Polymer-modified cement mortars and concretes and processes for the production thereof
Assignee: Marley Tile AG
•
Filing: 1982-07-06
•
Granted: 1985-06-25
•
Expires: 2002-07-06
Abstract
Abstract The invention provides articles made of polymer-modified cement mortars and concretes and processes for the production thereof. The processes comprise curing compositions which contain hydraulic cement and aqueous dispersions of polymers or copolymers of methacrylic or acrylic acid esters by means of a two stage curing process the first stage of which is carried out at an elevated temperature under conditions of high humidity and the second stage of which is carried out under drying conditions, preferably at elevated temperatures. The cement mortar and concrete articles according to the invention have relatively high Modulus of Rupture (MOR) values and preferably are roof tiles or shingles or other articles of relatively thin cross-section.
Inventors
- 👤 Michael E. Lynn
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 12:47
CPC Classifications
C; C04; C04B; C04B40/00; C04B40/02; C04B24/00; C04B24/24; C04B24/26; C04B24/2641
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
156 words
A process for the production of mortars and concretes which comprises curing a composition which contains hydraulic cement and an aqueous dispersion of a polymer or copolymer of a methacrylic or acrylic acid ester by means of a two stage curing process, the first stage being carried out at an elevated temperature under conditions of high humidity whereby hydration of the cement is effected, and the second stage being carried out under drying conditions and elevated temperature whereby curing of the polymer or copolymer is effected, the said polymer or copolymer dispersion having a viscosity of less than 1,500 cps when measured by means of a Brookfield LVT viscometer using spindle 2, 12 rpm at a temperature of 23° C., and a minimum film-forming temperature (MFT) of not lower than 5° C., wherein the polymer or copolymer is present in an amount of from 10 to 40% based upon the weight of cement in the composition.
Claim 2
Dependent Claim
156 words
A process for the production of mortars and concretes which comprises curing a composition which contains hydraulic cement and an aqueous dispersion of a polymer or copolymer of a methacrylic or acrylic acid ester by means of a two stage curing process, the first stage being carried out at an elevated temperature under conditions of high humidity whereby hydration of the cement is effected, and the second stage being carried out under drying conditions and elevated temperature whereby curing of the polymer or copolymer is effected, the said polymer or copolymer dispersion having a viscosity of less than 1,500 cps when measured by means of a Brookfield LVT viscometer using spindle 2, 12 rpm at a temperature of 23° C., and a minimum film-forming temperature (MFT) of not lower than 5° C., wherein the polymer or copolymer is present in an amount of from 10 to 40% based upon the weight of cement in the composition.
Claim 3
Dependent Claim
24 words
A process according to claim 1 in which the polymer or copolymer dispersion is stable at alkaline pHs of at least 8 and above.
Claim 4
Dependent Claim
19 words
A process according to claim 2 in which the polymer or copolymer dispersion has a pH of above 8.
Claim 5
Dependent Claim
37 words
A process according to claim 1 in which the aqueous dispersion contains a copolymer of (i) an alkyl methacrylate or acrylate in which the alkyl groups have from 1 to 8 carbon atoms and (ii) acrylic acid.
Claim 6
Dependent Claim
31 words
A process according to claim 1 in which the said composition contains as aggregate sand having a porosity of less than 1.5% (when measured according to British Standard 812:1967) and/or cenospheres.
Claim 7
Dependent Claim
38 words
A process according to claim 1, 2, 3, 4, or 5 in which the first stage of the curing process is effected at a temperature of at least 35° C. and a relative humidity of at least 75%.
Claim 8
Dependent Claim
16 words
A process according to claim 1 wherein the said polymer or copolymer dispersion comprises Primal B-60A.
Claim 9
Dependent Claim
28 words
A process according to claim 1 or 7 in which the second stage of the curing process is effected at a relative humidity of not greater than 50%.
Claim 10
Dependent Claim
48 words
Moulded articles having a thickness in section of not greater than 25 mm, said articles being made of mortars or concretes modified by means of polymer or copolymer dispersions as defined in claim 1 and having Modulus of Rupture (MOR) values in excess of 22.5 MNm -2 .
Claim 11
Dependent Claim
15 words
Articles according to claim 9 having MOR values in excess of 25 MNm -2 .
Claim 12
Dependent Claim
77 words
Moulded articles having a thickness in section of not greater than 25 mm, said articles being made of mortars or concretes containing cenospheres as lightweight aggregate, having a dry density not greater than half that of cement mortar made using a conventional mix with a ratio of sand to cement of 3.5:1, being modified by means of polymer or copolymer dispersions as defined in claim 1 and having MOR values of at least 12 MNm -2 .
Claim 13
Dependent Claim
13 words
Articles according to claim 11 in the form of roof tiles and shingles.
Claim 14
Dependent Claim
13 words
Articles according to claim 11 in the form of roof tiles and shingles.
References Cited (Backward Citations)
US3806571A
Cited
US3634567A
Cited
US3819565A
Cited
US3781396A
Cited
US3947398A
Cited
US3850651A
Cited
US4002713A
Cited
US3879909A
Cited
JPS5166316A
Cited
US4070199A
Cited
US4240840A
Cited
GB2001261A
Cited
US4125504A
Cited
US4229224A
Cited
US4410366A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-24 | 1988-12-24 | 1989-06-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-24 | 1992-12-24 | 1993-06-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-24 | 1996-12-24 | 1997-06-25 | $7700.00 | Window Closed / Lapsed |