US4497692A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Laser-enhanced jet-plating and jet-etching: high-speed maskless patterning method
Assignee: International Business Machines Corp
•
Filing: 1983-06-13
•
Granted: 1985-02-05
•
Expires: 2003-06-13
Abstract
Abstract This metal deposition/material removal technique modifies free-standing or submerged jet plating with an electromagnetic energy beam such as an intense laser beam, directed collinearly along the jet. Experiments were made to deposit gold contact areas on nickel plated beryllium-copper substrates used for microelectronic connectors. The deposits are found to be crack-free and dense, possessing excellent adhesion to the substrate. Deposition rates for 0.05 cm diameter gold spots are on the order of 10 micrometers per second.
Inventors
- 👤 Mordechai H. Gelchinski
- 👤 Lubomyr T. Romankiw
- 👤 Donald R. Vigliotti
- 👤 Robert J. VON Gutfeld
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 22:34
CPC Classifications
C; C23; C23F; C23F1/00; C25; C25D; C25D5/00; C25D5/02; C25D5/024; C25D5/026; C25F; C25F3/00; C25F3/02; C25F3/14; H; H05; H05K; H05K3/00; H05K3/02; H05K3/06; H05K3/068; H05K3/22; H05K3/24; H05K3/241
Claims Analysis
Total Claims: 84
Claim 1
Independent Claim
92 words
In a process of chemically-enhanced additive or subtractive processing of a substrate in a chemically-active electrolyte fluid, the improvement comprising directing a high intensity energy beam to heat said substrate at the site to be treated concomitantly with simultaneously directing a jet of said fluid at the locus of desired enhanced-chemical action on said substrate, said energy beam being collinear with said jet, said site and said locus coinciding at the same spot, and said beam having a diameter comparable to or less than the diameter of said jet at said locus.
Claim 2
Dependent Claim
92 words
In a process of chemically-enhanced additive or subtractive processing of a substrate in a chemically-active electrolyte fluid, the improvement comprising directing a high intensity energy beam to heat said substrate at the site to be treated concomitantly with simultaneously directing a jet of said fluid at the locus of desired enhanced-chemical action on said substrate, said energy beam being collinear with said jet, said site and said locus coinciding at the same spot, and said beam having a diameter comparable to or less than the diameter of said jet at said locus.
Claim 3
Dependent Claim
30 words
The method in accordance with claim 1 wherein said fluid comprises an electrolyte with said beam cooperating with said fluid to enhance the rate of said process at said site.
Claim 4
Dependent Claim
14 words
The method of claim 2 wherein said additive or subtractive processing is performed electrochemically.
Claim 5
Dependent Claim
92 words
In a process of chemically-enhanced additive or subtractive processing of a substrate in a chemically-active fluid, directing a high intensity, laser energy beam to heat said substrate at the site to be treated concomitantly with directing a jet of said fluid at the locus of desired enhanced-chemical action on said substrate, said laser beam being collinear with said jet and said jet of fluid serving as an optical waveguide for said beam, whereby said processing is focussed on an area defined by the point of impact of said jet upon said substrate.
Claim 6
Dependent Claim
92 words
In a process of chemically-enhanced additive or subtractive processing of a substrate in a chemically-active fluid, directing a high intensity, laser energy beam to heat said substrate at the site to be treated concomitantly with directing a jet of said fluid at the locus of desired enhanced-chemical action on said substrate, said laser beam being collinear with said jet and said jet of fluid serving as an optical waveguide for said beam, whereby said processing is focussed on an area defined by the point of impact of said jet upon said substrate.
Claim 7
Dependent Claim
51 words
The process of claim 1 wherein said jet can be either a free-standing jet or a submerged jet, said jet is collinear with said energy beam, and said energy beam comprises a laser beam, with said beam cooperating with said fluid to enhance the rate of said process at said site.
Claim 8
Dependent Claim
51 words
A process in accordance with claim 1 wherein said jet is larger in diameter than said energy beam thereby permitting a large ionic resupply surrounding a finely focussed energy beam employed for patterning (etching/plating), with said beam cooperating with said fluid to enhance the rate of said process at said site.
Claim 9
Dependent Claim
14 words
A process in accordance with claim 6 wherein said beam is a laser beam.
Claim 10
Dependent Claim
147 words
A process of chemical treatment with a chemical fluid comprising an electrolyte and an energy beam in jet-chemical plating and jet-chemical etching of any variety to achieve improved product quality at high rates of plating or etching, providing a jet of said chemical fluid, said energy beam being collinear with said jet, wherein plating or etching is accomplished selectively by applying said energy beam to sites to be plated or etched concomitantly with use of a said jet to circulate the plating solution rapidly at the locus to be plated more rapidly on the surface of the object to be plated, said site and said locus coinciding at the same spot, with said beam cooperating with said fluid to enhance the rate of said process at said site, and said beam having a diameter comparable to or less than the diameter of said jet at said locus.
Claim 11
Dependent Claim
147 words
A process of chemical treatment with a chemical fluid comprising an electrolyte and an energy beam in jet-chemical plating and jet-chemical etching of any variety to achieve improved product quality at high rates of plating or etching, providing a jet of said chemical fluid, said energy beam being collinear with said jet, wherein plating or etching is accomplished selectively by applying said energy beam to sites to be plated or etched concomitantly with use of a said jet to circulate the plating solution rapidly at the locus to be plated more rapidly on the surface of the object to be plated, said site and said locus coinciding at the same spot, with said beam cooperating with said fluid to enhance the rate of said process at said site, and said beam having a diameter comparable to or less than the diameter of said jet at said locus.
