Methods of forming a protective diffusion layer on nickel, cobalt, and iron base alloys
Assignee: Turbine Components Corp
•
Filing: 1982-11-19
•
Granted: 1985-07-02
•
Expires: 2002-11-19
Abstract
Abstract Methods are provided for forming protective diffusion layers on nickel, cobalt and iron base alloy parts comprising the formation of a diffusion layer of platinum, chromium and aluminum on said surfaces either by deposition of platinum and gas phase chromizing followed by aluminizing or by gas phase chromizing and deposition of platinum followed by aluminizing, or by gas phase chromizing followed by aluminizing and deposition of platinum, said gas phase chromizing performed out of contact with a source of gaseous chromizing species at elevated temperature, said aluminizing performed either out of contact or in contact with a powder mixture at elevated temperature.
Inventors
- 👤 Srinivasan Shankar
- 👤 G. William Goward
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 23:23
CPC Classifications
C; C23; C23C; C23C10/00; C23C10/06; C23C10/16; C23C10/28; C23C10/34; C23C10/58
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
98 words
A method for forming a protective diffusion layer of chromium, platinum group metal and aluminum on nickel, cobalt and iron base alloy parts comprising the steps of depositing a coating of a platinum group metal on the surface of the part to be protected, forming a diffusion layer of platinum group metal and chromium on said surfaces by gas phase chromizing said surfaces out of contact with a source of gaseous chromizing species at elevated temperature, and forming a diffusion layer of platinum group metal, chromium and aluminum on said surfaces by aluminizing said surfaces at elevated temperature.
Claim 2
Independent Claim
98 words
A method for forming a protective diffusion layer of chromium, platinum group metal and aluminum on nickel, cobalt and iron base alloy parts comprising the steps of depositing a coating of a platinum group metal on the surface of the part to be protected, forming a diffusion layer of platinum group metal and chromium on said surfaces by gas phase chromizing said surfaces out of contact with a source of gaseous chromizing species at elevated temperature, and forming a diffusion layer of platinum group metal, chromium and aluminum on said surfaces by aluminizing said surfaces at elevated temperature.
Claim 3
Dependent Claim
83 words
A method for forming a protective diffusion layer on nickel, cobalt, and iron base alloy parts as claimed in claim 1 comprising the steps of forming a diffusion layer of chromium by gas phase chromizing on the surface of the part to be protected, depositing a coating of a platinum group metal on the surface of the part to be protected, and forming a diffusion layer of chromium, platinum group metal, and aluminum on said surface by aluminizing said surfaces at elevated temperature.
Claim 4
Dependent Claim
79 words
A method for forming a protective diffusion layer on nickel, cobalt, and iron base alloy parts as claimed in claim 1 comprising the steps of forming a diffusion layer of chromium by gas phase chromizing on the surface of the part to be protected, followed by formation of a diffusion layer of chromium and aluminum by aluminizing said surfaces at elevated temperature, followed by deposition of a platinum group metal on the surface of the part to be protected.
Claim 5
Dependent Claim
16 words
The method of claim 1 or 2 or 3 wherein the platinum group metal is platinum.
Claim 6
Dependent Claim
29 words
The method of claim 1 or 2 or 3 wherein the platinum group metal coating is applied by one of electroplating, dipping, spraying, vapor deposition, sputtering, and mechanical plating.
Claim 7
Dependent Claim
25 words
A method as claimed in claim 4 wherein the platinum coating is applied by one of electroplating, dipping, spraying, vapor deposition, sputtering, and mechanical plating.
Claim 8
Dependent Claim
44 words
The method as claimed in claim 1 or 2 or 3 wherein the gas phase chromizing is carried out by holding the part at elevated temperature above and spaced from a mixture consisting of a source of chromium, and activator, and an inert filler.
Claim 9
Dependent Claim
40 words
A method as claimed in claim 4 wherein the gas phase chromizing is carried out by holding the part at elevated temperature above and spaced from a pack consisting of a source of chromium, an activator and an inert filler.
Claim 10
Dependent Claim
37 words
A method as claimed in claim 6 wherein the gas phase chromizing is carried out by holding the part above and spaced from a pack consisting of a source of chromium, an activator, and an inert filler.
Claim 11
Dependent Claim
33 words
The method as claimed in claim 1 or 2 or 3 wherein the part coated with platinum group metal is heated to diffuse the platinum group metal into the surfaces of the part.
Claim 12
Dependent Claim
35 words
A method as claimed in claim 10 wherein the part is heated to a temperature between about 1500° F. and 2000° F. in one of a vacuum or inert atmosphere for one to five hours.
