Process for the production of an optical glass article
Assignee: Sumitomo Electric Industries Ltd
•
Filing: 1981-09-11
•
Granted: 1983-06-21
•
Expires: 2001-09-11
Abstract
Abstract This invention relates to a process for the production of an optical glass article, which comprises neutralizing an aqueous solution containing silicic acid to form a porous gelled body, removing soluble materials from the porous gelled body to form a porous glass body, stuffing the porous glass body with a solution containing at least one compound capable of being converted into an oxide dopant for changing the refractive index of the glass body, selected from the group consisting of CsNO 3 , RbNO 3 and TlNO 3 , unstuffing the glass body with a solvent or solution having a suitable composition at a suitable temperature to leach the compound out of the outside glass body and to give a predetermined concentration distribution in the micropores of the glass body, optionally immersing the unstuffed body in an organic solvent, precipitating the compound in the micropores, drying the glass body in a predetermined atmosphere to decompose the compound, further heating at a higher temperature, and then firing at a temperature sufficiently high to completely decompose the compound and to completely burn the organic materials, but lower than the melting point of silica.
Inventors
- 👤 Shiro Kurosaki
- 👤 Minoru Watanabe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 19:55
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/016; C03C; C03C13/00; C03C13/04; C03C13/045; C03C23/00; C03C23/008; C03B2201/00; C03B2201/06; C03B2201/30; C03B2201/50; Y; Y10; Y10S; Y10S65/00; Y10S65/901
Claims Analysis
Total Claims: 40
Claim 1
Independent Claim
338 words
A process for producing an optical glass article, which comprises preparing at least two solutions having a pH of 10 to 15 and an SiO 2 content of about 1 to 12 mols/l and containing at least one silicate selected from the group consisting of lithium polysilicate, sodium silicate, potassium silicate, rubidium silicate, cesium silicate, thallium silicate, quaternary ammonium silicate and colloidal silica, combining these solutions to form a mixed solution, reacting the mixed solution with at least one organic compound selected from the group consisting of formaldehyde, paraformaldehyde, formamide, glyoxal, methyl formate, ethyl formate, methyl acetate and ethyl acetate at a temperature from the freezing point to the boiling point of the reaction solution in a time sufficient to polymerize silica and form a porous gelled body, leaching the porous gelled body with a leaching solution selected from the group consisting of water, an aqueous solution of an inorganic acid and an aqueous solution of an organic material, capable of dissolving residues in the porous gelled body, until the leaching reaches the central part of the porous gelled body, to form a porous glass body having micropores therein, stuffing the porous glass body with a solution containing at least one compound capable of being converted into an oxide dopant for changing the refractive index of the porous glass body, selected from the group consisting of CsNO 3 , RbNO 3 and TlNO 3 , unstuffing the porous glass body with a solvent or solution having a suitable composition at a suitable temperature to leach the compound out of the porous glass body so as to give a predetermined concentration distribution of the compound in the micropores, precipitating the compound in the micropores, drying the glass body in a predetermined atmosphere to decompose the compound, further heating the glass body at a higher temperature, and firing the glass body at a temperature sufficiently high to completely decompose the compound and to completely burn any organic materials in the glass body, but lower than the melting point of silica.
Claim 2
Dependent Claim
338 words
A process for producing an optical glass article, which comprises preparing at least two solutions having a pH of 10 to 15 and an SiO 2 content of about 1 to 12 mols/l and containing at least one silicate selected from the group consisting of lithium polysilicate, sodium silicate, potassium silicate, rubidium silicate, cesium silicate, thallium silicate, quaternary ammonium silicate and colloidal silica, combining these solutions to form a mixed solution, reacting the mixed solution with at least one organic compound selected from the group consisting of formaldehyde, paraformaldehyde, formamide, glyoxal, methyl formate, ethyl formate, methyl acetate and ethyl acetate at a temperature from the freezing point to the boiling point of the reaction solution in a time sufficient to polymerize silica and form a porous gelled body, leaching the porous gelled body with a leaching solution selected from the group consisting of water, an aqueous solution of an inorganic acid and an aqueous solution of an organic material, capable of dissolving residues in the porous gelled body, until the leaching reaches the central part of the porous gelled body, to form a porous glass body having micropores therein, stuffing the porous glass body with a solution containing at least one compound capable of being converted into an oxide dopant for changing the refractive index of the porous glass body, selected from the group consisting of CsNO 3 , RbNO 3 and TlNO 3 , unstuffing the porous glass body with a solvent or solution having a suitable composition at a suitable temperature to leach the compound out of the porous glass body so as to give a predetermined concentration distribution of the compound in the micropores, precipitating the compound in the micropores, drying the glass body in a predetermined atmosphere to decompose the compound, further heating the glass body at a higher temperature, and firing the glass body at a temperature sufficiently high to completely decompose the compound and to completely burn any organic materials in the glass body, but lower than the melting point of silica.