Claim 12
Dependent Claim
38 words
The process of claim 8 wherein said energy beam is directed through said jet of fluid, so that it passes along the length of the jet of fluid which acts as an optical waveguide for said energy beam.
Claim 13
Dependent Claim
54 words
The process of claim 9 wherein said energy beam comprises a laser, with said beam cooperating with said fluid to apply energy to said substrate at said site, whereby said process performed by said chemical fluid is accelerated at said site as contrasted with the surrounding areas near said site and within said locus.
Claim 14
Dependent Claim
24 words
The process of claim 1 wherein said energy beam has an energy density of at least about 10 2 watts per cm 2 .
Claim 15
Dependent Claim
66 words
The process of claim 9 wherein said energy beam has an energy density of at least about 10 2 watts per cm 2 , with said beam cooperating with said fluid to apply energy to said substrate at said site, whereby said process performed by said chemical fluid is accelerated at said site as contrasted with the surrounding areas near said site and within said locus.
Claim 16
Dependent Claim
83 words
The process of claim 8 wherein a substrate is located in a chamber and said energy beam is directed through a free-standing jet stream of a solution of said electrolyte containing an active chemical species adapted to interact with said substrate, with said beam cooperating with said fluid to apply energy to said substrate at said site, whereby said process performed by said chemical fluid is accelerated at said site as contrasted with the surrounding areas near said site and within said locus.
Claim 17
Dependent Claim
54 words
The process of claim 12 wherein said energy beam is a laser beam and said jet acts as a light guide, said laser beam passing through said jet to said site within said locus, said jet of fluid having optical characteristics trapping the light of said laser within the fluid column of said jet.
Claim 18
Dependent Claim
31 words
The energy beam of claim 1 wherein said energy beam comprises a microwave beam, with said beam cooperating with said fluid to enhance the rate of said process at said site.
Claim 19
Dependent Claim
12 words
The energy beam of claim wherein said beam comprises a microwave beam.
Claim 20
Dependent Claim
66 words
A process in accordance with claim 1 wherein said energy beam comprises a laser beam having a diameter comparable to the diameter of the jet of electrolyte, whereby both the fluid of said jet and the light of said laser strike the substrate coincidentally, i.e. in the same spot, with said beam cooperating with said fluid to enhance the rate of said process at said site.
Claim 21
Dependent Claim
91 words
A process in accordance with claim 8 wherein said energy beam comprises a laser beam having a diameter comparable to the diameter of the jet of electrolyte, whereby both the fluid of said jet and the light of said laser strike the substrate coincidentally, i.e. in the same spot, with said beam cooperating with said fluid to apply energy to said substrate at said site, whereby said process performed by said chemical fluid is accelerated at said site as contrasted with the surrounding areas near said site and within said locus.
Claim 22
Dependent Claim
84 words
A process in accordance with claim 1 wherein said process is an electrochemical process with an anode and a cathode with a voltage between the anode and the cathode, said voltage being applied by a power supply connected between said substrate onto which the jet and the laser are impinging and an electrode suitably positioned inside the compartment containing the nozzle for producing said jet of fluid, with said beam cooperating with said fluid to enhance the rate of said process at said site.
Claim 23
Dependent Claim
109 words
A process in accordance with claim 8 wherein said process is an electrochemical process with an anode and a cathode with a voltage between the anode and the cathode, said voltage being applied by a power supply connected between said substrate onto which the jet and the laser are impinging and an electrode suitably positioned inside the compartment containing the nozzle for producing said jet of fluid, with said beam cooperating with said fluid to apply energy to said substrate at said site, whereby said process performed by said chemical fluid is accelerated at said site as contrasted with the surrounding areas near said site and within said locus.
Claim 24
Dependent Claim
171 words
The process of chemically-enhanced additive plating or subtractive etching of a substrate in a chemically-active fluid, while directing a high intensity energy beam to heat said substrate at the site to be treated concomitantly with directing a jet of said fluid at the locus of desired enhanced-chemical action on said substrate said energy beam being collinear with said jet, said site and said locus coinciding at the same spot, wherein said plating or etching is accomplished selectively by applying an energy beam such as an electromagnetic beam preferably in the form of laser to spots to be plated concomitantly with use of a jet to transport the plating solution rapidly to and at the surface of the object to be chemically treated by plating, etching, etc. whereby said laser beam is passed along the length of the jet of fluid which acts as a light guide or waveguide for the laser beam, and said beam having a diameter comparable to or less than the diameter of said jet at said locus.
Claim 25
Dependent Claim
171 words
The process of chemically-enhanced additive plating or subtractive etching of a substrate in a chemically-active fluid, while directing a high intensity energy beam to heat said substrate at the site to be treated concomitantly with directing a jet of said fluid at the locus of desired enhanced-chemical action on said substrate said energy beam being collinear with said jet, said site and said locus coinciding at the same spot, wherein said plating or etching is accomplished selectively by applying an energy beam such as an electromagnetic beam preferably in the form of laser to spots to be plated concomitantly with use of a jet to transport the plating solution rapidly to and at the surface of the object to be chemically treated by plating, etching, etc. whereby said laser beam is passed along the length of the jet of fluid which acts as a light guide or waveguide for the laser beam, and said beam having a diameter comparable to or less than the diameter of said jet at said locus.
