Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for producing a well-adhered durable optical coating on an optical plastic substrate
Assignee: National Aeronautics and Space Administration
•
Filing: 1976-12-15
•
Granted: 1978-06-20
•
Expires: 1996-12-15
Abstract
Abstract A process for coating an optical plastic substrate, for example polymethylmethacrylate (PPMA), with a single layer coating for the purpose of improving the durability of the plastic, the coating being deposited by a low temperature plasma polymerization process.
Inventors
- 👤 Ronald M. Kubacki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 12:30
CPC Classifications
B; B29; B29D; B29D11/00; B29D11/00865; G02B1/105; G; G02; G02B; G02B1/00; G02B1/10; G02B1/14; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31507; Y10T428/31652; Y10T428/31663
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
135 words
A method of coating an optical plastic substrate with an abrasion resistant coating comprising the sequential steps of: a. exposing the substrate in an evacuated plasma polymerization reactor chamber to a first plasma that forms hydroxyl groups on said substrate surface, b. evacuating the reactor chamber, c. exposing the substrate in the reactor chamber to a second plasma, said second plasma being a polymerizable monomer to produce a coating of the monomer on the substrate, the coating being less than 3000 nm thick and wherein the monomer contains silicon, d. evacuating the reaction chamber, e. exposing the substrate to a third plasma for a predetermined time at a predetermined pressure, said third plasma being selected from the group consisting of noble gases, oxygen, nitrogen, and air, and f. removing the substrate from the reactor chamber.
Claim 2
Independent Claim
135 words
A method of coating an optical plastic substrate with an abrasion resistant coating comprising the sequential steps of: a. exposing the substrate in an evacuated plasma polymerization reactor chamber to a first plasma that forms hydroxyl groups on said substrate surface, b. evacuating the reactor chamber, c. exposing the substrate in the reactor chamber to a second plasma, said second plasma being a polymerizable monomer to produce a coating of the monomer on the substrate, the coating being less than 3000 nm thick and wherein the monomer contains silicon, d. evacuating the reaction chamber, e. exposing the substrate to a third plasma for a predetermined time at a predetermined pressure, said third plasma being selected from the group consisting of noble gases, oxygen, nitrogen, and air, and f. removing the substrate from the reactor chamber.
Claim 3
Dependent Claim
30 words
The method of coating an optical plastic substrate as recited in claim 1 wherein said first plasma is selected from the group consisting of oxygen, hydrogen, air and water vapor.
Claim 4
Dependent Claim
40 words
The method of coating an optical plastic substrate as recited in claim 1 wherein said third plasma is employed to cross-link and stress-relieve the silicon monomer and is selected from the group consisting of a noble gas, oxygen and nitrogen.
Claim 5
Dependent Claim
26 words
The method of coating an optical plastic substrate as recited in claim 1 wherein said first plasma is water vapor and said third plasma is argon.
Claim 6
Dependent Claim
30 words
A method of coating an optical plastic substrate as recited in claim 1 wherein said monomer is selected from the group consisting of vinyltrimethylsilane, vinyltrimethylethoxysilane, vinyldimethylethoxysilane, hexamethyldisilizane, and mixtures thereof.
Claim 7
Dependent Claim
38 words
The method of coating an optical plastic substrate as recited in claim 1 wherein exposure of the substrate to the first plasma is undertaken at a pressure of about 15 to 25 nt/m 2 within the reactor chamber.
Claim 8
Dependent Claim
77 words
The method of coating an optical plastic substrate as recited in claim 5 wherein the step of producing the monomer coating is undertaken at a flow rate of 1 to 5 cc/min. at standard temperature and pressure, with an interior pressure within the reactor chamber in the range of 6.67 to 13.33 nt/m 2 and at an RF power of 20 to 60 watts RMS with an RMS current in the range of 1.24 to 2.07 amps.
Claim 9
Dependent Claim
37 words
The coating of an optical plastic substrate as recited in claim 7 wherein the step of producing the monomer coating on the substrate is undertaken at a deposition rate in the range of 0.1 to 0.25 nm/sec.
Claim 10
Dependent Claim
44 words
A method of coating an optical plastic substrate as recited in claim 5 wherein the step of exposing the substrate to the third plasma is undertaken at a pressure of 20 nt/m 2 at 100 watts of RF power for 200 to 1,000 seconds.