Claim 3
Dependent Claim
276 words
A process for producing an optical glass article, which comprises preparing an aqueous solution containing at least one silicate selected from the group consisting of lithium polysilicate, sodium silicate, potassium silicate, rubidium silicate, cesium silicate, thallium silicate, quaternary ammonium silicate and colloidal silica, preparing a dilute acid, mixing and stirring the aqueous solution of the silicate and the dilute acid to form a porous gelled body, leaching the porous gelled body with a leaching solution selected from the group consisting of water, an aqueous solution of an inorganic acid and an aqueous solution of an organic material, capable of dissolving residues in the porous gelled body, until the leaching reaches the central part of the porous gelled body, to form a porous glass body having micropores therein, stuffing the porous glass body with a solution containing at least one compound capable of being converted into an oxide dopant for changing the refractive index of the porous glass body, selected from the group consisting of CsNO 3 , RbNO 3 and TlNO 3 , unstuffing the porous glass body with a solvent or solution having a suitable composition at a suitable temperature to leach the compound out of the porous glass body so as to give a predetermined concentration distribution of the compound in the micropores, precipitating the compound in the micropores, drying the glass body in a predetermined atmosphere to decompose the compound, further heating the glass body at a higher temperature, and firing the glass body at a temperature sufficiently high to completely decompose the compound and to completely burn any organic materials in the glass body, but lower than the melting point of silica.
Claim 4
Dependent Claim
276 words
A process for producing an optical glass article, which comprises preparing an aqueous solution containing at least one silicate selected from the group consisting of lithium polysilicate, sodium silicate, potassium silicate, rubidium silicate, cesium silicate, thallium silicate, quaternary ammonium silicate and colloidal silica, preparing a dilute acid, mixing and stirring the aqueous solution of the silicate and the dilute acid to form a porous gelled body, leaching the porous gelled body with a leaching solution selected from the group consisting of water, an aqueous solution of an inorganic acid and an aqueous solution of an organic material, capable of dissolving residues in the porous gelled body, until the leaching reaches the central part of the porous gelled body, to form a porous glass body having micropores therein, stuffing the porous glass body with a solution containing at least one compound capable of being converted into an oxide dopant for changing the refractive index of the porous glass body, selected from the group consisting of CsNO 3 , RbNO 3 and TlNO 3 , unstuffing the porous glass body with a solvent or solution having a suitable composition at a suitable temperature to leach the compound out of the porous glass body so as to give a predetermined concentration distribution of the compound in the micropores, precipitating the compound in the micropores, drying the glass body in a predetermined atmosphere to decompose the compound, further heating the glass body at a higher temperature, and firing the glass body at a temperature sufficiently high to completely decompose the compound and to completely burn any organic materials in the glass body, but lower than the melting point of silica.
Claim 5
Dependent Claim
265 words
A process for producing an optical glass article, which comprises preparing an aqueous solution containing silicic acid, neutralizing and reacting the aqueous solution containing silicic acid at a temperature from the freezing point to the boiling point of the solution in a period of time sufficient to polymerize silica and form a porous gelled body, leaching the porous gelled body with a leaching solution selected from the group consisting of water, an aqueous solution of an inorganic acid and an aqueous solution of an organic material, capable of dissolving residues in the porous gelled body, until the leaching reaches the central part of the porous gelled body, to form a porous glass body having micropores therein, stuffing the porous glass body with a solution containing at least one compound capable of being converted into an oxide dopant for changing the refractive index of the porous glass body, selected from the group consisting of CsNO 3 , RbNO 3 and TlNO 3 , unstuffing the porous glass body with a solvent or solution having a suitable composition at a suitable temperature to leach the compound out of the porous glass body so as to give a predetermined concentration distribution of the compound in the micropores, precipitating the compound in the micropores, drying the glass body in a predetermined atmosphere to decompose the compound, further heating the glass body at a higher temperature, and firing the glass body at a temperature sufficiently high to completely decompose the compound and to completely burn any organic materials in the glass body, but lower than the melting point of silica.