Claim 26
Dependent Claim
229 words
A process of chemical treatment with a chemical fluid comprising an electrolyte and an energy beam in jet-chemical plating and jet-chemical etching of any variety to achieve improved product quality at high rates of plating or etching, providing a jet of said chemical fluid, said energy beam being collinear with said jet, said site and said locus coinciding at the same spot, wherein plating or etching is accomplished selectively by applying said energy beam to sites to be plated or etched concomitantly with use of a said jet to circulate the plating solution rapidly at the locus to be plated more rapidly on the surface of the object to be plated, with said beam cooperating with said fluid to enhance the rate of said process at said site, said plating or etching being accomplished selectively by applying an energy beam such as an electromagnetic beam preferably in the form of laser to spots to be plated concomitantly with use of a jet to transport the plating solution rapidly to and at the surface of the object to be chemically treated by plating, etching, etc. whereby said laser beam is passed along the length of the jet of fluid which acts as a light guide or waveguide for the laser beam, and said beam having a diameter comparable to or less than the diameter of said jet at said locus.
Claim 27
Dependent Claim
229 words
A process of chemical treatment with a chemical fluid comprising an electrolyte and an energy beam in jet-chemical plating and jet-chemical etching of any variety to achieve improved product quality at high rates of plating or etching, providing a jet of said chemical fluid, said energy beam being collinear with said jet, said site and said locus coinciding at the same spot, wherein plating or etching is accomplished selectively by applying said energy beam to sites to be plated or etched concomitantly with use of a said jet to circulate the plating solution rapidly at the locus to be plated more rapidly on the surface of the object to be plated, with said beam cooperating with said fluid to enhance the rate of said process at said site, said plating or etching being accomplished selectively by applying an energy beam such as an electromagnetic beam preferably in the form of laser to spots to be plated concomitantly with use of a jet to transport the plating solution rapidly to and at the surface of the object to be chemically treated by plating, etching, etc. whereby said laser beam is passed along the length of the jet of fluid which acts as a light guide or waveguide for the laser beam, and said beam having a diameter comparable to or less than the diameter of said jet at said locus.
Claim 28
Dependent Claim
118 words
In a process of chemically-enhanced additive or subtractive processing of a substrate in a photolytic chemically-active fluid, said fluid comprising an electrolyte, the improvement comprising directing a laser beam to illuminate said substrate at the site to be treated concomitantly with directing a jet of said fluid at the locus of desired enhanced-chemical action on said substrate, with said beam cooperating with said fluid to apply energy to said substrate at said site, whereby said process performed by said chemical fluid is accelerated at said site as contrasted with the surrounding areas near said site and within said locus, and said beam having a diameter comparable to or less than the diameter of said jet at said locus.
Claim 29
Dependent Claim
118 words
In a process of chemically-enhanced additive or subtractive processing of a substrate in a photolytic chemically-active fluid, said fluid comprising an electrolyte, the improvement comprising directing a laser beam to illuminate said substrate at the site to be treated concomitantly with directing a jet of said fluid at the locus of desired enhanced-chemical action on said substrate, with said beam cooperating with said fluid to apply energy to said substrate at said site, whereby said process performed by said chemical fluid is accelerated at said site as contrasted with the surrounding areas near said site and within said locus, and said beam having a diameter comparable to or less than the diameter of said jet at said locus.
Claim 30
Dependent Claim
146 words
A process of chemically-enhanced additive or subtractive processing of a substrate in an electroplating fluid bath comprising directing a high intensity energy beam to heat said substrate at the site on said substrate to be treated concomitantly with directing a jet of said fluid at the locus of desired enhanced-chemical action on said substrate at said site, said jet and said beam being collinear, said plating or etching being accomplished selectively by applying said beam to spots to be processed concomitantly with use of said jet to transport the plating solution rapidly to and at the surface of the object to be chemically processed, said beam being passed along the length of the jet of fluid which acts as a light guide or waveguide for said beam, and said beam having a diameter comparable to or less than the diameter of said jet at said locus.
Claim 31
Dependent Claim
146 words
A process of chemically-enhanced additive or subtractive processing of a substrate in an electroplating fluid bath comprising directing a high intensity energy beam to heat said substrate at the site on said substrate to be treated concomitantly with directing a jet of said fluid at the locus of desired enhanced-chemical action on said substrate at said site, said jet and said beam being collinear, said plating or etching being accomplished selectively by applying said beam to spots to be processed concomitantly with use of said jet to transport the plating solution rapidly to and at the surface of the object to be chemically processed, said beam being passed along the length of the jet of fluid which acts as a light guide or waveguide for said beam, and said beam having a diameter comparable to or less than the diameter of said jet at said locus.
Claim 32
Dependent Claim
196 words
A process of chemically-enhanced additive or subtractive processing of a substrate in an electroless fluid bath, said bath comprising an electrolyte, comprising directing a high intensity energy beam to heat said substrate at the site on said substrate to be treated concomitantly with directing a jet of said fluid at the locus of desired enhanced-chemical action on said substrate at said site, said jet and said beam being collinear, said plating or etching being accomplished selectively by applying said beam to spots on said substrate to be processed concomitantly with use of said jet to transport the plating solution rapidly to and at the surface of said substrate to be chemically processed, said beam being passed along the length of said jet of fluid which acts as a light guide or waveguide for said beam, with said beam cooperating with said fluid to apply energy to said substrate at said site, whereby said process performed by said chemical fluid is accelerated at said site as contrasted with the surrounding areas near said site and within said locus, and said beam having a diameter comparable to or less than the diameter of said jet at said locus.
