Abstract The disclosure relates to a method for removing the unwanted impurities from an HgCdTe alloy which consists of the steps of depositing a thin film on the order of from about 1 to about 100 microns in thickness of tellurium onto the backside of a mercury cadmium telluride bar to insure the presence of a substantial amount of excess tellurium on the backside of the alloy bar and allow the gettering mechanism to work. A protective film to shield the tellurium film from mercury ambient atmosphere is then optionally placed over the tellurium film. The protective film can be formed of a silicon oxide such as SiO and is preferably in the range of about 1000 angstroms to 10 microns or more in thickness. The bar with the tellurium and protective film thereon is then annealed at a temperature of less than 450° C., preferably about 280° C., for a period of from about one day to about four weeks in a saturated mercury atmosphere to allow the impurities in the alloy to diffuse to the backside thereof and into the tellurium layer. The bulk of the impurities will travel into the tellurium layer within a matter of several days at the preferred temperature noted hereinabove. The tellurium layer and protective film are then removed such as by grinding, etching or other appropriate method to remove the impurities from the alloy bar.
Inventors
👤 Herbert F. Schaake
👤 John H. Tregilgas
👤 Jeffrey D. Beck
Bibliographic Details
Application Number—
JurisdictionUS
Data Sourcegoogle_patents
Last Synchronized2026-11-09 20:12
CPC Classifications
H; H10; H10P; H10P95/00; H10P95/90
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
86 words
A method of removing impurities from a HgCdTe member comprising the steps of: (a) providing a HgCdTe member having impurities substantially uniformly dispersed therethrough; (b) forming a tellurium layer on a portion of the exposed surface of said member; (c) annealing the member resulting from step (b) at a temperature less than about 450 degrees C. in a saturated mercury atmosphere for a period of from about one day to about four weeks; and (d) removing said tellurium layer and impurities in an adjacent layer thereto.
Claim 2
Independent Claim
86 words
A method of removing impurities from a HgCdTe member comprising the steps of: (a) providing a HgCdTe member having impurities substantially uniformly dispersed therethrough; (b) forming a tellurium layer on a portion of the exposed surface of said member; (c) annealing the member resulting from step (b) at a temperature less than about 450 degrees C. in a saturated mercury atmosphere for a period of from about one day to about four weeks; and (d) removing said tellurium layer and impurities in an adjacent layer thereto.
Claim 3
Dependent Claim
36 words
A method as set forth in claim 1 further including the step of placing a protective film stable at said annealing temperature and not a contaminant to said member over said tellurium layer after step (b).
Claim 4
Dependent Claim
15 words
A method as set forth in claim 2 wherein said film is a silicon oxide.
Claim 5
Dependent Claim
28 words
A method as set forth in claim 3 wherein the thickness of said tellurium layer is in the range of from about 1 micrometer to about 100 micrometers.
Claim 6
Dependent Claim
28 words
A method as set forth in claim 2 wherein the thickness of said tellurium layer is in the range of from about 1 micrometer to about 100 micrometers.
Claim 7
Dependent Claim
28 words
A method as set forth in claim 1 wherein the thickness of said tellurium layer is in the range of from about 1 micrometer to about 100 micrometers.