US4493902A — Fluid catalytic cracking catalyst comprising micr…

Claim 1

Independent Claim 97 words

A fluid catalytic cracking catalyst comprising microspheres containing at least about 40% by weight Y-faujasite and having less than about 0.20 cc/g. of pores having diameters in the range of 20-100Å, said microspheres having the following characteristics: (a) a deactivated activity at least about 1.5 times that of standard commercial catalyst; (b) a severely deactivated activity at least about 1.5 times that of standard commercial catalyst; (c) a coke yield no greater than about that of standard commercial catalyst at 70% conversion; and (d) an EAI no more than about 5.0 times that of standard commercial catalyst.

Claim 2

Dependent Claim 97 words

A fluid catalytic cracking catalyst comprising microspheres containing at least about 40% by weight Y-faujasite and having less than about 0.20 cc/g. of pores having diameters in the range of 20-100Å, said microspheres having the following characteristics: (a) a deactivated activity at least about 1.5 times that of standard commercial catalyst; (b) a severely deactivated activity at least about 1.5 times that of standard commercial catalyst; (c) a coke yield no greater than about that of standard commercial catalyst at 70% conversion; and (d) an EAI no more than about 5.0 times that of standard commercial catalyst.

Claim 3

Dependent Claim 30 words

The fluid catalytic cracking catalyst of claim 1 wherein the microspheres have the following characteristic: a hydrogen yield no greater than about that of standard commercial catalyst at 70% conversion.

Claim 4

Dependent Claim 39 words

The fluid catalytic cracking catalyst of claim 1 wherein the microspheres have at least about the deactivated activity of standard commercial catalyst when about 4000 ppm of vanadium and about 2000 ppm of nickel are deposited on both catalysts.

Claim 5

Dependent Claim 59 words

The fluid catalytic cracking catalyst of claim 1 wherein the microspheres have the following characteristics: (a) a deactivated activity at least about 2.0 times that of standard commercial catalyst; (b) a severely deactivated activity at least about 2.0 times that of standard commercial catalyst; and (c) an EAI no more than about 3.0 times that of standard commercial catalyst.

Claim 6

Dependent Claim 41 words

The fluid catalytic cracking catalyst of claim 1 wherein the microspheres have about 1.5 times the deactivated activity as compared to standard commercial catalyst when about 4000 ppm of vanadium and about 2000 ppm of nickel are deposited on both catalysts.

Claim 7

Dependent Claim 24 words

The fluid catalytic cracking catalyst of claim 1 wherein the microspheres have no more than about 3.0 times the EAI of standard commercial catalyst.

Claim 8

Dependent Claim 24 words

The fluid catalytic cracking catalyst of claim 1 wherein the microspheres have no more than about 1.5 times the EAI of standard commercial catalyst.

Claim 9

Dependent Claim 51 words

The fluid catalytic cracking catalyst of claim 1 wherein the microspheres contain a non-zeolitic component comprising the zeolite crystallization process residue of calcined clay, said calcined clay comprising about 30-60% by weight metakaolin and about 40-70% by weight kaolin clay that had been calcined at least substantially through its characteristic exotherm.

Claim 10

Dependent Claim 42 words

The fluid catalytic cracking catalyst of claim 8 wherein the two types of calcined clay were present in the same microspheres and the kaolin clay that had been calcined at least substantially through its characteristic exotherm contained a substantial amount of mullite.

Claim 11

Dependent Claim 41 words

The fluid catalytic cracking catalyst of claim 8 wherein the two types of calcined clay were present in the same microspheres and said kaolin clay that had been calcined at least substantially through its characteristic / exotherm contained substantially no mullite.

Claim 12

Dependent Claim 17 words

The fluid catalytic cracking catalyst of claim 8 wherein the microspheres contain about 50-70% by weight Y-faujasite.

Claim 13

Dependent Claim 21 words

The fluid catalytic cracking catalyst of claim 11 wherein the two types of calcined clay were present in the same microspheres.

Claim 14

Dependent Claim 17 words

The fluid catalytic cracking catalyst of claim 1 wherein the microspheres contain about 50-70% by weight Y-faujasite.

Claim 15

Dependent Claim 26 words

The fluid catalytic cracking catalyst of claim 13 wherein the Y-faujasite, in the sodium form, has a crystalline unit cell size of less than about 24.73Å.

Claim 16

Dependent Claim 30 words

The fluid catalytic cracking catalyst of claim 14 wherein the microspheres have the following characteristic: a hydrogen yield no greater than about that of standard commercial catalyst at 70% conversion.

