobium, vanadium, tantalum and hafnium being present for forming carbides, the sum of the zirconium, niobium, vanadium, tantalum and hafnium contents totaling between about 0.02 and about 0.2 percent by weight; between 0 and about 20 percent by weight of tungsten; between 0 and about 20 percent by weight of molybdenum, the sum of the tungsten and molybdenum contents totaling between about 6 and about 20 percent by weight; aluminum and titanium, the sum of the aluminum and titanium contents totaling between about 1 and about 5 percent by weight and the ratio of the percentage by weight of aluminum to the percentage by weight of titanium being between about 0.5 and about 2; balance nickel and incidental impurities; said component having a titanium-stabilized aluminum oxide coating formed by exposure of said alloy component to an atmosphere having an oxidation potential of between about 10 -21 and about 10 -23 atmospheres at a temperature of between about 850° C. and about 1050° C.
Claim 4
Dependent Claim
261 words
A structural component for use in contact with the coolant gas environment of a nuclear reactor, said component being formed of a nickel-based wrought alloy consisting essentially of between 0 and about 10 percent by weight chromium; between about 0.02 and about 0.1 percent by weight carbon; between 0 and about 0.2 percent by weight zirconium; between 0 and about 0.2 percent by weight niobium; between 0 and about 0.2 percent by weight vanadium; between 0 and about 0.2 percent by weight tantalum; between 0 and about 0.2 percent by weight of hafnium; at least one of zirconium, niobium, vanadium, tantalum and hafnium being present for forming carbides, the sum of the zirconium, niobium, vanadium, tantalum and hafnium contents totaling between about 0.02 and about 0.2 percent by weight; between 0 and about 20 percent by weight of tungsten; between 0 and about 20 percent by weight of molybdenum, the sum of the tungsten and molybdenum contents totaling between about 6 and about 20 percent by weight; aluminum and titanium, the sum of the aluminum and titanium contents totaling between about 1 and about 5 percent by weight and the ratio of the percentage by weight of aluminum to the percentage by weight of titanium being between about 0.5 and about 2; balance nickel and incidental impurities; said component having a titanium-stabilized aluminum oxide coating formed by exposure of said alloy component to an atmosphere having an oxidation potential of between about 10 -21 and about 10 -23 atmospheres at a temperature of between about 850° C. and about 1050° C.
Claim 5
Dependent Claim
20 words
The component of claim 2 wherein said tungsten and molybdenum total between about 10 and about 12 percent by weight.
Claim 6
Dependent Claim
19 words
The component of claim 2 wherein said alloy contains between 0 and about 8 percent by weight of chromium.
Claim 7
Dependent Claim
14 words
The component of claim 2 wherein said alloy contains about 0.04 weight percent carbon.
Claim 8
Dependent Claim
25 words
A method according to claim 1 wherein said alloy is formed with a weight percent of aluminum about equal to the weight percent of titanium.
Claim 9
Dependent Claim
12 words
The method according to claim 1 wherein the carbide-forming element is zirconium.
Claim 10
Dependent Claim
18 words
A method according to claim 7 wherein said alloy is formed having about 0.02 percent by weight zirconium.
Claim 11
Dependent Claim
25 words
A method according to claim 1 wherein said alloy is formed with tungsten and molybdenum totalling between about 10 and about 12 percent by weight.
Claim 12
Dependent Claim
17 words
A method according to claim 1 wherein said alloy is formed having about 0.04% by weight carbon.
Claim 13
Dependent Claim
28 words
A method according to claim 1, forming said alloy with a controlled amount of boron so that boron comprises between about 0 and about 2 parts per million.
Claim 14
Dependent Claim
29 words
The method according to claim 1, forming said alloy with a controlled amount of cobalt is so that cobalt comprises between about 0 and about 0.01 percent by weight.
Claim 15
Dependent Claim
28 words
The component of claim 2 further characterized in that the ratio of the percentage by weight of aluminum to the percentage by weight of titanium is about 1.
Claim 16
Dependent Claim
18 words
The component of claim 2 further characterized in that zirconium is the element selected from the carbide-forming group.
Claim 17
Dependent Claim
21 words
The component of claim 2 further characterized in that the concentration of boron is between 0 and 2 parts per million.
Claim 18
Dependent Claim
22 words
The component of claim 2 further characterized in that the concentration of cobalt is between 0 and about 0.01 percent by weight.
References Cited (Backward Citations)
US28681A
Cited
US2977222A
Cited
US2920956A
Cited
US2912323A
Cited
US3093476A
Cited
US2975051A
Cited
US2971838A
Cited
US3094414A
Cited
US3228095A
Cited
US3293030A
Cited
US3166412A
Cited
US3376132A
Cited
US3322534A
Cited
US3390023A
Cited
US3479157A
Cited
US3524744A
Cited
US3565611A
Cited
US3615376A
Cited
US3576681A
Cited
US3726722A
Cited
US3723101A
Cited
US3874938A
Cited
US3902900A
Cited
US3748192A
Cited
US3850624A
Cited
USRE28681E
Cited
US3973952A
Cited
US3941590A
Cited
US4126495A
Cited
US3976480A
Cited
US4140555A
Cited
US4078951A
Cited
US4152488A
Cited
US4245698A
Cited
US4236943A
Cited
US4226644A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-22 | 1989-01-21 | 1989-07-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-22 | 1993-01-21 | 1993-07-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-22 | 1997-01-21 | 1997-07-23 | $7700.00 | Window Closed / Lapsed |