Claim 6
Dependent Claim
265 words
A process for producing an optical glass article, which comprises preparing an aqueous solution containing silicic acid, neutralizing and reacting the aqueous solution containing silicic acid at a temperature from the freezing point to the boiling point of the solution in a period of time sufficient to polymerize silica and form a porous gelled body, leaching the porous gelled body with a leaching solution selected from the group consisting of water, an aqueous solution of an inorganic acid and an aqueous solution of an organic material, capable of dissolving residues in the porous gelled body, until the leaching reaches the central part of the porous gelled body, to form a porous glass body having micropores therein, stuffing the porous glass body with a solution containing at least one compound capable of being converted into an oxide dopant for changing the refractive index of the porous glass body, selected from the group consisting of CsNO 3 , RbNO 3 and TlNO 3 , unstuffing the porous glass body with a solvent or solution having a suitable composition at a suitable temperature to leach the compound out of the porous glass body so as to give a predetermined concentration distribution of the compound in the micropores, precipitating the compound in the micropores, drying the glass body in a predetermined atmosphere to decompose the compound, further heating the glass body at a higher temperature, and firing the glass body at a temperature sufficiently high to completely decompose the compound and to completely burn any organic materials in the glass body, but lower than the melting point of silica.
Claim 7
Dependent Claim
29 words
The process of claim 1, wherein the molar ratio of the organic compound, except formamide, to alkali metal oxide (R 2 O) in the silicate is 2 to 13.
Claim 8
Dependent Claim
22 words
The process of claim 1, wherein the molar ratio of formamide to alkali metal oxide in the silicate is 0.67 to 13.
Claim 9
Dependent Claim
22 words
The process of claim 1, wherein the reaction to form the porous gelled body is carried out at 40° to 100° C.
Claim 10
Dependent Claim
22 words
The process of claim 1, wherein the leaching solution is a solution of 1-5% HNO 3 +95-99% C 2 H 5 OH.
Claim 11
Dependent Claim
20 words
The process of claim 1, wherein the leaching solution is a solution of 1 M NH 4 NO 3 .
Claim 12
Dependent Claim
13 words
The process of claim 2, wherein the dilute acid contains a metal salt.
Claim 13
Dependent Claim
51 words
The process of claim 2, wherein the dilute acid is selected from the group consisting of dilute HNO 3 , dilute H 2 SO 4 , dilute HCl, aqueous H 2 CO 3 , aqueous H 3 BO 3 , aqueous H 3 PO 4 , acetic acid and formic acid.
Claim 14
Dependent Claim
20 words
The process of claim 2, wherein the leaching solution is an aqueous solution of an organic acid or inorganic acid.
Claim 15
Dependent Claim
23 words
The process of claim 11, wherein the organic acid is selected from the group consisting of acetic acid, formic acid and uric acid.
Claim 16
Dependent Claim
64 words
The process of claim 11, wherein the inorganic acid is selected from the group consisting of dilute HNO 3 , dilute H 2 SO 4 , dilute HCl, aqueous H 2 CO 3 , aqueous NH 4 NO 3 , aqueous (NH 4 ) 2 SO 4 , aqueous NH 4 Cl, aqueous H 3 BO 3 and aqueous H 3 PO 4 .
Claim 17
Dependent Claim
27 words
The process of claim 9, wherein the metal salt is selected from the group consisting of sulfates and nitrates of Al, Zn, Sn, Pb, As and Sb.
Claim 18
Dependent Claim
23 words
The process of claim 1, which further comprises immersing the unstuffed body in an organic solvent before precipitating the compound in the micropores.
Claim 19
Dependent Claim
28 words
The process of claim 3, wherein the aqueous solution containing silicic acid is an acidic aqueous solution of silicic acid or an acidic aqueous solution of ammonium silicate.