Claim 17

Dependent Claim 26 words

The fluid catalytic cracking catalyst of claim 1 wherein the Y-faujasite, in the sodium form, has a crystalline unit cell size of less than about 24.69Å.

Claim 18

Dependent Claim 26 words

The fluid catalytic cracking catalyst of claim 1 wherein the microspheres have less than about 0.15 cc/g. of pores having diameters in the range of 20-100Å.

Claim 19

Dependent Claim 41 words

The fluid catalytic cracking catalyst of claim 1 wherein the microspheres contain less than about 0.7% by weight Na 2 O, more than about 4% weight REO, and have a SiO 2 /Al 2 O 3 molar ratio of about 1.7-3.4.

Claim 20

Dependent Claim 31 words

The fluid catalytic cracking catalyst of claim 18 wherein the microspheres contain about 50-70% by weight Y-faujasite having, in its sodium form, a unit cell size of less than about 24.73Å.

Claim 21

Dependent Claim 61 words

The fluid catalytic cracking catalyst of claim 19 wherein the microspheres have less than about 0.15 cc/g. of pores having diameters in the range of 20-100Å, less than about 0.20 cc/g. of pores having diameters in the range of 600-20,000Å, a surface area of about 400-750m 2 /g., and a bulk density of the 200/270 mesh fraction of about 0.9-1.2 g/cc.

Claim 22

Dependent Claim 21 words

The fluid catalytic cracking catalyst of claim 1 wherein the microspheres have a total porosity of less than about 0.15 cc/g.

Claim 23

Dependent Claim 21 words

The fluid catalytic cracking catalyst of claim 1 wherein the microspheres have a total porosity of less than about 0.10 cc/g.

Claim 24

Dependent Claim 21 words

The fluid catalytic cracking catalyst of claim 14 wherein the microspheres have a total porosity of less than about 0.15 cc/g.

Claim 25

Dependent Claim 155 words

A fluid catalytic cracking catalyst comprising microspheres containing more than about 40% by weight Y-faujasite, less than about 0.7 by weight Na 2 O, more than about 4% by weight REO, and having a SiO 2 /Al 2 O 3 molar ratio of about 1.7-3.4, less than about 0.20 cc/g. of pores having diameters in the range of 20-100Å, less than about 0.30 cc/g. of pores having diameters in the range of 600-20,000Å, a surface area of about 300-750m 2 /g. and a bulk density of the 200/270 mesh fraction of about 0.8-1.2 g/cc., said microspheres comprising: (a) a non-zeolitic component comprising the zeolite crystallization process residue of calcined clay, said calcined clay comprising about 30-60% by weight metakaolin and about 40-70% by weight kaolin clay that had been calcined at least substantially through its characteristic exotherm; and (b) Y-faujasite having, in the sodium form, a crystalline unit cell size of less than about 24.73Å.

Claim 26

Dependent Claim 155 words

A fluid catalytic cracking catalyst comprising microspheres containing more than about 40% by weight Y-faujasite, less than about 0.7 by weight Na 2 O, more than about 4% by weight REO, and having a SiO 2 /Al 2 O 3 molar ratio of about 1.7-3.4, less than about 0.20 cc/g. of pores having diameters in the range of 20-100Å, less than about 0.30 cc/g. of pores having diameters in the range of 600-20,000Å, a surface area of about 300-750m 2 /g. and a bulk density of the 200/270 mesh fraction of about 0.8-1.2 g/cc., said microspheres comprising: (a) a non-zeolitic component comprising the zeolite crystallization process residue of calcined clay, said calcined clay comprising about 30-60% by weight metakaolin and about 40-70% by weight kaolin clay that had been calcined at least substantially through its characteristic exotherm; and (b) Y-faujasite having, in the sodium form, a crystalline unit cell size of less than about 24.73Å.

Claim 27

Dependent Claim 76 words

The fluid catalytic cracking catalyst of claim 24 wherein the microspheres have the following characteristics: (a) a deactivated activity at least about 1.5 times that of standard commercial catalyst; (b) a severely deactivated activity at least about 1.5 times that of standard commerical catalyst; (c) a coke yield no greater than about that of standard commercial catalyst at 70% conversion; and (d) an EAI of no more than about 5.0 times that of standard commercial catalyst.

