US4070507A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Platinum-rhodium-containing high temperature alloy coating method
Assignee: Chromalloy Gas Turbine Corp
•
Filing: 1976-07-29
•
Granted: 1978-01-24
•
Expires: 1996-07-29
Abstract
Abstract Aluminized nickel-base, cobalt-base and nickel-cobalt-base heat resistant alloy substrates are provided in which, prior to aluminizing the substrate, the substrate is provided with a thin coating of rhodium and thereafter a thin coating of platinum, the coatings being diffusion bonded to the substrate, such that when the prepared substrate is aluminized by pack cementation, a compositely structured coating is obtained characterized by improved resistance to high temperature oxidation and sulfidation.
Inventors
- 👤 Richard J. Stueber
- 👤 Stanley J. Klach
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 21:21
CPC Classifications
C; C23; C23C; C23C10/00; C23C10/28; C23C10/34; C23C10/58; Y; Y02; Y02T; Y02T50/00; Y02T50/60; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/923; Y10S428/924; Y10S428/925; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12861; Y10T428/12875; Y10T428/12931
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
236 words
A method for improving the heat and corrosion resistance of a heat resistant article formed of an alloy selected from the group consisting of nickel-base, cobalt-base and nickel-cobalt-base alloys which comprises, providing said articles with a clean surface for receiving a metal coating, thermally diffusing first and second coatings of rhodium and platinum into the surface of said article, said rhodium and platinum having been applied to said article prior to diffusion therein as first and second coatings, respectively, at a Rh/Pt thickness ratio of about 0.5/1 to 2.5/1 at thicknesses of each ranging from about 0.00005 inch to 0.002 inch, and then pack aluminizing said article at an elevated aluminizing temperature by embedding it in a cementation pack containing by weight about 5 to 40% chromium metal and about 1/8 to 20% aluminum sufficient to effect the diffusion coating thereof into the surface of said article, said pack also containing about 1/8 to 2% of a vaporizable halogen material as a carrier for said aluminum, thereby producing a multi-layered protective coating characterized metallographically by an outer zone containing platinum and an inner zone substantially adjacent the surface of the article containing rhodium with an intermediate zone enriched in aluminum in the form of at least one intermetallic compound selected from the group consisting of nickel aluminide in the case of nickel-base and nickel-cobalt-base alloys, and cobalt aluminide in the case of nickel-cobalt-base and cobalt-base alloys.
Claim 2
Independent Claim
236 words
A method for improving the heat and corrosion resistance of a heat resistant article formed of an alloy selected from the group consisting of nickel-base, cobalt-base and nickel-cobalt-base alloys which comprises, providing said articles with a clean surface for receiving a metal coating, thermally diffusing first and second coatings of rhodium and platinum into the surface of said article, said rhodium and platinum having been applied to said article prior to diffusion therein as first and second coatings, respectively, at a Rh/Pt thickness ratio of about 0.5/1 to 2.5/1 at thicknesses of each ranging from about 0.00005 inch to 0.002 inch, and then pack aluminizing said article at an elevated aluminizing temperature by embedding it in a cementation pack containing by weight about 5 to 40% chromium metal and about 1/8 to 20% aluminum sufficient to effect the diffusion coating thereof into the surface of said article, said pack also containing about 1/8 to 2% of a vaporizable halogen material as a carrier for said aluminum, thereby producing a multi-layered protective coating characterized metallographically by an outer zone containing platinum and an inner zone substantially adjacent the surface of the article containing rhodium with an intermediate zone enriched in aluminum in the form of at least one intermetallic compound selected from the group consisting of nickel aluminide in the case of nickel-base and nickel-cobalt-base alloys, and cobalt aluminide in the case of nickel-cobalt-base and cobalt-base alloys.
Claim 3
Dependent Claim
42 words
The method of claim 1, wherein said rhodium and platinum coatings applied to the article are thermally diffused into the surface of the article prior to aluminizing by heating to an elevated temperature in the range of about 1010° to 1150° C.
Claim 4
Dependent Claim
56 words
The method of claim 2, wherein the rhodium first applied to said article surface prior to aluminizing the thermally diffused by heating to said elevated temperature and wherein platinum is applied to said thermally diffused rhodium layer followed by then thermally diffusing said platinum into said article surface prior to aluminizing said article by pack cementation.
Claim 5
Dependent Claim
29 words
The method of claim 2, wherein the rhodium and the platinum, respectively, applied to the surface of the article are simultaneously thermally diffused therein at said elevated diffusion temperature.
Claim 6
Dependent Claim
139 words
The method of claim 1, wherein said alloy article treated has the following composition containing by weight up to about 30% Cr, up to about 20% of a metal selected from the group consisting of Mo and W, up to about 10% of a metal selected from the group consisting of Cb and Ta, up to about 1% C, up to about 10% by weight of a metal selected from the group consisting of Ti and Al, the total amount of Ti and Al not exceeding about 12%, up to about 20% Fe, up to about 2% Mn, up to about 2Si, up to about 0.2% B, up to about 1% Zr, up to about 2% Hf, and the balance at least 45% by weight of at least one metal selected from the group consisting of nickel and cobalt.
References Cited (Backward Citations)
US3257230A
Cited
US3494748A
Cited
US3677789A
Cited
US3819338A
Cited
US3692554A
Cited
US3957454A
Cited
US3961910A
Cited
US3978251A
Cited
US3976436A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-23 | 1981-07-25 | 1982-01-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-23 | 1985-07-25 | 1986-01-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-23 | 1989-07-25 | 1990-01-24 | $7700.00 | Window Closed / Lapsed |