Claim 13
Dependent Claim
25 words
A method as claimed in claim 4 wherein the part coated with platinum is heated to diffuse the platinum into the surfaces of the part.
Claim 14
Dependent Claim
35 words
A method as claimed in claim 13 wherein the part is heated to a temperature between about 1500° F. and 2000° F. in one of a vacuum or inert atmosphere for one to five hours.
Claim 15
Dependent Claim
45 words
The method as claimed in claim 1 or 2 or 3 wherein gas phase chromizing is carried out at a temperature between about 1200° F. and 2100° F. in one of a vacuum, an inert atmosphere and a reducing atmosphere for 1 to 20 hours.
Claim 16
Dependent Claim
41 words
A method as claimed in claim 4 wherein gas phase chromizing is carried out at a temperature between about 1200° F. and 2100° F. in one of a vacuum, an inert atmosphere and a reducing atmosphere for 1 to 20 hours.
Claim 17
Dependent Claim
41 words
A method as claimed in claim 6 wherein the mixture consists essentially of about 1 to 35% of one or more of the group consisting of chromium and chromium alloys, up to about 40% activator and the balance aluminum oxide filler.
Claim 18
Dependent Claim
41 words
A method as claimed in claim 8 wherein the mixture consists essentially of about 1 to 35% of one or more of the group consisting of chromium and chromium alloys, up to about 40% activator and the balance aluminum oxide filler.
Claim 19
Dependent Claim
39 words
The method as claimed in claim 1 or 2 or 3 wherein the aluminizing is carried out at elevated temperature in a mixture or above a mixture consisting of a source of aluminum, an activator, and an inert filler.
Claim 20
Dependent Claim
35 words
A method as claimed in claim 4 wherein the aluminizing is carried out at elevated temperature in a mixture or above a mixture consisting of a source of aluminum, an activator, and an inert filler.
Claim 21
Dependent Claim
35 words
A method as claimed in claim 6 wherein the aluminizing is carried out at elevated temperature in a mixture or above a mixture consisting of a source of aluminum, an activator, and an inert filler.
Claim 22
Dependent Claim
44 words
The method as claimed in claim 1 or 2 or 3 wherein the aluminizing is carried out at a temperature between about 1200° F. and 2100° F. in one of a vacuum, an inert atmosphere and a reducing atmosphere for 1 to 20 hours.
Claim 23
Dependent Claim
39 words
A method as claimed in claim 4 wherein the aluminizing is carried out at temperature between about 1200° F. and 2100° F. in one of a vacuum, an inert atmosphere and a reducing atmosphere for 1 to 20 hours.
Claim 24
Dependent Claim
41 words
A method as claimed in claim 18 wherein the mixture consists essentially of about 1 to 35% of one or more of the group consisting of aluminum and aluminum alloys, up to about 40% activator and the balance aluminum oxide filler.
Claim 25
Dependent Claim
41 words
A method as claimed in claim 19 wherein the mixture consists essentially of about 1 to 35% of one or more of the group consisting of aluminum and aluminum alloys, up to about 40% activator and the balance aluminum oxide filler.
Claim 26
Dependent Claim
35 words
A method as claimed in claim 7 wherein the aluminizing is carried out at elevated temperature in a mixture or above a mixture consisting of a source of aluminum, an activator, and an inert filler.
Claim 27
Dependent Claim
35 words
A method as claimed in claim 8 wherein the aluminizing is carried out at elevated temperature in a mixture or above a mixture consisting of a source of aluminum, an activator, and an inert filler.
Claim 28
Dependent Claim
35 words
A method as claimed in claim 25 wherein the aluminizing is carried out at elevated temperature in a mixture or above a mixture consisting of a source of aluminum, an activator, and an inert filler.
Claim 29
Dependent Claim
40 words
A method as claimed in claim 14 wherein the aluminizing is carried out at a temperature between about 1200° F. and 2100° F. in one of a vacuum, an inert atmosphere, and a reducing atmosphere for 1 to 20 hours.
Claim 30
Dependent Claim
40 words
A method as claimed in claim 15, wherein the aluminizing is carried out at a temperature between about 1200° F. and 2100° F. in one of a vacuum, an inert atmosphere, and a reducing atmosphere for 1 to 20 hours.
References Cited (Backward Citations)
US4041196A
Cited
US4070507A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-01 | 1988-12-31 | 1989-07-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-01 | 1992-12-31 | 1993-07-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-01 | 1996-12-31 | 1997-07-02 | $7700.00 | Window Closed / Lapsed |