Method for providing an abrasion resistant coating for plastic ophthalmic lenses and the resulting lenses
Assignee: BMC Industries Inc
•
Filing: 1973-07-05
•
Granted: 1976-04-27
•
Expires: 1993-07-05
Abstract
Abstract A process is disclosed for applying an adherent, optically clear, abrasion resistant coating to plastic ophthalmic substrates such as plastic lenses. The process includes: (a) forming a partially hydrolyzed solution of a vinyltri(lower alkoxy)silane, such as vinyltriethoxysilane, in a water-miscible, volatile, organic solvent, the silane being present from 25-75% by weight; (b) applying a thin, uniform coating of the partially hydrolyzed solution to a clean surface of the ophthalmic lens; (c) maintaining the coated substrate in a high humidity and preferably elevated temperature environment until the silane is substantially completely hydrolyzed; and, (d) dehydrating the coated substrate under low humidity conditions at an elevated temperature below the temperature at which the substrate degrades until an adherent, abrasion resistant coating is formed. Plastic lenses and other ophthalmic plastic components coated according to the above process are also described.
Inventors
- 👤 Hollis E. French
- 👤 Jurgen M. Kruse
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 08:01
CPC Classifications
B; B29; B29D; B29D11/00; B29D11/00865; B29D11/00009; G; G02; G02B; G02B1/00; G02B1/04; G02B1/041; G02B1/105; G02B1/10; G02B1/14; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31507; Y10T428/31652; Y10T428/31663
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
121 words
A process for forming an abrasion resistant, adherent coating on a polymeric optical component, comprising: a. forming a solution consisting essentially of a partially hydrolyzed vinyltri(lower alkoxy)silane in a water-miscible, volatile, organic solvent wherein said partially hydrolyzed vinyltri(lower alkoxy)silane is present from about 25 to about 75% by weight; b. applying a thin, uniform coating of said solution to a clean surface of the optical component; c. maintaining said coated component in an environment having a relative humidity greater than or equal to 70% and at a temperature of from about 25°C. to about 80°C.; and, d. dehydrating said coated component at an elevated temperature below the temperature at which the component degrades until an adherent, abrasion resistant coating is formed.
Claim 2
Dependent Claim
121 words
A process for forming an abrasion resistant, adherent coating on a polymeric optical component, comprising: a. forming a solution consisting essentially of a partially hydrolyzed vinyltri(lower alkoxy)silane in a water-miscible, volatile, organic solvent wherein said partially hydrolyzed vinyltri(lower alkoxy)silane is present from about 25 to about 75% by weight; b. applying a thin, uniform coating of said solution to a clean surface of the optical component; c. maintaining said coated component in an environment having a relative humidity greater than or equal to 70% and at a temperature of from about 25°C. to about 80°C.; and, d. dehydrating said coated component at an elevated temperature below the temperature at which the component degrades until an adherent, abrasion resistant coating is formed.
Claim 3
Dependent Claim
24 words
A process of claim 1 wherein said optical component is formed from a polymeric material containing a major amount of diethylene glycol bis(allyl carbonate).
Claim 4
Dependent Claim
25 words
A process of claim 1 wherein said optical component comprises a polymeric, ophthalmic lens formed from a polymer consisting essentially of diethylene glycol bis(allyl carbonate).
Claim 5
Dependent Claim
12 words
A process of claim 3 wherein said silane consists essentially of vinyltriethoxysilane.
Claim 6
Dependent Claim
50 words
A process of claim 4 wherein said coated lens is maintained at a temperature of from about 30°C. to about 50°C. and a relative humidity above about 70% for a period of about 24 to about 30 minutes thereby allowing further hydrolysis of Si--O--R bonds where R is lower alkyl.
Claim 7
Dependent Claim
31 words
A process of claim 5 wherein said coated lens is dehydrated in an atmosphere having a relative humidity below about 10% and at a temperature between about 80°C. and about 100°C.
Claim 8
Dependent Claim
18 words
A process of claim 6 wherein said solution is formed using a solvent chosen from ethanol and isopropanol.
Claim 9
Dependent Claim
22 words
A process of claim 7 wherein said wet coating is applied to said lens from about 3 to about 6 microns thick.
Claim 10
Dependent Claim
19 words
A process of claim 8 wherein said lens surface is cleaned using an oxygen containing plasma prior to coating.
Claim 11
Dependent Claim
33 words
A process of claim 9 wherein said solution of a vinyltri(lower alkoxy)silane is partially hydrolyzed to a degree sufficient to provide said solution with a visocsity of about 25 centipoises at room temperature.
Claim 12
Dependent Claim
19 words
A process of claim 10 wherein said vinyltriethoxysilane is present in said solution in an amount of about 50%.
Claim 13
Dependent Claim
12 words
A coated ophthalmic component prepared according to the process of claim 1.
Claim 14
Dependent Claim
12 words
A coated ophthalmic component prepared according to the process of claim 4.
Claim 15
Dependent Claim
12 words
A coated ophthalmic component prepared according to the process of claim 11.
Claim 16
Dependent Claim
27 words
A process of claim 1 wherein said partially hydrolyzed solution of a vinyltri(lower alkoxy)silane contains from about 1 to about 20 weight percent of a curing catalyst.
