Process for producing glass product having gradient of refractive index
Assignee: Hoya Corp
•
Filing: 1983-04-26
•
Granted: 1985-06-25
•
Expires: 2003-04-26
Abstract
Abstract A process for producing a glass product having Δn, the difference between the central and peripheral portions of the glass, greater than 0.04. This process utilizes a porous glass body which is produced via a phase separation technique. A dopant selected from the group consisting of (1) TlNO 3 , (2) TlNO 3 and an alkali metal compound and (3) TlNO 3 , Pb(NO 3 ) 2 and an alkali metal compound is then permeated into the micropores of the porous glass product. A concentration gradient of the dopant is then formed by leaching out a portion of the dopant from the micropores. After the dopant is solidified in the micropores, the porous glass product is dried. A heat-treatment step then serves to collapse the micropores. A glass product having a gradient of refractive indices is thereby obtained.
Inventors
- 👤 Shigeaki Ohmi
- 👤 Seiichi Shingaki
- 👤 Hiroyuki Sakai
- 👤 Yoshiyuki Asahara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 01:21
CPC Classifications
C; C03; C03C; C03C23/00; C03C23/0095; C03B; C03B19/00; C03B19/12; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/016; C03C13/00; C03C13/04; C03B2201/00; C03B2201/06; C03B2201/30; C03B2201/50
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
188 words
A process for producing a glass product having a gradient of refractive indices which comprises: (a) producing a porous glass body by: (1) heating a glass body to effectuate a phase separation; (2) leaching out the acid-soluble phase from said glass body; and then (3) recovering therefrom the porous glass body; (b) permeating a solution of dopant comprising TlNO 3 and an alkali metal nitrate into the micropores of said porous glass product wherein the concentration of said TlNO 3 is between 100 to 400 g/100 ml of H 2 O the concentration of said alkali metal nitrate is at least 20 g/100 ml of water; (c) leaching out a portion of the dopant from the micropores with or without solidifying the dopant in the micropores to form a concentration gradient of the dopant in said porous glass product, (d) solidifying the dopant in the micropores, (e) drying the porous glass product, (f) heat treating said porous glass product to collapse the micropores, and (g) recovering a glass product having Δn greater than 0.04 wherein Δn is the difference between the central and peripheral portions of the glass.
Claim 2
Dependent Claim
188 words
A process for producing a glass product having a gradient of refractive indices which comprises: (a) producing a porous glass body by: (1) heating a glass body to effectuate a phase separation; (2) leaching out the acid-soluble phase from said glass body; and then (3) recovering therefrom the porous glass body; (b) permeating a solution of dopant comprising TlNO 3 and an alkali metal nitrate into the micropores of said porous glass product wherein the concentration of said TlNO 3 is between 100 to 400 g/100 ml of H 2 O the concentration of said alkali metal nitrate is at least 20 g/100 ml of water; (c) leaching out a portion of the dopant from the micropores with or without solidifying the dopant in the micropores to form a concentration gradient of the dopant in said porous glass product, (d) solidifying the dopant in the micropores, (e) drying the porous glass product, (f) heat treating said porous glass product to collapse the micropores, and (g) recovering a glass product having Δn greater than 0.04 wherein Δn is the difference between the central and peripheral portions of the glass.
Claim 3
Dependent Claim
14 words
The process of claim 1, wherein the alkali metal nitrate is CsNO 3 .
Claim 4
Dependent Claim
30 words
The process of claim 1, wherein a solvent for the dopant is selected from the group consisting of water, an organic solvent, and a mixture of water and organic solvent.
Claim 5
Dependent Claim
24 words
The process of claim 1 wherein the concentration of said alkali metal nitrate is between 100 to 200 g/100 ml of H 2 O.
Claim 6
Dependent Claim
15 words
The process of claim 1, wherein said dopant further comprises Pb(NO 3 ) 2 .
Claim 7
Dependent Claim
24 words
The process of claim 5, wherein the concentration of said Pb(NO 3 ) 2 is at least 20 g/100 ml of H 2 O.
Claim 8
Dependent Claim
44 words
The process of claim 6, wherein the concentration of said Pb(NO 3 ) 2 is between 80 to 120 g/100 ml of H 2 O, and the concentration of said alkali metal nitrate is between 100 to 200 g/100 ml of H 2 O.
References Cited (Backward Citations)
US3938974A
Cited
US4110093A
Cited
US4110096A
Cited
US4225330A
Cited
GB2084990A
Cited
US4389233A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-24 | 1988-12-24 | 1989-06-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-24 | 1992-12-24 | 1993-06-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-24 | 1996-12-24 | 1997-06-25 | $7700.00 | Window Closed / Lapsed |