Low cost method of making superplastically formed and diffusion bonded structures
Assignee: Boeing North American Inc
•
Filing: 1979-12-10
•
Granted: 1985-07-02
•
Expires: 1999-12-10
Abstract
Abstract A method of making metallic sandwich structures is disclosed using a plurality of metal blank workpieces with at least one of the blank workpieces capable of being superplastically formed against a surface of a die. At least one of the blanks is treated at selective areas to prevent bonding in those areas. The blanks are positioned in a stack with at least one of the outer workpieces of the stack having the capacity to be superplastically formed. The stack is then diffusion bonded together in the untreated areas. At least one insert, preferably made from wax, is coupled to the bonded stack such that the external configuration of the at least one insert and bonded stack conform to the external configuration of the sandwich structure. A mold is cast around the at least one insert and bonded stack, after which the at least one insert is removed from the mold. Thereafter, the bonded stack is superplastically formed within the cast mold, resulting in the desired sandwich structure. In a second embodiment, wherein the metallic structure has a curvature, the stack may be either formed to the curvature of the sandwich structure and then diffusion bonded or simultaneously formed to the curvature of the sandwich structure and diffusion bonded in the untreated areas of the blanks. Thereafter, at least one insert is coupled to the curved and diffusion bonded stack, such that the combination has the external configuration of the sandwich structure to be formed. A mold is then cast about the curved and bonded stack and the at least one insert, after which the insert is removed from the mold. The curved and bonded stack is then superplastically formed in the cast mold to sandwich structure.
Inventors
- 👤 Joseph R. Goss
- 👤 David W. Schulz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 11:42
CPC Classifications
B; B21; B21D; B21D26/00; B21D26/02; B21D26/053; B21D26/055; B23; B23K; B23K20/00; B23K20/02; B23K20/18
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
149 words
A method of making a metallic structure comprising: providing a plurality of metal blank workpieces, each of said workpieces having two opposed principal surfaces, at least one of said workpieces having superplastic characteristics; treating said workpieces at selected areas to prevent bonding at those areas; positioning said workpieces in a stack, contacting at their principal surfaces, at least one of the outer workpieces of said stack having superplastic characteristics; diffusion bonding said stack together in the untreated areas; coupling at least one insert to said stack, such that said at least one insert and said bonded stack conform to the external configuration of said structure; casting a mold about said at least one insert and said stack; removing said at least one insert from said cast mold; and expanding by superplastic forming at least one of said workpieces having superplastic characteristics against said cast mold to form said structure.
Claim 2
Independent Claim
149 words
A method of making a metallic structure comprising: providing a plurality of metal blank workpieces, each of said workpieces having two opposed principal surfaces, at least one of said workpieces having superplastic characteristics; treating said workpieces at selected areas to prevent bonding at those areas; positioning said workpieces in a stack, contacting at their principal surfaces, at least one of the outer workpieces of said stack having superplastic characteristics; diffusion bonding said stack together in the untreated areas; coupling at least one insert to said stack, such that said at least one insert and said bonded stack conform to the external configuration of said structure; casting a mold about said at least one insert and said stack; removing said at least one insert from said cast mold; and expanding by superplastic forming at least one of said workpieces having superplastic characteristics against said cast mold to form said structure.
Claim 3
Dependent Claim
32 words
The method of claim 1 wherein said structure has a curvature and also including the step of superplastically forming said stack to a curvature substantially equal to said curvature of said structure.
Claim 4
Dependent Claim
25 words
The method of claim 2 wherein the step of superplastically forming said stack to a curvature is accomplished substantially with the step of diffusion bonding.
Claim 5
Dependent Claim
77 words
The method of claim 1 or 2 or 3 wherein the step of coupling at least one insert comprises: enclosing said stack in a formed mold having an internal cavity complementary to the external configuration of said structure; flowing a liquid into said mold, filling the space between said stack and said cavity; solidifying said liquid forming said at least one insert; and removing said formed mold from about said at least one insert and said stack.
Claim 6
Dependent Claim
67 words
The method of claim 4 wherein said liquid is a wax heated to a liquid state; and the step of solidifying said liquid comprises cooling said liquid to about room temperature; and the step of removing said at least one insert from said cast mold comprises: heating said at least one insert to a temperature where it liquifies; and withdrawing said liquid insert from said cast mold.
Claim 7
Dependent Claim
24 words
The method of claim 1 or 2 or 3 wherein said at least one of said workpieces having superplastic characteristics is a titanium alloy.
Claim 8
Dependent Claim
21 words
The method of claim 1 or 2 or 3 wherein said treatment comprises coating said selected areas with a stop-off compound.
Claim 9
Dependent Claim
11 words
The method of claim 7 wherein said stop-off compound is Yttria.
Claim 10
Dependent Claim
92 words
The method of claim 1 or 2 or 3 wherein the step of casting a mold comprises: dipping said stacked workpieces and said at least one insert in and out of a ceramic slurry containing a binder; dipping said stacked workpieces and said at least one insert in and out of a fluidized bed of ceramic material such that a coating is formed thereon; curing said coating on said workpieces and said at least one insert; and repeating said dipping and curing steps until the desired thickness of said mold is achieved.
Claim 11
Dependent Claim
18 words
The method of claim 9 wherein said binder is ethyl silicate and said ceramic material is silicon dioxide.
Claim 12
Dependent Claim
168 words
The method of claim 1 wherein the step of treating said workpieces comprises coating said selected areas with a stop-off compound; the step of coupling at least one insert comprises: enclosing said stack in a formed mold having an internal cavity complimentary to the external configuration of said structure; flowing a liquid into said mold, filling the space between said stack and said cavity; solidifying said liquid forming said at least one insert; and removing said formed mold from about said at least one insert and said stack; and the step of casting a mold comprises: dipping said stacked workpieces and said at least one insert in and out of a ceramic slurry containing a binder; dipping said stacked workpieces and said at least one insert in and out of a fluidized bed of ceramic material forming a coating thereon; curing said coating on said workpieces and said at least one insert; and repeating said dipping and curing steps until the desired thickness of said mold is achieved.
Claim 13
Dependent Claim
33 words
The method of claim 9 also including the steps of: pouring a ceramic slurry around said cast mold; and curing said poured ceramic slurry to form a reinforcement mold around said cast mold.
Claim 14
Dependent Claim
35 words
The method of claim 1 or 11 also including the steps of: pouring a ceramic slurry around said cast mold; and curing said poured ceramic slurry to form a reinforcement mold around said cast mold.
Claim 15
Dependent Claim
23 words
The method of claim 1 wherein said casting step is performed such that said mold has sufficient strength to withstand said expanding step.
Claim 16
Dependent Claim
23 words
The method of claim 9 wherein said casting step is performed such that said mold has sufficient strength to withstand said expanding step.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-01 | 1988-12-31 | 1989-07-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-01 | 1992-12-31 | 1993-07-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-01 | 1996-12-31 | 1997-07-02 | $7700.00 | Window Closed / Lapsed |