Claim 33
Dependent Claim
196 words
A process of chemically-enhanced additive or subtractive processing of a substrate in an electroless fluid bath, said bath comprising an electrolyte, comprising directing a high intensity energy beam to heat said substrate at the site on said substrate to be treated concomitantly with directing a jet of said fluid at the locus of desired enhanced-chemical action on said substrate at said site, said jet and said beam being collinear, said plating or etching being accomplished selectively by applying said beam to spots on said substrate to be processed concomitantly with use of said jet to transport the plating solution rapidly to and at the surface of said substrate to be chemically processed, said beam being passed along the length of said jet of fluid which acts as a light guide or waveguide for said beam, with said beam cooperating with said fluid to apply energy to said substrate at said site, whereby said process performed by said chemical fluid is accelerated at said site as contrasted with the surrounding areas near said site and within said locus, and said beam having a diameter comparable to or less than the diameter of said jet at said locus.
Claim 34
Dependent Claim
199 words
A process of chemically-enhanced additive or subtractive processing of a substrate in an electrodeless fluid bath comprising employing a fluid bath comprising an electrolyte, directing a high intensity energy beam to heat said substrate at the site on said substrate to be treated concomitantly with directing a jet of said fluid at the locus of desired enhanced-chemical action on said substrate, said locus being at said site, said jet and said beam being collinear, said processing being accomplished selectively by applying said beam to spots on said substrate to be processed concomitantly with use of said jet to transport the plating solution rapidly to and at the surface of said substrate to be chemically processed, said beam being passed along the length of said jet of fluid which acts as a light guide or waveguide for said beam, with said beam cooperating with said fluid to apply energy to said substrate at said site, whereby said process performed by said chemical fluid is accelerated at said site as contrasted with the surrounding areas near said site and within said locus, and said beam having a diameter comparable to or less than the diameter of said jet at said locus.
Claim 35
Dependent Claim
199 words
A process of chemically-enhanced additive or subtractive processing of a substrate in an electrodeless fluid bath comprising employing a fluid bath comprising an electrolyte, directing a high intensity energy beam to heat said substrate at the site on said substrate to be treated concomitantly with directing a jet of said fluid at the locus of desired enhanced-chemical action on said substrate, said locus being at said site, said jet and said beam being collinear, said processing being accomplished selectively by applying said beam to spots on said substrate to be processed concomitantly with use of said jet to transport the plating solution rapidly to and at the surface of said substrate to be chemically processed, said beam being passed along the length of said jet of fluid which acts as a light guide or waveguide for said beam, with said beam cooperating with said fluid to apply energy to said substrate at said site, whereby said process performed by said chemical fluid is accelerated at said site as contrasted with the surrounding areas near said site and within said locus, and said beam having a diameter comparable to or less than the diameter of said jet at said locus.
Claim 36
Dependent Claim
198 words
A process of chemically-enhanced additive or subtractive processing of a substrate in an exchange plating fluid bath said bath comprising an electrolyte said process comprising directing a high intensity energy beam to heat said substrate at the site on said substrate to be treated concomitantly with directing a jet of said fluid electrolyte at the locus of desired enhanced-chemical action on said substrate at said site, said jet and said beam being collinear, said plating or etching being accomplished selectively by applying said beam to spots on said substrate to be processed concomitantly with use of said jet to transport the plating solution rapidly to and at the surface of said substrate to be chemically processed, said beam passing along the length of said jet of fluid which acts as a light guide or waveguide for said beam, with said beam cooperating with said fluid to apply energy to said substrate at said site, whereby said process performed by said fluid is accelerated at said site as contrasted with the surrounding areas near said site and within said locus, and said beam having a diameter comparable to or less than the diameter of said jet at said locus.
Claim 37
Dependent Claim
198 words
A process of chemically-enhanced additive or subtractive processing of a substrate in an exchange plating fluid bath said bath comprising an electrolyte said process comprising directing a high intensity energy beam to heat said substrate at the site on said substrate to be treated concomitantly with directing a jet of said fluid electrolyte at the locus of desired enhanced-chemical action on said substrate at said site, said jet and said beam being collinear, said plating or etching being accomplished selectively by applying said beam to spots on said substrate to be processed concomitantly with use of said jet to transport the plating solution rapidly to and at the surface of said substrate to be chemically processed, said beam passing along the length of said jet of fluid which acts as a light guide or waveguide for said beam, with said beam cooperating with said fluid to apply energy to said substrate at said site, whereby said process performed by said fluid is accelerated at said site as contrasted with the surrounding areas near said site and within said locus, and said beam having a diameter comparable to or less than the diameter of said jet at said locus.
Claim 38
Dependent Claim
29 words
The process of claim 1 wherein said fluid comprises a liquid electrolyte with said beam cooperating with said fluid to enhance the rate of said process at said site.
Claim 39
Dependent Claim
49 words
The process of claim 1 wherein said energy beam is directed along an axis which intersects said jet of fluid downstream from the origin thereof and merges therewith to travel collinearly therealong with said beam cooperating with said fluid to enhance the rate of said process at said site.
Claim 40
Dependent Claim
120 words
A process of plating by employing a jet plating system employing a jet of plating fluid, said fluid comprising an electrolyte, said jet comprising a relatively wide jet in conjunction with a relatively narrow focussed laser beam with said beam and said jet being directed at the same site on a substrate, with said beam covering a smaller surface within the surface covered by said jet, said beam having a diameter comparable to or less than the diameter of said jet at said locus, with two plating rates for patterning a center section that is plated to a much higher value than the periphery, and said beam having a diameter less than the diameter of said jet at said site.
Claim 41
Dependent Claim
120 words
A process of plating by employing a jet plating system employing a jet of plating fluid, said fluid comprising an electrolyte, said jet comprising a relatively wide jet in conjunction with a relatively narrow focussed laser beam with said beam and said jet being directed at the same site on a substrate, with said beam covering a smaller surface within the surface covered by said jet, said beam having a diameter comparable to or less than the diameter of said jet at said locus, with two plating rates for patterning a center section that is plated to a much higher value than the periphery, and said beam having a diameter less than the diameter of said jet at said site.
