US4502983A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Composite silicon carbide sintered shapes and its manufacture
Assignee: MAMORU OMORI
•
Filing: 1983-06-28
•
Granted: 1985-03-05
•
Expires: 2003-06-28
Abstract
Abstract A composite silicon carbide sintered shape is provided in two forms in which the former form includes rare earth oxides as a sintering assist, and the latter form includes rare earth oxides and/or aluminum oxide or boron oxide as a sintering assist, characterized in that both forms have a surface layer abundant in rare earth oxides. Methods for manufacturing such sintered shapes are also provided.
Inventors
- 👤 Mamoru Omori
- 👤 Humihiko Takei
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 15:41
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/565; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/30
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
41 words
A composite silicon carbide sintered shape consisting of 11.300-65.000 atomic percent of one or more members selected from the group of rare earth oxides and balance substantially being of SiC, said shape having a surface layer abundant in rare earth oxide.
Claim 2
Dependent Claim
41 words
A composite silicon carbide sintered shape consisting of 11.300-65.000 atomic percent of one or more members selected from the group of rare earth oxides and balance substantially being of SiC, said shape having a surface layer abundant in rare earth oxide.
Claim 3
Dependent Claim
72 words
A composite silicon carbide sintered shape consisting of 0.021-65.000 atomic percent of one or more members selected from the group of rare earth oxides, 0.006-79.984 atomic percent of at least either member of aluminum oxide or boron oxide, total sum of said rare earth oxide plus aluminum oxide or boron oxide being 11.306-80.000 atomic percent, the balance substantially being of SiC, said shape having a surface layer abundant in rare earth oxide.
Claim 4
Dependent Claim
72 words
A composite silicon carbide sintered shape consisting of 0.021-65.000 atomic percent of one or more members selected from the group of rare earth oxides, 0.006-79.984 atomic percent of at least either member of aluminum oxide or boron oxide, total sum of said rare earth oxide plus aluminum oxide or boron oxide being 11.306-80.000 atomic percent, the balance substantially being of SiC, said shape having a surface layer abundant in rare earth oxide.
Claim 5
Independent Claim
195 words
A method of manufacturing a silicon carbide sintered shape comprising the steps of (a) mixing silicon carbide powder with a sintering assist consisting essentially of at least one member selected from the group consisting of rare earth elements and rare earth compounds to form a mixture, the amount of said assist being in a range of 11.300-65.000 atomic percent on a rare earth oxide basis, 100 atomic percent being the sum of said assist and silicon carbide; (b) compacting said mixture at a pressure in a range from 100 MPa to 200 l MPa; (c) burning said mixture in a primary firing at a temperature of from 500° to 1,400° C. for a period from 5 to 14 hours; and (d) sintering said burnt mixture at a temperature of from 1800° to 2,000° C. for a period from 6 to 14 hours in an atmosphere consisting essentially of a gas selected from the group consisting of argon and nitrogen; thereby forming in said shape a central portion and a surface layer, said surface layer being abundant in rare earth oxide, whereby said surface layer exhibits electrical insulating properties and said central portion exhibits semi-conductive properties.
Claim 6
Independent Claim
195 words
A method of manufacturing a silicon carbide sintered shape comprising the steps of (a) mixing silicon carbide powder with a sintering assist consisting essentially of at least one member selected from the group consisting of rare earth elements and rare earth compounds to form a mixture, the amount of said assist being in a range of 11.300-65.000 atomic percent on a rare earth oxide basis, 100 atomic percent being the sum of said assist and silicon carbide; (b) compacting said mixture at a pressure in a range from 100 MPa to 200 l MPa; (c) burning said mixture in a primary firing at a temperature of from 500° to 1,400° C. for a period from 5 to 14 hours; and (d) sintering said burnt mixture at a temperature of from 1800° to 2,000° C. for a period from 6 to 14 hours in an atmosphere consisting essentially of a gas selected from the group consisting of argon and nitrogen; thereby forming in said shape a central portion and a surface layer, said surface layer being abundant in rare earth oxide, whereby said surface layer exhibits electrical insulating properties and said central portion exhibits semi-conductive properties.
Claim 7
Independent Claim
219 words
A method of manufacturing a silicon carbide sintered shape comprising the steps of (a) mixing silicon carbide powder with a sintering assist consisting of less than 99 percent by weight of at least one member selected from the group consisting of aluminum, carbon, boron and their compounds, and the balance being of at least one member selected from the group consisting of rare earth elements and rare earth compounds, to form a mixture, the amount of said rare earth elements or their compounds being 0.021-65.000 atomic percent on their oxide basis, 100 atomic percent being the sum of said assist and silicon carbide; (b) compacting said mixture at a pressure in a range from 100 MPa to 200 MPa; (c) burning said mixture in a primary firing at a temperature of from 500° to 1,400° C. for a period from 5 to 14 hours; and sintering said burnt mixture at a temperature of from 1800° to 2,000° C. for a period from 6 to 14 hours in an atmosphere consisting essentially of a gas selected from the group consisting of argon and nitrogen; thereby forming in said shape a central portion and a surface layer, said surface layer being abundant in rare earth oxide whereby said surface layer exhibits electrical insulating properties and said central portion exhibits semi-conducting properties.
Claim 8
Independent Claim
219 words
A method of manufacturing a silicon carbide sintered shape comprising the steps of (a) mixing silicon carbide powder with a sintering assist consisting of less than 99 percent by weight of at least one member selected from the group consisting of aluminum, carbon, boron and their compounds, and the balance being of at least one member selected from the group consisting of rare earth elements and rare earth compounds, to form a mixture, the amount of said rare earth elements or their compounds being 0.021-65.000 atomic percent on their oxide basis, 100 atomic percent being the sum of said assist and silicon carbide; (b) compacting said mixture at a pressure in a range from 100 MPa to 200 MPa; (c) burning said mixture in a primary firing at a temperature of from 500° to 1,400° C. for a period from 5 to 14 hours; and sintering said burnt mixture at a temperature of from 1800° to 2,000° C. for a period from 6 to 14 hours in an atmosphere consisting essentially of a gas selected from the group consisting of argon and nitrogen; thereby forming in said shape a central portion and a surface layer, said surface layer being abundant in rare earth oxide whereby said surface layer exhibits electrical insulating properties and said central portion exhibits semi-conducting properties.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-03-04 | 1988-09-03 | 1989-03-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-03-04 | 1992-09-03 | 1993-03-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-03-04 | 1996-09-03 | 1997-03-05 | $7700.00 | Window Closed / Lapsed |