US4503174A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Low temperature curing coating composition
Assignee: EIDP Inc
•
Filing: 1983-09-06
•
Granted: 1985-03-05
•
Expires: 2003-09-06
Abstract
Abstract A low temperature curing coating composition containing 10-80% by weight of binder and 20-90% by weight of an organic solvent in which the binder is (1) an acrylic polymer containing monomers having reactive groups such as acrylamide, methacrylamide, methacrylic acid, acrylic acid and glycidyl methacrylate, (2) an epoxy resin, (3) a polyamine curing agent, (4) phenol and (5) a bicyclic amindine; The composition is used as a primer or topcoating for metal substrates and curings at temperatures of 0 DEG C. to ambient temperatures and provides a primer that has excellent adhesion to the substrate and provides a durable, corrosion resistant finish.
Inventors
- 👤 Joseph A. Vasta
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 19:54
CPC Classifications
C; C09; C09D; C09D163/00; C08; C08G; C08G59/00; C08G59/18; C08G59/40; C08G59/50; C08G59/54; C09D133/00; C09D133/04; C09D133/06; C09D133/10; C08L; C08L63/00; Y; Y10; Y10S; Y10S525/00; Y10S525/939
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
89 words
A coating composition comprising 10-80% by weight of binder and 20-90% by weight of an organic solvent; wherein the binder consists essentially of (1) an acrylic polymer containing 0.1-10% by weight of polymerized monomers having reactive groups selected from the group consisting of acrylamide, methacrylamide, methacrylic acid, acrylic acid and glycidyl methacrylate, (2) an epoxy resin, (3) a polyamine curing agent of the formula ##STR6## where R 1 is R 2 NH 2 and R 2 is an aliphatic or cycloaliphatic radical (4) phenol and (5) a bicyclic amidine.
Claim 2
Dependent Claim
89 words
A coating composition comprising 10-80% by weight of binder and 20-90% by weight of an organic solvent; wherein the binder consists essentially of (1) an acrylic polymer containing 0.1-10% by weight of polymerized monomers having reactive groups selected from the group consisting of acrylamide, methacrylamide, methacrylic acid, acrylic acid and glycidyl methacrylate, (2) an epoxy resin, (3) a polyamine curing agent of the formula ##STR6## where R 1 is R 2 NH 2 and R 2 is an aliphatic or cycloaliphatic radical (4) phenol and (5) a bicyclic amidine.
Claim 3
Dependent Claim
20 words
The coating composition of claim 1 containing pigment in a pigment to binder weight ratio of about 20:100 to 200:100.
Claim 4
Dependent Claim
42 words
The coating composition of claim 2 in which the acrylic polymer comprises methyl methacrylate, alkyl methacrylate or an alkyl acrylate each having 2-8 carbon atoms in the alkyl group and methacrylic acid and having a weight average molecular weight of about 5,000-75,000.
Claim 5
Dependent Claim
28 words
The coating composition of claim 3 in which the acrylic polymer consists essentially of methyl methacrylate, butyl methacrylate, methacrylic acid and has a molecular weight of about 40,000-60,000.
Claim 6
Dependent Claim
32 words
The coating composition of claim 3 in which the epoxy resin has the formula ##STR7## where R is an aromatic radical and n is a positive integer of about 0.5 to 4.
Claim 7
Dependent Claim
11 words
The coating composition of claim 5 in which R is ##STR8##
Claim 8
Dependent Claim
29 words
The coating composition of claim 3 in which the epoxy resin is an epoxy novolac resin of the formula ##STR9## where n is a positive integer of about 0.2-2.
Claim 9
Dependent Claim
12 words
The coating composition of claim 2 in which R 1 is ##STR10##
Claim 10
Dependent Claim
13 words
The coating composition of claim 2 in which the bicyclic amidine is 1,8-diaza-bicyclo[5,4,0]-undecene-7.
Claim 11
Dependent Claim
22 words
The coating composition of claim 2 containing about 0.5-5% by weight, based on the weight of the binder, of a chloride scavanger.
Claim 12
Dependent Claim
14 words
The coating composition of claim 10 in which the chloride scavanger is lead naphthenate.