Claim 17
Dependent Claim
20 words
A process of claim 15 wherein said curing catalyst comprises a C 1 -C 8 alkyltri(C 1 -C 3 alkoxy)silane.
Claim 18
Dependent Claim
10 words
A process of claim 16 wherein said catalyst comprises aminopropyltriethoxysilane.
Claim 19
Dependent Claim
11 words
A process of claim 16 wherein said catalyst comprises N(beta-amino ethyl)-gammaaminopropyltrimethoxysilane.
Claim 20
Dependent Claim
173 words
A process for forming a thin, abrasion resistant, adherent, optically clear coating on a polymerized diethylene glycol bis(allyl carbonate) ophthalmic lens, comprising: a. forming a solution consisting essentially of vinyltriethoxysilane in a water-miscible, volatile, organic solvent, said vinyl triethoxysilane being present in an amount of about 50% by weight; b. partially hydrolyzing said solution by contacting it with from about 7 to about 30 parts by weight of 0.1N hydrochloric acid per 100 parts of solution; c. applying a coating of from about 3 to about 6 microns of said partially hydrolyzed solution to a clean surface of said lens; d. maintaining said coated lens for at least about 24 minutes at a temperature between about 30°C. and 50°C. and a relative humidity above 90%; and, e. dehydrating said coated lens at a temperature of from about 80°C. to about 100°C. and a relative humidity below about 10% to form an abrasion resistant, adherent, optically clear coating thereon, said dry coating having a thickness of from about 1.5 microns to about 3 microns.
Claim 21
Dependent Claim
173 words
A process for forming a thin, abrasion resistant, adherent, optically clear coating on a polymerized diethylene glycol bis(allyl carbonate) ophthalmic lens, comprising: a. forming a solution consisting essentially of vinyltriethoxysilane in a water-miscible, volatile, organic solvent, said vinyl triethoxysilane being present in an amount of about 50% by weight; b. partially hydrolyzing said solution by contacting it with from about 7 to about 30 parts by weight of 0.1N hydrochloric acid per 100 parts of solution; c. applying a coating of from about 3 to about 6 microns of said partially hydrolyzed solution to a clean surface of said lens; d. maintaining said coated lens for at least about 24 minutes at a temperature between about 30°C. and 50°C. and a relative humidity above 90%; and, e. dehydrating said coated lens at a temperature of from about 80°C. to about 100°C. and a relative humidity below about 10% to form an abrasion resistant, adherent, optically clear coating thereon, said dry coating having a thickness of from about 1.5 microns to about 3 microns.
Claim 22
Dependent Claim
27 words
A process of claim 19 wherein said partially hydrolyzed solution of a vinyltri(lower alkoxy)silane contains from about 1 to about 20 weight percent of a curing catalyst.
Claim 23
Dependent Claim
20 words
A process of claim 20 wherein said curing catalyst comprises a C 1 -C 8 alkyltri(C 1 -C 3 alkoxy)silane.
Claim 24
Dependent Claim
10 words
A process of claim 21 wherein said catalyst comprises aminopropyltriethoxysilane.
Claim 25
Dependent Claim
11 words
A process of claim 21 wherein said catalyst comprises N(beta-amino ethyl)-gammaaminopropyltrimethoxysilane.
Claim 26
Dependent Claim
113 words
A process for coating a polymeric substrate, comprising: a. forming a solution consisting essentially of a partially hydrolyzed vinyltri(lower alkoxy)silane in a water-miscible, volatile, organic solvent wherein said partially hydrolyzed vinyltri(lower alkoxy)silane is present from about 25 to about 75% by weight; b. applying a thin, uniform coating of said solution to a clean surface of the substrate; c. maintaining said coated substrate in an environment having a relative humidity greater than or equal to 70% and at a temperature of from about 25°C. to about 80°C.; and, d. dehydrating said coated substrate at an elevated temperature below the temperature at which the substrate degrades until an adherent, abrasion resistant coating is formed.
Claim 27
Dependent Claim
113 words
A process for coating a polymeric substrate, comprising: a. forming a solution consisting essentially of a partially hydrolyzed vinyltri(lower alkoxy)silane in a water-miscible, volatile, organic solvent wherein said partially hydrolyzed vinyltri(lower alkoxy)silane is present from about 25 to about 75% by weight; b. applying a thin, uniform coating of said solution to a clean surface of the substrate; c. maintaining said coated substrate in an environment having a relative humidity greater than or equal to 70% and at a temperature of from about 25°C. to about 80°C.; and, d. dehydrating said coated substrate at an elevated temperature below the temperature at which the substrate degrades until an adherent, abrasion resistant coating is formed.
Claim 28
Dependent Claim
12 words
A process of claim 24 wherein said silane consists essentially of vinyltriethoxysilane.
References Cited (Backward Citations)
CA688702A
Cited
US3258382A
Cited
US3278476A
Cited
US3389114A
Cited
US3427273A
Cited
US3367910A
Cited
US3451838A
Cited
US3458342A
Cited
US3713880A
Cited
US3637416A
Cited
US3650808A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-04-27 | 1979-10-27 | 1980-04-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-04-27 | 1983-10-27 | 1984-04-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-04-27 | 1987-10-27 | 1988-04-27 | $7700.00 | Window Closed / Lapsed |