Claim 42
Dependent Claim
95 words
A process of etching by employing a jet etching system employing a jet of etching fluid comprising an electrolyte, and said jet comprising a relatively wide jet in conjunction with a relatively narrow focussed laser beam with said beam and said jet being directed at the same site on a substrate, with said beam covering a smaller surface within the surface covered by said jet, said beam having a diameter less than the diameter of said jet at said site, with two etching rates, the center etching rate being greater than that at the periphery.
Claim 43
Dependent Claim
95 words
A process of etching by employing a jet etching system employing a jet of etching fluid comprising an electrolyte, and said jet comprising a relatively wide jet in conjunction with a relatively narrow focussed laser beam with said beam and said jet being directed at the same site on a substrate, with said beam covering a smaller surface within the surface covered by said jet, said beam having a diameter less than the diameter of said jet at said site, with two etching rates, the center etching rate being greater than that at the periphery.
Claim 44
Dependent Claim
100 words
A process of etching by employing a jet etching system employing a jet of etching fluid, said etching fluid comprising an electrolyte, and said jet comprising a relatively wide jet in conjunction with a relatively narrow focussed laser with a single very high etching rate defined by the laser with low peripheral etching, depending on the etchant, where, said jet has a stagnation region that is much larger in diameter than said laser, hence allowing for the two finite etching rates to occur simultaneously, whereby said beam has a diameter less than the diameter of said jet at said site.
Claim 45
Dependent Claim
100 words
A process of etching by employing a jet etching system employing a jet of etching fluid, said etching fluid comprising an electrolyte, and said jet comprising a relatively wide jet in conjunction with a relatively narrow focussed laser with a single very high etching rate defined by the laser with low peripheral etching, depending on the etchant, where, said jet has a stagnation region that is much larger in diameter than said laser, hence allowing for the two finite etching rates to occur simultaneously, whereby said beam has a diameter less than the diameter of said jet at said site.
Claim 46
Dependent Claim
122 words
A process of plating a metal on a substrate by employing a jet plating system employing a jet of plating fluid comprising an electrolyte, said jet comprising a relatively wide jet in conjunction with a relatively narrow focussed laser beam with two plating rates, a substrate, the center plating rate being greater than the plating rate at periphery, said jet being directed onto a spot on said substrate where a thickness of metal is plated, said laser beam being directed collinearly with said jet at the center of said spot of metal which results in a thicker deposit of metal at said center of said spot, and said beam having a diameter less than the diameter of said jet at said site.
Claim 47
Dependent Claim
122 words
A process of plating a metal on a substrate by employing a jet plating system employing a jet of plating fluid comprising an electrolyte, said jet comprising a relatively wide jet in conjunction with a relatively narrow focussed laser beam with two plating rates, a substrate, the center plating rate being greater than the plating rate at periphery, said jet being directed onto a spot on said substrate where a thickness of metal is plated, said laser beam being directed collinearly with said jet at the center of said spot of metal which results in a thicker deposit of metal at said center of said spot, and said beam having a diameter less than the diameter of said jet at said site.
Claim 48
Dependent Claim
102 words
A process of plating/etching by employing a jet plating/etching system employing a jet of plating/etching, electrolyte fluid comprising a relatively wide jet in conjunction with a relatively narrow focussed laser beam with a single very high plating/etching rate defined by said laser beam with low peripheral plating/etching, said beam and said jet being directed onto a spot on said substrate, where, said jet has a stagnation region that is much larger in diameter than said laser, and said beam having a diameter less than the diameter of said jet at said spot, hence allowing for the two finite plating/etching rates to occur.
Claim 49
Dependent Claim
102 words
A process of plating/etching by employing a jet plating/etching system employing a jet of plating/etching, electrolyte fluid comprising a relatively wide jet in conjunction with a relatively narrow focussed laser beam with a single very high plating/etching rate defined by said laser beam with low peripheral plating/etching, said beam and said jet being directed onto a spot on said substrate, where, said jet has a stagnation region that is much larger in diameter than said laser, and said beam having a diameter less than the diameter of said jet at said spot, hence allowing for the two finite plating/etching rates to occur.
Claim 50
Dependent Claim
140 words
A process of etching a substrate by employing a jet etching system employing an electrolyte fluid and a jet comprising a wide jet of etching fluid in conjunction with a narrow focussed laser beam with two etching rates, the center etching rate resulting from etching on a site where said beam hits said substrate being greater than the etching rate at the periphery of said site, a jet-etching jet directed onto a spot on said substrate where a hole is etched in said substrate, and a laser beam is directed, collinearly with said jet, with said site where said beam is directed being at the center of said hole, and said beam having a diameter less than the diameter of said jet at said spot, which results in a deeper hole at said site in said center of said hole.
Claim 51
Dependent Claim
140 words
A process of etching a substrate by employing a jet etching system employing an electrolyte fluid and a jet comprising a wide jet of etching fluid in conjunction with a narrow focussed laser beam with two etching rates, the center etching rate resulting from etching on a site where said beam hits said substrate being greater than the etching rate at the periphery of said site, a jet-etching jet directed onto a spot on said substrate where a hole is etched in said substrate, and a laser beam is directed, collinearly with said jet, with said site where said beam is directed being at the center of said hole, and said beam having a diameter less than the diameter of said jet at said spot, which results in a deeper hole at said site in said center of said hole.