Claim 13
Dependent Claim
23 words
The coating composition of claim 2 containing about 0.1-3% by weight, based on the weight of the binder, of a silicone wetting agent.
Claim 14
Dependent Claim
16 words
The coating composition of claim 12 in which the silicone wetting agent is oxyethylene methyl siloxane.
Claim 15
Dependent Claim
51 words
The coating composition of claim 2 in which the binder consists essentially of about the binder consists essentially of about 20-60% by weight of acrylic polymer, 15-45% by weight of epoxy resin 10-25% by weight of polyamine curing agent, 1-7% by weight of phenol and 0.01-3% by weight of bicyclic amidine.
Claim 16
Dependent Claim
177 words
The coating composition of claim 1 in which the binder consists essentially of about (1) 20-60% by weight, based on the weight of the binder, of an acrylic polymer consisting essentially of 50-69.9% by weight, based on the weight of the acrylic polymer, of methyl methacrylate, 30-47% by weight, based on the weight of the acrylic polymer, of butyl methacrylate, 0.1-3% by weight, based on the weight of the acrylic polymer, of methacrylic acid, wherein the acrylic polymer has a weight average molecular weight of about 40,000-60,000; (2) 15-45% by weight, based on the weight of the binder, of an epoxy resin of the formula ##STR11## where n is a positive integer of about 0.5 to 4; (3) 10-25% by weight, based on the weight of the binder, of a polyamine curing agent of the formula ##STR12## where R1 is ##STR13## (4) 1-7% by weight, based on the weight of the binder, of phenol, and (5) 0.01-3% by weight of 1,8-diaza-bicyclo(5,4,0)-undecene 7 and containing pigment in a pigment to binder weight ratio of about 20:100 to 200:100.
Claim 17
Dependent Claim
41 words
The coating composition of claim 15 containing about 0.5-5% by weight, based on the weight of the binder, of lead naphthenate and 0.1-3% by weight, based on the weight of the binder, of a silicone wetting agent of oxyethylene methyl siloxane.
Claim 18
Dependent Claim
79 words
A two-component composition, wherein the two components are mixed together to form a composition comprising about 10-80% by weight binder and 20-90% by weight organic solvent and wherein the components comprise component (1) a solution of an acrylic polymer containing 0.1-10% by weight of polymerized monomers having reactive groups selected from the group consisting of acrylamide, methacrylamide, methacrylic acid, acrylic acid and glycidyl methacrylate, and an epoxy resin, component (2) a polyamine curing agent, phenol and a bicyclic amidine.
Claim 19
Dependent Claim
79 words
A two-component composition, wherein the two components are mixed together to form a composition comprising about 10-80% by weight binder and 20-90% by weight organic solvent and wherein the components comprise component (1) a solution of an acrylic polymer containing 0.1-10% by weight of polymerized monomers having reactive groups selected from the group consisting of acrylamide, methacrylamide, methacrylic acid, acrylic acid and glycidyl methacrylate, and an epoxy resin, component (2) a polyamine curing agent, phenol and a bicyclic amidine.
References Cited (Backward Citations)
US2795564A
Cited
US2798861A
Cited
US2842459A
Cited
US3011909A
Cited
US2954358A
Cited
US3070564A
Cited
US3305601A
Cited
US3107226A
Cited
US3301801A
Cited
US3154598A
Cited
US3215757A
Cited
US3196120A
Cited
US3245925A
Cited
US3248356A
Cited
US3492252A
Cited
US3375227A
Cited
US3544495A
Cited
US3509086A
Cited
US3647765A
Cited
US3532653A
Cited
US3558564A
Cited
US3954898A
Cited
DE2064916A1
Cited
US3679642A
Cited
US3758633A
Cited
US3776865A
Cited
US3846368A
Cited
US3945963A
Cited
US4069174A
Cited
US4018848A
Cited
US3960979A
Cited
US3979540A
Cited
US4032479A
Cited
US4122128A
Cited
US4181645A
Cited
US4177178A
Cited
US4192929A
Cited
US4383059A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-03-04 | 1988-09-03 | 1989-03-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-03-04 | 1992-09-03 | 1993-03-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-03-04 | 1996-09-03 | 1997-03-05 | $7700.00 | Window Closed / Lapsed |