Claim 20
Dependent Claim
28 words
The process of claim 16, wherein the acidic aqueous solution of silicic acid is prepared by passing an aqueous solution of sodium silicate through a cation exchange resin.
Claim 21
Dependent Claim
46 words
The process of claim 16, wherein the acidic aqueous solution of ammonium silicate is prepared by passing an aqueous solution of sodium silicate through a cation exchange resin of the NH 4 + type and acidifying the resultant solution with hydrochloric acid or carbon dioxide gas.
Claim 22
Dependent Claim
18 words
The process of claim 3, wherein the neutralizing is carried out to a pH of 4 to 6.
Claim 23
Dependent Claim
26 words
The process of claim 3, wherein the leaching is carried out at a temperature of from room temperature to the boiling point of the leaching solution.
Claim 24
Dependent Claim
19 words
The process of claim 3, wherein the leaching solution is 1-5% HNO 3 +95-99% C 2 H 5 OH.
Claim 25
Dependent Claim
17 words
The process of claim 3, wherein the leaching solution is 1 M NH 4 NO 3 .
Claim 26
Dependent Claim
33 words
The process of claim 1, wherein between the stuffing and unstuffing steps, precipitating is carried out by lowering the temperature of the stuffing solution or by changing the composition of the stuffing solution.
Claim 27
Dependent Claim
29 words
The process of claim 1, wherein the precipitating after the unstuffing step is carried out by changing the composition of the solvent or solution or by raising the temperature.
Claim 28
Dependent Claim
14 words
The process of claim 1, wherein the solvent for the unstuffing step is water.
Claim 29
Dependent Claim
46 words
The process of claim 1, wherein the solution for the unstuffing step is an aqueous solution containing at least one compound selected from the group consisting of NH 4 NO 3 , (NH 4 ) 2 CO 3 and (NH 4 ) 2 SO 4 .
Claim 30
Dependent Claim
56 words
The process of claim 1, wherein the solution for the unstuffing step is an aqueous solution containing at least one compound selected from the group consisting of K 2 B 4 O 7 , K 3 PO 4 , H 3 PO 4 , H 3 BO 3 and NH 4 HB 4 O 7 .
Claim 31
Dependent Claim
38 words
The process of claim 1, wherein the predetermined atmosphere in the drying step is selected from the group consisting of a vacuum, dry O 2 under sub-atmospheric pressure, He gas and mixture of He and O 2 gases.
Claim 32
Dependent Claim
21 words
The process of claim 1, wherein the drying is carried out at a temperature of from room temperature to 500° C.
Claim 33
Dependent Claim
21 words
The process of claim 1, wherein the heating after drying is carried out at a temperature of 500° to 800° C.
Claim 34
Dependent Claim
38 words
The process of claim 1, wherein the heating after drying is carried out in an atmosphere selected from the group consisting of a vacuum, O 2 gas, He gas, and a mixture of He and O 2 .
Claim 35
Dependent Claim
19 words
The process of claim 1, wherein the firing is carried out at a temperature of 900° to 1450° C.
Claim 36
Dependent Claim
36 words
The process of claim 1, wherein the firing is carried out in an atmosphere selected from the group consisting of a vacuum, O 2 gas, He gas and a mixture of He and O 2 .
Claim 37
Dependent Claim
23 words
The process of claim 2, which further comprises immersing the unstuffed body in an organic solvent before precipitating the compound in the micropores.
Claim 38
Dependent Claim
23 words
The process of claim 3, which further comprises immersing the unstuffed body in an organic solvent before precipitating the compound in the micropores.
Claim 39
Dependent Claim
22 words
The process of claim 3, wherein the aqueous solution containing silicic acid further contains, dissolved therein, another water-soluble inorganic or organic compound.
Claim 40
Dependent Claim
19 words
The process of claim 30, wherein the heating is carried out at a temperature of 550° to 650° C.
References Cited (Backward Citations)
US3640093A
Cited
US4110093A
Cited
DE2447353A1
Cited
US4059658A
Cited
US4112032A
Cited
US4317668A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-06-20 | 1986-12-20 | 1987-06-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-06-20 | 1990-12-20 | 1991-06-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-06-20 | 1994-12-20 | 1995-06-21 | $7700.00 | Window Closed / Lapsed |