Claim 28

Dependent Claim 30 words

The fluid catalytic cracking catalyst of claim 25 wherein the microspheres have the following characteristic: a hydrogen yield no greater than about that of standard commercial catalyst at 70% conversion.

Claim 29

Dependent Claim 26 words

The fluid catalytic cracking catalyst of claim 25 wherein the EAI of the microspheres is no more than about 3.0 times that of standard commercial catalyst.

Claim 30

Dependent Claim 26 words

The fluid catalytic cracking catalyst of claim 25 wherein the EAI of the microspheres is no more than about 1.5 times that of standard commercial catalyst.

Claim 31

Dependent Claim 42 words

The fluid catalytic cracking catalyst of claim 24 wherein the two types of calcined clay were present in the same microspheres and the kaolin clay that had been calcined at least substantially through its characteristic exotherm contained a substantial amount of mullite.

Claim 32

Dependent Claim 40 words

The fluid catalytic cracking catalyst of claim 24 wherein the two types of calcined clay were present in the same microspheres and the kaolin clay that had been calcined at least substantially through its characteristic exotherm contained substantially no mullite.

Claim 33

Dependent Claim 21 words

The fluid catalytic cracking catalyst of claim 25 wherein the two types of calcined clay were present in the same microspheres.

Claim 34

Dependent Claim 17 words

The fluid catalytic cracking catalyst of claim 24 wherein the microspheres contain about 50-70% by weight Y-faujasite.

Claim 35

Dependent Claim 26 words

The fluid catalytic cracking catalyst of claim 24 wherein the Y-faujasite, in the sodium form, has a crystalline unit cell size of less than about 24.69Å.

Claim 36

Dependent Claim 29 words

The fluid catalytic cracking catalyst of claim 24 wherein the microspheres contain more than about 7% by weight REO and less than about 0.5% by weight Na 2 O.

Claim 37

Dependent Claim 21 words

The fluid catalytic cracking catalyst of claim 24 wherein the microspheres have a total porosity of less than about 0.15 cc/g.

Claim 38

Dependent Claim 61 words

The fluid catalytic cracking catalyst of claim 24 wherein the microspheres have less than about 0.15 cc/g. of pores having diameters in the range of 20-100Å, less than about 0.20 cc/g. of pores having diameters in the range of 600-20,000Å, a surface area of about 400-750m 2 /g., and a bulk density of the 200/270 mesh fraction of about 0.9-1.2 g/cc.

Claim 39

Independent Claim 297 words

The method for making a fluid catalytic cracking catalyst comprising the steps of: (a) forming an aqueous slurry of finely divided hydrous kaolin clay and finely divided kaolin clay that has been calcined at least substantially through its characteristic exotherm; (b) spray drying the aqueous slurry to obtain microspheres comprising a mixture of hydrous kaolin clay and kaolin clay that has been calcined at least substantially through its characteristic exotherm; (c) calcining the microspheres obtained in step (b) at a temperature and for a time sufficient to convert the hydrous kaolin clay in the microspheres substantially to metakaolin and to obtain microspheres of calcined clay comprising a mixture of about 30-60% by weight metakaolin and about 40-70% by weight kaolin clay that has been calcined at least substantially through its characteristic exotherm; (d) mixing the microspheres obtained in step (c) with one or more sources of sodium silicate and water to obtain an alkaline slurry of microspheres of calcined clay in an aqueous solution containing sodium silicate, said sodium silicate being provided in an amount so that microspheres having a SiO 2 /Al 2 O 3 molar ratio of about 1.7-3.4 are obtained in step (h) below; (e) adding zeolite initiator to the kaolin clay that has been calcined at least substantially through its characteristic exotherm before step (f) below; (f) heating the slurry of microspheres of calcined clay to a temperature and for a time sufficient to crystallize at least about 40% by weight Y-faujasite in the microspheres, said Y-faujasite being in the sodium form; (g) separating the microspheres containing at least about 40% by weight Y-faujasite from at least a major portion of its mother liquor; (h) replacing sodium cations in the microspheres separated in step (g) with ammonium or rare earth cations or both.