Claim 11
Dependent Claim
19 words
A method of coating an optical plastic substrate as recited in claim 9 wherein the third plasma is argon.
Claim 12
Dependent Claim
29 words
A method of coating an optical plastic substrate as recited in claim 5 wherein the monomer is a mixture of approximately 50% hexamethyldisilizane and 50% vinyl dimethylethoxysilane by volume.
Claim 13
Dependent Claim
28 words
The method of coating an optical plastic substrate as recited in claim 5 wherein the monomer is a mixture of approximately 50% vinyltrimethylsilane and 50% hexamethyldisilizane by volume.
Claim 14
Dependent Claim
26 words
The method of coating an optical plastic substrate as recited in claim 5 wherein the monomer is a mixture of approximately 50% vinyltrimethylethoxysilane and 50% hexamethyldisilizane.
Claim 15
Dependent Claim
82 words
The method of coating an optical plastic substrate as recited in claim 1 further comprising the step of cleaning the substrate prior to the step of exposing the substrate in the reactor chamber to the first plasma by dipping the substrate in a first solvent to remove water soluble contaminants and then rinsing the substrate in a second solvent to remove the first solvent and finally vapor degreasing the substrate and allowing the substrate to dry before insertion into the plasma reactor.
Claim 16
Dependent Claim
18 words
The method of coating an optical plastic substrate as recited in claim 1 wherein said substrate is polymethylmethacrylate.
Claim 17
Dependent Claim
19 words
The method of coating an optical plastic substrate as recited in claim 1 wherein said substrate is a polycarbonate.
Claim 18
Dependent Claim
19 words
The method of coating an optical plastic substrate as recited in claim 1 wherein said substrate is a polystyrene.
Claim 19
Dependent Claim
20 words
The method of coating an optical plastic substrate as recited in claim 1 wherein said substrate is a polystyrenepolymethylmethacrylate copolymer.
Claim 20
Dependent Claim
67 words
A method of coating an optical plastic substrate as recited in claim 1 wherein the optical plastic substrate has a higher refractive index than the refractive index of the monomer coating and the monomer cOating is deposited to have an optical thickness equal to an odd multiple of 1/4 of the wavelength of the midpoint of the light range over which the substrate is to be utilized.
Claim 21
Dependent Claim
13 words
A coated optical plastic substrate produced according to the method of claim 1.
Claim 22
Dependent Claim
72 words
An optical plastic substrate having an abrasion resistant coating comprising: a. an optical plastic substrate selected from the group consisting of polymethylmethacrylate, a polycarbonate, a polystyrene, and a polystyrene-polymethylmethacrylate copolymer, b. an interlayer hydroxyl group coating on at least one surface of the substrate, and c. an outer, plasma polymerized monomer coating over the hydroxyl interlayer, the monomer being selected from the group consisting of vinyltrimethylsilane, vinyltrimethylethoxysilane, vinyldimethylethoxysilane, hexamethyldisilizane and mixtures thereof.
Claim 23
Dependent Claim
72 words
An optical plastic substrate having an abrasion resistant coating comprising: a. an optical plastic substrate selected from the group consisting of polymethylmethacrylate, a polycarbonate, a polystyrene, and a polystyrene-polymethylmethacrylate copolymer, b. an interlayer hydroxyl group coating on at least one surface of the substrate, and c. an outer, plasma polymerized monomer coating over the hydroxyl interlayer, the monomer being selected from the group consisting of vinyltrimethylsilane, vinyltrimethylethoxysilane, vinyldimethylethoxysilane, hexamethyldisilizane and mixtures thereof.
Claim 24
Dependent Claim
64 words
A coated optical plastic substrate as recited in claim 21 wherein the combined interlayer and monomer coating is chosen to have a lower refractive index than the refractive index of the optical plastic substrate and has an optical thickness equal to an odd multiple of 1/4 of the wavelength of the midpoint of the light range over which the substrate is to be utilized.
References Cited (Backward Citations)
US2428357A
Cited
US3111424A
Cited
US3477902A
Cited
US3450465A
Cited
US3829324A
Cited
US3746567A
Cited
US3707397A
Cited
US3822928A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-19 | 1981-12-19 | 1982-06-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-19 | 1985-12-19 | 1986-06-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-19 | 1989-12-19 | 1990-06-20 | $7700.00 | Window Closed / Lapsed |