Claim 52
Dependent Claim
81 words
In a process of chemically-enhanced electroetching of a substrate in a chemically-active electrolyte fluid, the improvement comprising directing a high intensity energy beam to heat said substrate at the site to be treated concomitantly with directing a jet of said electrolyte fluid at the locus of desired enhanced-chemical action on said substrate, said site being included within said locus, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said locus.
Claim 53
Dependent Claim
81 words
In a process of chemically-enhanced electroetching of a substrate in a chemically-active electrolyte fluid, the improvement comprising directing a high intensity energy beam to heat said substrate at the site to be treated concomitantly with directing a jet of said electrolyte fluid at the locus of desired enhanced-chemical action on said substrate, said site being included within said locus, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said locus.
Claim 54
Dependent Claim
92 words
In a process of chemically-enhanced electroless etching of a substrate in a chemically-active electrolyte fluid, the improvement comprising directing a high intensity energy beam to heat said substrate at the site to be treated concomitantly with directing a jet of said electrolyte fluid at the locus of desired enhanced-chemical action on said substrate, said beam passing collinearly through said jet to said site, said site being included within said locus, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said locus.
Claim 55
Dependent Claim
92 words
In a process of chemically-enhanced electroless etching of a substrate in a chemically-active electrolyte fluid, the improvement comprising directing a high intensity energy beam to heat said substrate at the site to be treated concomitantly with directing a jet of said electrolyte fluid at the locus of desired enhanced-chemical action on said substrate, said beam passing collinearly through said jet to said site, said site being included within said locus, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said locus.
Claim 56
Dependent Claim
95 words
In a process of chemically-enhanced electrodeless etching and/or exchange etching of a substrate in a chemically-active electrolyte fluid, the improvement comprising diverting a high intensity energy beam to heat said substrate at the site to be treated concomitantly with directing a jet of said electrolyte fluid at the locus of desired enhanced-chemical action on said substrate, said beam passing collinearly through said jet to said site, said site being included within said locus, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said locus.
Claim 57
Dependent Claim
95 words
In a process of chemically-enhanced electrodeless etching and/or exchange etching of a substrate in a chemically-active electrolyte fluid, the improvement comprising diverting a high intensity energy beam to heat said substrate at the site to be treated concomitantly with directing a jet of said electrolyte fluid at the locus of desired enhanced-chemical action on said substrate, said beam passing collinearly through said jet to said site, said site being included within said locus, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said locus.
Claim 58
Dependent Claim
93 words
In a process of chemically-enhanced etching and/or exchange etching of a substrate in a chemically-active, electrolyte fluid, the improvement comprising directing a high intensity energy beam to heat said substrate at the site to be treated concomitantly with directing a jet of said fluid at the locus of desired enhanced-chemical action on said substrate, said beam passing collinearly through said jet to said site, said site being included within said locus, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said locus.
Claim 59
Dependent Claim
93 words
In a process of chemically-enhanced etching and/or exchange etching of a substrate in a chemically-active, electrolyte fluid, the improvement comprising directing a high intensity energy beam to heat said substrate at the site to be treated concomitantly with directing a jet of said fluid at the locus of desired enhanced-chemical action on said substrate, said beam passing collinearly through said jet to said site, said site being included within said locus, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said locus.
Claim 60
Dependent Claim
91 words
In a process of chemically-enhanced electroplating of a substrate in a chemically-active, electrolyte fluid, the improvement comprising directing a high intensity energy beam to heat said substrate at the site to be treated concomitantly with directing a jet of said electrolyte fluid at the locus of desired enhanced-chemical action on said substrate, said beam passing collinearly through said jet to said site, said site being included within said locus, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said locus.
Claim 61
Dependent Claim
91 words
In a process of chemically-enhanced electroplating of a substrate in a chemically-active, electrolyte fluid, the improvement comprising directing a high intensity energy beam to heat said substrate at the site to be treated concomitantly with directing a jet of said electrolyte fluid at the locus of desired enhanced-chemical action on said substrate, said beam passing collinearly through said jet to said site, said site being included within said locus, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said locus.
Claim 62
Dependent Claim
92 words
In a process of chemically-enhanced electroless plating of a substrate in a chemically-active electrolyte fluid, the improvement comprising directing a high intensity energy beam to heat said substrate at the site to be treated concomitantly with directing a jet of said electrolyte fluid at the locus of desired enhanced-chemical action on said substrate, said beam passing collinearly through said jet to said site, said site being included within said locus, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said locus.
Claim 63
Dependent Claim
92 words
In a process of chemically-enhanced electroless plating of a substrate in a chemically-active electrolyte fluid, the improvement comprising directing a high intensity energy beam to heat said substrate at the site to be treated concomitantly with directing a jet of said electrolyte fluid at the locus of desired enhanced-chemical action on said substrate, said beam passing collinearly through said jet to said site, said site being included within said locus, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said locus.
Claim 64
Dependent Claim
95 words
In a process of chemically-enhanced electrodeless plating and/or exchange plating of a substrate in a chemically-active electrolyte fluid, the improvement comprising directing a high intensity energy beam to heat said substrate at the site to be treated concomitantly with directing a jet of said electrolyte fluid at the locus of desired enhanced-chemical action on said substrate, said beam passing collinearly through said jet to said site, said site being included within said locus, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said locus.
Claim 65
Dependent Claim
95 words
In a process of chemically-enhanced electrodeless plating and/or exchange plating of a substrate in a chemically-active electrolyte fluid, the improvement comprising directing a high intensity energy beam to heat said substrate at the site to be treated concomitantly with directing a jet of said electrolyte fluid at the locus of desired enhanced-chemical action on said substrate, said beam passing collinearly through said jet to said site, said site being included within said locus, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said locus.