Claim 40

Independent Claim 297 words

The method for making a fluid catalytic cracking catalyst comprising the steps of: (a) forming an aqueous slurry of finely divided hydrous kaolin clay and finely divided kaolin clay that has been calcined at least substantially through its characteristic exotherm; (b) spray drying the aqueous slurry to obtain microspheres comprising a mixture of hydrous kaolin clay and kaolin clay that has been calcined at least substantially through its characteristic exotherm; (c) calcining the microspheres obtained in step (b) at a temperature and for a time sufficient to convert the hydrous kaolin clay in the microspheres substantially to metakaolin and to obtain microspheres of calcined clay comprising a mixture of about 30-60% by weight metakaolin and about 40-70% by weight kaolin clay that has been calcined at least substantially through its characteristic exotherm; (d) mixing the microspheres obtained in step (c) with one or more sources of sodium silicate and water to obtain an alkaline slurry of microspheres of calcined clay in an aqueous solution containing sodium silicate, said sodium silicate being provided in an amount so that microspheres having a SiO 2 /Al 2 O 3 molar ratio of about 1.7-3.4 are obtained in step (h) below; (e) adding zeolite initiator to the kaolin clay that has been calcined at least substantially through its characteristic exotherm before step (f) below; (f) heating the slurry of microspheres of calcined clay to a temperature and for a time sufficient to crystallize at least about 40% by weight Y-faujasite in the microspheres, said Y-faujasite being in the sodium form; (g) separating the microspheres containing at least about 40% by weight Y-faujasite from at least a major portion of its mother liquor; (h) replacing sodium cations in the microspheres separated in step (g) with ammonium or rare earth cations or both.

Claim 41

Dependent Claim 23 words

The method of claim 37 wherein the clay that has been calcined at least substantially through its characteristic exotherm contains substantially no mullite.

Claim 42

Dependent Claim 47 words

The method of claim 38 further comprising conducting the following steps after step (g) and before step (h): (i) contacting the microspheres separated in step (g) with a solution containing sodium silicate; and (j) drying the microspheres obtained in step (i) to obtain microspheres containing sodium silicate.

Claim 43

Dependent Claim 49 words

The method of claim 38 wherein a portion of the mother liquor is left entrained in the microspheres in step (g) and further comprising conducting the following step after step (g) and before step (h): (i) drying the microspheres separated in step (g) to obtain microspheres containing sodium silicate.

Claim 44

Dependent Claim 22 words

The method of claim 37 wherein the clay that has been calcined through its characteristic exotherm contains a substantial amount of mullite.

Claim 45

Dependent Claim 41 words

The method of claim 37 wherein the sodium silicate provided in step (d) is, at least in part, mother liquor recycled from the separating step of step (g) and the mother liquor by-product produced during the preparation of another zeolite product.

Claim 46

Dependent Claim 17 words

The method of claim 37 further comprising adding zeolite initiator to the slurry formed in step (a).

Claim 47

Dependent Claim 37 words

The method of claim 37 wherein the molar ratios of constitutents present at the beginning of the crystallization process of step (f) are: ______________________________________ Na.sub.2 O/SiO.sub.2 SiO.sub.2 /Al.sub.2 O.sub.3 H.sub.2 O/Na.sub.2 O ______________________________________ 0.30-0.60 5-13 20-35 ______________________________________

Claim 48

Dependent Claim 27 words

The method of claim 44 wherein the weight ratio of water to clay microspheres at the beginning of the crystallization process of step (f) is about 4-12.

Claim 49

Dependent Claim 59 words

The method of claim 45 wherein the molar ratio of Na 2 O/SiO 2 in the solution phase at the beginning of the crystallization process of step (f) is about 0.49-0.57 and the weight ratio of SiO 2 in the solution phase to the clay microspheres at the beginning of the crystallization process of step (f) is about 1.0-1.7.

Claim 50

Dependent Claim 19 words

The method of claim 37 wherein about 50-70% by weight Y-faujasite is crystallized in the microspheres in step (f).

Claim 51

Independent Claim 211 words

The method for making a fluid catalytic cracking catalyst comprising the steps of: (a) making microspheres of calcined kaolin clay, said microspheres comprising about 30-60% by weight metakaolin and about 40-70% by weight kaolin clay that has been calcined at least substantially through its characteristic exotherm and containing no or no more than about 10% by weight hydrous clay; (b) mixing the microspheres of step (a) with one or more sources of sodium silicate and water to obtain an alkaline slurry of microspheres of calcined clay in an aqueous solution containing sodium silicate, said sodium silicate being provided in an amount so that microspheres having an SiO 2 /Al 2 O 3 molar ratio of about 1.7-3.4 are obtained in step (f) below; (c) adding zeolite initiator to the microspheres before step (d) below; (d) heating the slurry of microspheres of calcined clay to a temperature and for a time sufficient to crystallize at least about 40% by weight Y-faujasite in the microspheres, said Y-faujasite being in the sodium form; (e) separating the microspheres containing at least about 40% by weight Y-faujasite from at least a major portion of its mother liquor; (f) replacing sodium cations in the microspheres separated in step (e) with ammonium or rare earth cations or both.

