US4492733A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making an abrasion resistant coating on a solid substrate and articles produced thereby
Assignee: Foster Grant Co Inc
•
Filing: 1983-08-17
•
Granted: 1985-01-08
•
Expires: 2003-08-17
Abstract
Abstract PCT No. PCT/US83/01260 Sec. 371 Date Jan. 23, 1984 Sec. 102(e) Date Jan. 23, 1984 PCT Filed Aug. 17, 1983 PCT Pub. No. WO84/00722 PCT Pub. Date Mar. 1, 1984.There is disclosed a method for providing an improved abrasion resistant coating on solid substrates such as plastic articles and solid articles prepared thereby having on the surface such abrasion resistant coating. A solid substrate is coated with an organosilanol-type coating liquid comprising organosilanol molecules or a partial condensation product thereof. At least 90 mole percent of said organosilanol molecules are trifunctional silanol molecules of the formula RSi(OH)3, R being a hydrocarbon radical, and at least 50 mole percent of said trisilanols being an alkyl trisilanols of 1-3 carbon atoms or phenyl trisilanol. Preferably, at least 70 mole percent of the trisilanol is methyltrisilanol. After the coating is cured by a conventional means, it is post-treated by a glow discharge to afford an abrasion resistance far superior to those obtained from organosilanol coating liquids without glow discharge post-treatment. There is also disclosed a mirrored solid substrate such as a plastic sheet having an improved abrasion resistance which comprises a layer of a glow discharge treated organosiloxane coating and a mirror layer deposited thereon.
Inventors
- 👤 Richard A. Phillips
- 👤 Theodore A. Haddad
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 23:41
CPC Classifications
C; C08; C08J; C08J7/00; C08J7/12; C08J7/123; B; B05; B05D; B05D3/00; B05D3/14; B05D3/141; B05D3/145; B05D3/148; C09; C09D; C09D183/00; C09D183/04; C08J2383/00; C08J2383/04; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31507; Y10T428/31652; Y10T428/31663; Y10T428/31725; Y10T428/31786; Y10T428/31855; Y10T428/31935
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
122 words
A method of improving the abrasion resistance of cross-linked organosiloxane coating, said coating having been prepared by applying to a solid substrate an organosiloxane coating liquid comprising as a main ingredient organosilanol molecules, at least 90 mole percent of which being trifunctional silanols of the formula RSi(OH) 3 where R is a hydrocarbon radical, and at least 50 mole percent of said trifunctional silanols being an alkyltrisilanol of 1-3 carbons or phenyltrisilanol, or a precursor thereof or a partial hydrolysis product thereof and by curing the resultant coating in order to obtain an abrasion resistant, cross-linked organosiloxane coating, which method comprises a glow discharge treatment of said cross-linked organosiloxane coating under a pressure range of from about 5 to about 150 microns.
Claim 2
Independent Claim
122 words
A method of improving the abrasion resistance of cross-linked organosiloxane coating, said coating having been prepared by applying to a solid substrate an organosiloxane coating liquid comprising as a main ingredient organosilanol molecules, at least 90 mole percent of which being trifunctional silanols of the formula RSi(OH) 3 where R is a hydrocarbon radical, and at least 50 mole percent of said trifunctional silanols being an alkyltrisilanol of 1-3 carbons or phenyltrisilanol, or a precursor thereof or a partial hydrolysis product thereof and by curing the resultant coating in order to obtain an abrasion resistant, cross-linked organosiloxane coating, which method comprises a glow discharge treatment of said cross-linked organosiloxane coating under a pressure range of from about 5 to about 150 microns.
Claim 3
Dependent Claim
23 words
The method as defined in claim 1 wherein the glow discharge treatment is conducted under a pressure within the range of 5-50 microns.
Claim 4
Dependent Claim
19 words
The method as defined in claim 1 wherein at least 50 mole percent of the trifunctional silanols is methyltrisilanol.
Claim 5
Dependent Claim
19 words
The method as defined in claim 3 wherein at least 70 mole percent of the trifunctional silanols is methyltrisilanol.
Claim 6
Dependent Claim
15 words
The method as defined in claim 1, wherein the solid substrate is a plastic material.
Claim 7
Dependent Claim
36 words
The method as defined in claim 5, wherein the plastic material is selected from the group consisting of acrylic resin, polycarbonate resin, allyl diglycol carbonate resin, polyester resin, polyamide resin, polystyrene resin and cellulose ester resin.
Claim 8
Dependent Claim
83 words
A solid substrate coated with an abrasion-resistant cross-linked organosilane coating comprising the cross-linked condensation product of organosilanol molecules at least 90 mole percent of which being trifunctional silanols of the formula RSi(OH) 3 where R is a hydrocarbon radical, and at least 50 mole percent of said trifunctional silanols being an alkyltrisilanol of 1-3 carbons or phenyltrisilanol, a precursor thereof or a partial hydrolysis product thereof that has been glow discharge treated at a pressure of 5-150 microns subsequent to condensation and crosslinking.