Claim 66
Dependent Claim
79 words
In a process of chemically-enhanced plating of a substrate in a chemically-active fluid, the improvement comprising directing a high intensity energy beam to heat said substrate at the site to be treated concomitantly with directing a jet of said fluid at the locus of desired enhanced-chemical action on said substrate, said site being included within said locus, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said locus.
Claim 67
Dependent Claim
79 words
In a process of chemically-enhanced plating of a substrate in a chemically-active fluid, the improvement comprising directing a high intensity energy beam to heat said substrate at the site to be treated concomitantly with directing a jet of said fluid at the locus of desired enhanced-chemical action on said substrate, said site being included within said locus, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said locus.
Claim 68
Dependent Claim
163 words
A laser-jet plating system including a plating fluid comprising an electrolyte, means for providing a source of a laser beam, a workpiece, a jet nozzle for emitting a jet of plating fluid, a lens, said laser beam being directed through said lens to focus approximately at the center of said jet nozzle, a numerically-controlled drive, a cathode attached to said numerically-controlled drive and to said workpiece, said jet both resupplying ions to be plated and acting as an optical waveguide or light pipe for said laser beam means for simultaneously directing said jet of said fluid at the locus of desired enhanced-chemical action on said substrate, said laser beam being collinear with said jet, said site and said locus coinciding at the same spot, with said beam cooperating with said fluid to enhance the rate of said system at said site, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said spot.
Claim 69
Dependent Claim
163 words
A laser-jet plating system including a plating fluid comprising an electrolyte, means for providing a source of a laser beam, a workpiece, a jet nozzle for emitting a jet of plating fluid, a lens, said laser beam being directed through said lens to focus approximately at the center of said jet nozzle, a numerically-controlled drive, a cathode attached to said numerically-controlled drive and to said workpiece, said jet both resupplying ions to be plated and acting as an optical waveguide or light pipe for said laser beam means for simultaneously directing said jet of said fluid at the locus of desired enhanced-chemical action on said substrate, said laser beam being collinear with said jet, said site and said locus coinciding at the same spot, with said beam cooperating with said fluid to enhance the rate of said system at said site, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said spot.
Claim 70
Dependent Claim
168 words
A laser-jet system for chemical treatment with an electrolyte including a source of a laser beam, a chemical solution comprising an electrolyte, a laser-jet cell with an inlet chamber containing said chemical solution maintained under pressure, said chamber including an electrode, a jet nozzle, a workpiece to be chemically treated with said solution, said workpiece being supported for relative motion with respect to the jet from said nozzle for patterning by treatment with said chemical solution, said laser beam being directed through said jet nozzle, said electrode being connected to said workpiece, means for simultaneously directing said jet of said fluid at the locus of desired enhanced-chemical action on said workpiece, said laser beam being collinear with said jet, said site and said locus coinciding at the same spot, with said beam cooperating with said fluid to enhance the rate of said system at said site, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said spot.
Claim 71
Dependent Claim
168 words
A laser-jet system for chemical treatment with an electrolyte including a source of a laser beam, a chemical solution comprising an electrolyte, a laser-jet cell with an inlet chamber containing said chemical solution maintained under pressure, said chamber including an electrode, a jet nozzle, a workpiece to be chemically treated with said solution, said workpiece being supported for relative motion with respect to the jet from said nozzle for patterning by treatment with said chemical solution, said laser beam being directed through said jet nozzle, said electrode being connected to said workpiece, means for simultaneously directing said jet of said fluid at the locus of desired enhanced-chemical action on said workpiece, said laser beam being collinear with said jet, said site and said locus coinciding at the same spot, with said beam cooperating with said fluid to enhance the rate of said system at said site, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said spot.
Claim 72
Dependent Claim
212 words
A laser-jet chemical treatment system including a source of a laser beam, a laser-jet cell with an inlet chamber containing a chemical solution comprising an electrolyte maintained under pressure, said chamber including an electrode, a jet nozzle, a workpiece to be chemically treated with said electrolyte solution, said workpiece being supported for relative motion with respect to the jet from said nozzle for patterning by treatment with said chemical solution, a cathode said cathode being connected to said workpiece said reservoir being heated by a heating means, said electrolyte solution being circulated through a line to a pump, with the outlet of said pump being connected by another line to said inlet chamber, and said laser beam being directed through said jet nozzle said jet nozzle and said laser being adapted for simultaneously directing said jet of said solution at the locus of desired enhanced-chemical action on said workpiece, said laser beam being collinear with said jet, said site and said locus coinciding at the same spot, with said beam cooperating with said fluid to enhance the rate of chemical treatment of said workpiece by said system at said site, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said spot.
Claim 73
Dependent Claim
212 words
A laser-jet chemical treatment system including a source of a laser beam, a laser-jet cell with an inlet chamber containing a chemical solution comprising an electrolyte maintained under pressure, said chamber including an electrode, a jet nozzle, a workpiece to be chemically treated with said electrolyte solution, said workpiece being supported for relative motion with respect to the jet from said nozzle for patterning by treatment with said chemical solution, a cathode said cathode being connected to said workpiece said reservoir being heated by a heating means, said electrolyte solution being circulated through a line to a pump, with the outlet of said pump being connected by another line to said inlet chamber, and said laser beam being directed through said jet nozzle said jet nozzle and said laser being adapted for simultaneously directing said jet of said solution at the locus of desired enhanced-chemical action on said workpiece, said laser beam being collinear with said jet, said site and said locus coinciding at the same spot, with said beam cooperating with said fluid to enhance the rate of chemical treatment of said workpiece by said system at said site, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said spot.
Claim 74
Dependent Claim
15 words
The system in accordance with claim 45 wherein said electrolyte is preheated by heater means.
Claim 75
Dependent Claim
17 words
A system in accordance with claim 46 wherein said laser beam is a cw argon laser beam.
Claim 76
Dependent Claim
115 words
A process of plating with an electrolyte fluid by the use of a wide jet in conjunction with a narrow focussed laser with a single very fine plating rate defined by the laser with no peripheral plating, depending on the plating solution, said jet having a stagnation region that is much larger in diameter than said jet, hence allowing for the two finite plating jobs to occur simultaneously, said jet being collinear with said energy beam with said beam cooperating with said fluid to enhance the rate of said process at said site, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said site.
Claim 77
Dependent Claim
115 words
A process of plating with an electrolyte fluid by the use of a wide jet in conjunction with a narrow focussed laser with a single very fine plating rate defined by the laser with no peripheral plating, depending on the plating solution, said jet having a stagnation region that is much larger in diameter than said jet, hence allowing for the two finite plating jobs to occur simultaneously, said jet being collinear with said energy beam with said beam cooperating with said fluid to enhance the rate of said process at said site, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said site.
Claim 78
Dependent Claim
109 words
A laser-jet treatment system including means for producing an energy beam, a jet nozzle having an input and an output for emitting said jet of chemically-active fluid, said energy beam being directed through a lens to focus approximately at the center of the input of said jet nozzle and to pass therethrough, a workpiece aligned with the output of said nozzle for said chemically active electrolyte fluid and said energy beam aligned for said fluid and said beam to hit said workpiece simultaneously at the same locus, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said locus.
Claim 79
Dependent Claim
109 words
A laser-jet treatment system including means for producing an energy beam, a jet nozzle having an input and an output for emitting said jet of chemically-active fluid, said energy beam being directed through a lens to focus approximately at the center of the input of said jet nozzle and to pass therethrough, a workpiece aligned with the output of said nozzle for said chemically active electrolyte fluid and said energy beam aligned for said fluid and said beam to hit said workpiece simultaneously at the same locus, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said locus.
Claim 80
Dependent Claim
38 words
A system in accordance with claim 50 wherein said energy beam passes through a window transparent to said energy beam in a chamber adapted to contain said electrolyte fluid confined for ejection through said nozzle towards said workpiece.
Claim 81
Dependent Claim
37 words
A system in accordance with claim 50 wherein an electrode is housed within said chamber for containing said electrolyte or in electrical contact with said chamber and said workpiece comprises another electrode in an electrochemical treatment system.
Claim 82
Dependent Claim
18 words
A system in accordance with claim 51 wherein said electrolyte fluid is maintained under pressure in said chamber.
Claim 83
Dependent Claim
231 words
A laser-jet treatment system including means for producing an energy beam, a jet nozzle having an input and an output for emitting said jet of chemically-active fluid, said energy beam being directed through a lens to focus approximately at the center of the input of said jet nozzle and to pass therethrough, a workpiece aligned with the output of said nozzle for said chemically active fluid and said energy beam to hit said workpiece simultaneously at the same locus, with said energy beam comprising a laser beam, a laser-jet cell with an inlet chamber containing a chemical solution maintained under pressure, said chamber including an electrode, a workpiece to be chemically treated with said solution connected to said electrode, said workpiece being supported for relative motion with respect to the jet from said nozzle for patterning by treatment with said chemical solution, said reservoir being heated by a heating means, said electrolyte being circulated through a line to a pump, with the outlet of said pump being connected by another line to said inlet chamber, said laser beam being directed through said jet nozzle, said chemically active fluid and said energy beam being aligned for said fluid and said beam to hit said workpiece simultaneously at the same locus, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said locus.
Claim 84
Dependent Claim
231 words
A laser-jet treatment system including means for producing an energy beam, a jet nozzle having an input and an output for emitting said jet of chemically-active fluid, said energy beam being directed through a lens to focus approximately at the center of the input of said jet nozzle and to pass therethrough, a workpiece aligned with the output of said nozzle for said chemically active fluid and said energy beam to hit said workpiece simultaneously at the same locus, with said energy beam comprising a laser beam, a laser-jet cell with an inlet chamber containing a chemical solution maintained under pressure, said chamber including an electrode, a workpiece to be chemically treated with said solution connected to said electrode, said workpiece being supported for relative motion with respect to the jet from said nozzle for patterning by treatment with said chemical solution, said reservoir being heated by a heating means, said electrolyte being circulated through a line to a pump, with the outlet of said pump being connected by another line to said inlet chamber, said laser beam being directed through said jet nozzle, said chemically active fluid and said energy beam being aligned for said fluid and said beam to hit said workpiece simultaneously at the same locus, and said beam having a diameter at said site comparable to or less than the diameter of said jet at said locus.
References Cited (Backward Citations)
US2846346A
Cited
US2799637A
Cited
US2930949A
Cited
US3039515A
Cited
US3345274A
Cited
US3486221A
Cited
US3679863A
Cited
US3810829A
Cited
US4042006A
Cited
US3965328A
Cited
US4217183A
Cited
US4283259A
Cited
US4390774A
Cited
US4409458A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-02-05 | 1988-08-06 | 1989-02-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-02-05 | 1992-08-06 | 1993-02-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-02-05 | 1996-08-06 | 1997-02-05 | $7700.00 | Window Closed / Lapsed |