Copper base metal termination for multilayer ceramic capacitors
Assignee: Kemet Electronics Corp
•
Filing: 1984-05-03
•
Granted: 1985-05-14
•
Expires: 2004-05-03
Abstract
Abstract Copper end terminations of excellent electrical and mechanical properties are provided on multielectrode ceramic capacitors by applying copper, glass frit metallizations to the ends of a ceramic capacitor and firing the applied metallization in an atmosphere of nitrogen which contains a controlled partial pressure of oxygen.
Inventors
- 👤 Sri Prakash
- 👤 William B. Snyder, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 12:31
CPC Classifications
H; H01; H01G; H01G4/00; H01G4/002; H01G4/228; H01G4/232; H01G4/2325; C; C04; C04B; C04B41/00; C04B41/45; C04B41/50; C04B41/51; C04B41/5127; C04B41/80; C04B41/81; C04B41/85; C04B41/88
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
236 words
A method for providing a copper metallization end termination on a fired ceramic capacitor having a dielectric formed of barium or neodymium titanates which comprises (i) providing a termination paste consisting essentially of about (a) 75% to 97% by weight of solids in the paste being finely divided copper particles (b) 3 to 25% by weight of solids the paste being cadmium-free and bismuth-free glass frit (c) a volatile and decomposable organic liquid vehicle suspending the solids (ii) applying the copper containing paste to an electrode exposed end portion of a matured ceramic multielectrode capacitor body having a dielectric formed of barium or neodymium titanates (iii) heating the copper containing paste-covered end portion of the ceramic capacitor body to a temperature in the range of about 300° to 800° C. in a gaseous environment containing a small amount of oxygen which is in excess of 20 ppm and sufficient to prevent chemical reduction of ceramic during said heating but insufficient to oxidize said copper, the heating initially being at a lower temperature in said range for a period of time sufficient to remove substantially all organic binder and solvent constituents from the applied paste and thereafter being at a higher temperature in said range for a period of time sufficient to sinter the copper constituent of said applied paste and melt the glass constituent of said applied paste and bond the same said ceramic capacitor body.
Claim 2
Independent Claim
236 words
A method for providing a copper metallization end termination on a fired ceramic capacitor having a dielectric formed of barium or neodymium titanates which comprises (i) providing a termination paste consisting essentially of about (a) 75% to 97% by weight of solids in the paste being finely divided copper particles (b) 3 to 25% by weight of solids the paste being cadmium-free and bismuth-free glass frit (c) a volatile and decomposable organic liquid vehicle suspending the solids (ii) applying the copper containing paste to an electrode exposed end portion of a matured ceramic multielectrode capacitor body having a dielectric formed of barium or neodymium titanates (iii) heating the copper containing paste-covered end portion of the ceramic capacitor body to a temperature in the range of about 300° to 800° C. in a gaseous environment containing a small amount of oxygen which is in excess of 20 ppm and sufficient to prevent chemical reduction of ceramic during said heating but insufficient to oxidize said copper, the heating initially being at a lower temperature in said range for a period of time sufficient to remove substantially all organic binder and solvent constituents from the applied paste and thereafter being at a higher temperature in said range for a period of time sufficient to sinter the copper constituent of said applied paste and melt the glass constituent of said applied paste and bond the same said ceramic capacitor body.
Claim 3
Dependent Claim
57 words
A method in accordance with claim 1 wherein said lower temperature of step (iii) is maintained in the range of about 300° to 600° C. and the oxygen content in the gaseous environment is in the range of about 50 to 150 ppm while said lower temperature is maintained in the range of 300° to 600° C.
Claim 4
Dependent Claim
57 words
A method in accordance with claim 1 wherein said higher temperature of step (iii) is maintained in the range of about 600° to 900° C. and the oxygen content in the gaseous environment is in the range of about 40 to 80 ppm while said higher temperature is maintained in the range of 600° to 900° C.
Claim 5
Dependent Claim
59 words
A method in accordance with claim 1 wherein said lower temperature of step (iii) is maintained in the range of about 300° to 600° C. and oxygen is added to the gaseous environment to provide an oxygen content therein of about 50 to 150 ppm while said lower temperature is maintained in the range of 300° to 600° C.
Claim 6
Dependent Claim
13 words
A method in accordance with claim 1 wherein said gaseous environment is nitrogen.
References Cited (Backward Citations)
US2389420A
Cited
US3350341A
Cited
US3647532A
Cited
US4072771A
Cited
US4070518A
Cited
US4064310A
Cited
US4234367A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-05-13 | 1988-11-12 | 1989-05-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-05-13 | 1992-11-12 | 1993-05-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-05-13 | 1996-11-12 | 1997-05-14 | $7700.00 | Window Closed / Lapsed |