Claim 9
Dependent Claim
83 words
A solid substrate coated with an abrasion-resistant cross-linked organosilane coating comprising the cross-linked condensation product of organosilanol molecules at least 90 mole percent of which being trifunctional silanols of the formula RSi(OH) 3 where R is a hydrocarbon radical, and at least 50 mole percent of said trifunctional silanols being an alkyltrisilanol of 1-3 carbons or phenyltrisilanol, a precursor thereof or a partial hydrolysis product thereof that has been glow discharge treated at a pressure of 5-150 microns subsequent to condensation and crosslinking.
Claim 10
Dependent Claim
24 words
The solid substrate as defined in claim 7 wherein the glow discharge treatment is conducted under a pressure within the range of 5-50 microns.
Claim 11
Dependent Claim
20 words
The solid substrate as defined in claim 7 wherein at least 50 mole percent of the trifunctional silanols is methyltrisilanol.
Claim 12
Dependent Claim
20 words
The solid substrate as defined in claim 9 wherein at least 70 mole percent of the trifunctional silanols is methyltrisilanol.
Claim 13
Dependent Claim
16 words
The solid substrate as defined in claim 7 wherein the solid substrate is a plastic material.
Claim 14
Dependent Claim
37 words
The solid substrate as defined in claim 11 wherein the plastic material is selected from the group consisting of acrylic resin, polycarbonate resin, allyl diglycol carbonate resin, polyester resin, polyamide resin, polystyrene resin and cellulose ester resin.
Claim 15
Dependent Claim
98 words
A solid substrate having (a) an abrasion-resistant cross-linked organosiloxane coating comprising the cross-linked condensation product of organosilanol molecules at least 90 mole percent of which being trifunctional silanols of the formula RSi(OH) 3 where R is a hydrocarbon radical, and at least 50 mole percent of said trifunctional silanols being an alkyltrisilanol of 1-3 carbons or phenyltrisilanol, a precursor thereof or a partial hydrolysis product thereof that has been glow discharge treated at a pressure of 5-150 microns subsequent to condensation and crosslinking and (b) a metallic layer deposited by a vapor deposition method on said organosiloxane coating.
Claim 16
Dependent Claim
98 words
A solid substrate having (a) an abrasion-resistant cross-linked organosiloxane coating comprising the cross-linked condensation product of organosilanol molecules at least 90 mole percent of which being trifunctional silanols of the formula RSi(OH) 3 where R is a hydrocarbon radical, and at least 50 mole percent of said trifunctional silanols being an alkyltrisilanol of 1-3 carbons or phenyltrisilanol, a precursor thereof or a partial hydrolysis product thereof that has been glow discharge treated at a pressure of 5-150 microns subsequent to condensation and crosslinking and (b) a metallic layer deposited by a vapor deposition method on said organosiloxane coating.
Claim 17
Dependent Claim
16 words
The solid substrate as defined in claim 13, wherein the solid substrate is a plastic material.
Claim 18
Dependent Claim
37 words
The solid substrate as defined in claim 14, wherein the plastic material is selected from the group consisting of acrylic resin, polycarbonate resin, allyl diglycol carbonate resin, polyester resin, polyamide resin, polystyrene resin and cellulose ester resin.
Claim 19
Dependent Claim
62 words
A solid substrate coated with an abrasion-resistant organosiloxane coating as defined in claim 7 having siloxane cross-linkages, which solid substrate having an abrasion resistance such that the number of cycles of abrasive motion required to increase the haze value of the solid substrate by 3% is at least 500 as determined by the rubbing pad abrader test method under 100 gram load.
Claim 20
Dependent Claim
16 words
The solid substrate as defined by claim 16 wherein the solid substrate is a plastic material.
Claim 21
Dependent Claim
37 words
The solid substrate as defined by claim 17 wherein the plastic material is selected from the group consisting of acrylic resin, polycarbonate resin, allyl diglycol carbonate resin, polyester resin, polyamide resin, polystyrene resin and cellulose ester resin.
References Cited (Backward Citations)
US2778793A
Cited
US3451838A
Cited
US3632386A
Cited
US3669720A
Cited
US3713880A
Cited
US3650808A
Cited
US3686018A
Cited
GB1362939A
Cited
US3843399A
Cited
US3953115A
Cited
US3901994A
Cited
US3986997A
Cited
US4018945A
Cited
US4137365A
Cited
US4225631A
Cited
US4096315A
Cited
US4072985A
Cited
US4123308A
Cited
JPS551839A
Cited
US4277287A
Cited
US4298655A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-01-08 | 1988-07-09 | 1989-01-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-01-08 | 1992-07-09 | 1993-01-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-01-08 | 1996-07-09 | 1997-01-08 | $7700.00 | Window Closed / Lapsed |