Claim 52

Independent Claim 211 words

The method for making a fluid catalytic cracking catalyst comprising the steps of: (a) making microspheres of calcined kaolin clay, said microspheres comprising about 30-60% by weight metakaolin and about 40-70% by weight kaolin clay that has been calcined at least substantially through its characteristic exotherm and containing no or no more than about 10% by weight hydrous clay; (b) mixing the microspheres of step (a) with one or more sources of sodium silicate and water to obtain an alkaline slurry of microspheres of calcined clay in an aqueous solution containing sodium silicate, said sodium silicate being provided in an amount so that microspheres having an SiO 2 /Al 2 O 3 molar ratio of about 1.7-3.4 are obtained in step (f) below; (c) adding zeolite initiator to the microspheres before step (d) below; (d) heating the slurry of microspheres of calcined clay to a temperature and for a time sufficient to crystallize at least about 40% by weight Y-faujasite in the microspheres, said Y-faujasite being in the sodium form; (e) separating the microspheres containing at least about 40% by weight Y-faujasite from at least a major portion of its mother liquor; (f) replacing sodium cations in the microspheres separated in step (e) with ammonium or rare earth cations or both.

Claim 53

Dependent Claim 25 words

The method of claim 48 wherein the two types of calcined clay in the microspheres made in step (a) are present in the same microspheres.

Claim 54

Dependent Claim 24 words

The method of claim 48 wherein the kaolin clay that has been calcined at least substantially through its characteristic exotherm contains substantially no mullite.

Claim 55

Dependent Claim 46 words

The method of claim 50 further comprising conducting the following steps after step (e) and before step (f): (g) contacting the microspheres separated in step (e) with a solution containing sodium silicate; (h) drying the microspheres obtained in step (g) to obtain microspheres containing sodium silicate.

Claim 56

Dependent Claim 49 words

The method of claim 50 wherein a portion of the mother liquor is left entrained in the microspheres in step (e) and further comprising conducting the following step after step (e) and before step (f): (g) drying the microspheres separated in step (e) to obtain microspheres containing sodium silicate.

Claim 57

Dependent Claim 22 words

The method of claim 48 wherein the clay that has been calcined through its characteristic exotherm contains a substantial amount of mullite.

Claim 58

Dependent Claim 37 words

The method of claim 48 wherein the molar ratios of constituents present at the beginning of the crystallization process of step (d) are: ______________________________________ Na.sub.2 O/SiO.sub.2 SiO.sub.2 /Al.sub.2 O.sub.3 H.sub.2 O/Na.sub.2 O ______________________________________ 0.30-0.60 5-13 20-35 ______________________________________

Claim 59

Dependent Claim 27 words

The method of claim 54 wherein the weight ratio of water to clay microspheres at the beginning of the crystallization process of step (d) is about 4-12.

Claim 60

Dependent Claim 58 words

The method of claim 55 wherein the molar ratio of Na 2 O/SiO 2 in the solution phase at the beginning of the crystallization process of step (d) is about 0.49-0.57 and the weight ratio of SiO 2 in the solution phase to clay microspheres at the beginning of the crystallization process of step (d) is about 1.0-1.7.

Claim 61

Dependent Claim 19 words

The method of claim 48 wherein about 50-70% by weight Y-faujasite is crystallized in the microspheres in step (d).

Claim 62

Dependent Claim 12 words

The fluid catalytic cracking catalyst made by the method of claim 37.

Claim 63

Dependent Claim 12 words

The fluid catalytic cracking catalyst made by the method of claim 47.

Claim 64

Dependent Claim 12 words

The fluid catalytic cracking catalyst made by the method of claim 48.

Claim 65

Dependent Claim 12 words

The fluid catalytic cracking catalyst made by the method of claim 49.

Claim 66

Dependent Claim 12 words

The fluid catalytic cracking catalyst made by the method of claim 57.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1988-01-15	1988-07-16	1989-01-15	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1992-01-15	1992-07-16	1993-01-15	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	1996-01-15	1996-07-16	1997-01-15	$7700.00	Window Closed / Lapsed

Fluid catalytic cracking catalyst comprising microspheres containing more than about 40 percent by weight Y-faujasite and methods for making

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag