High wet strength waferboard
Assignee: MacMillan Bloedel Ltd
•
Filing: 1983-06-16
•
Granted: 1985-01-08
•
Expires: 2003-06-16
Abstract
Abstract A high wet strength waferboard panel is disclosed made from aspen species of wood flakes or equivalent with average specific gravity less than 0.6 and having wet strength equivalent to plywood. At least a portion of the wood wafers are oriented generally in a lengthwise direction such that the length to width strength ratio of the panel, measured as modulus of rupture, is in the range of about 1.3:1 to 2:1, the density of the waferboard panel being in the range of about 38 to 45 lb/ft 3 , the content of adhesive resin in the panel being in the range of about 4% to 10%, the content of wax in the panel being in the range of about 1% to 21/2% and the thickness of the panel being in the range of about 3/8 to 11/2 inches. The fully soaked panel having a moisture content of at least about 30% with an MOR lengthwise greater than about 2900 lb/in 2 and an MOE lengthwise greater than about 0.9×10 6 lb/in 2 .
Inventors
- 👤 George N. Rosenberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 09:04
CPC Classifications
B; B32; B32B; B32B21/00; B32B21/02; B32B21/04; B32B21/042; B32B21/06; C; C08; C08L; C08L97/00; C08L97/02; E; E04; E04C; E04C2/00; E04C2/02; E04C2/10; E04C2/16; B32B2260/00; B32B2260/02; B32B2260/028; B32B2260/04; B32B2260/046; B32B2307/00; B32B2307/50; B32B2307/514; B32B2307/70; B32B2307/72; B32B2309/00; B32B2309/08; B32B2309/10; B32B2309/105; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24777; Y10T428/24793; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/25; Y10T428/253; Y10T428/28; Y10T428/2839; Y10T428/31504; Y10T428/31942; Y10T428/31949; Y10T428/31964; Y10T428/31967; Y10T428/31971; Y10T428/31975; Y10T428/31978; Y10T428/31982; Y10T428/4935; Y10T428/662
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
182 words
A waferboard panel comprising wood wafers having an initial average specific gravity, based on oven dry weight with volume at 12% moisture content, of less than about 0.6, said wood wafers having a length of at least about 1.5 inches and a width in the range of about 0.125 to 1.5 inches, adhesive resin in the range of about 4% to 10% by weight of the wood wafers, at least a portion of the wood wafers being oriented generally in a lengthwise direction, such that the length to width strength ratio of the waferboard panel, measured as modulus of rupture, is in the range of about 1.3:1 to 2:1, the waferboard panel having a density in the range of about 38 to 45 lb/ft 3 , the fully soaked waferboard panel having a moisture content of at least about 30%, with an MOR lengthwise greater than about 2900 lb/in 2 and an MOE lengthwise greater than about 0.9×10 6 lb/in 2 , and the waferboard panel having a weight gain of not more than about 14% after a ten week exterior exposure.
Claim 2
Dependent Claim
182 words
A waferboard panel comprising wood wafers having an initial average specific gravity, based on oven dry weight with volume at 12% moisture content, of less than about 0.6, said wood wafers having a length of at least about 1.5 inches and a width in the range of about 0.125 to 1.5 inches, adhesive resin in the range of about 4% to 10% by weight of the wood wafers, at least a portion of the wood wafers being oriented generally in a lengthwise direction, such that the length to width strength ratio of the waferboard panel, measured as modulus of rupture, is in the range of about 1.3:1 to 2:1, the waferboard panel having a density in the range of about 38 to 45 lb/ft 3 , the fully soaked waferboard panel having a moisture content of at least about 30%, with an MOR lengthwise greater than about 2900 lb/in 2 and an MOE lengthwise greater than about 0.9×10 6 lb/in 2 , and the waferboard panel having a weight gain of not more than about 14% after a ten week exterior exposure.
Claim 3
Dependent Claim
87 words
The waferboard panel according to claim 1 having a thickness in the range of about 5/8 to 1 inch, the waferboard panel after a seven day water soak having a load carrying capacity lengthwise of at least about 4800 lb in/ft, stiffness lengthwise being at least about 500,000 lb in 2 /ft, shear modulus being at least about 9500 lb/in 2 and mean maximum deflection of not more than about 0.27 inches at a uniformly distributed load of 720 lb/ft 2 over a 24 inch support spacing.
Claim 4
Dependent Claim
16 words
The waferboard panel according to claim 2 having a thickness of about 13/16 of an inch.
Claim 5
Dependent Claim
44 words
The waferboard panel according to claim 2 wherein the surface layers are formed on both surfaces of the panel having wood wafers oriented generally in a lengthwise direction and at least one core layer between the surface layers has wood wafers randomly oriented therein.
Claim 6
Dependent Claim
25 words
The waferboard panel according to claim 4 wherein the surface layers are each in the range of about 14% to 33% of the panel thickness.
Claim 7
Dependent Claim
38 words
The waferboard panel according to claim 2 wherein edge sealing is applied to all edges of the panel and the waferboard panel has a weight gain of not more than about 8% after a ten week exterior exposure.
Claim 8
Dependent Claim
22 words
The waferboard panel according to claim 2 including a phenolic impregnated paper overlay applied to at least one surface of the panel.
Claim 9
Dependent Claim
17 words
The waferboard panel according to claim 7 wherein the paper overlay is coated with a release agent.
Claim 10
Dependent Claim
29 words
The waferboard panel according to claim 2 wherein the wood wafers are about 3 inches long and the density of the waferboard panel is about 41 lb/ft 3 .
Claim 11
Dependent Claim
28 words
The waferboard panel according to claim 2 wherein the wood wafers are about 1-1/2 long and the density of the waferboard panel is about 45 lb/ft 3 .
Claim 12
Dependent Claim
27 words
The waferboard panel according to claim 4 wherein the surface layer at each surface of the panel is about 20% of the total thickness of the panel.
Claim 13
Dependent Claim
127 words
A waferboard panel comprising wood wafers predominantly of aspen species hardwoods, said wood wafers having a length of at least about 1.5 inches and a width in the range of about 0.125 to 1.5 inches, at least a portion of the wood wafers being oriented generally in a lengthwise direction such that length to width strength ratio of the waferboard panel, measured as modulus of rupture, is in the range of about 1.3:1 to 2:1, the density of the waferboard panel being in the range of about 38 to 45 lbs/ft 3 , the content of adhesive resin in the waferboard panel being in the range of about 4% to 10%, and the thickness of the panel being in the range of about 1/2 to 1-1/2 inches.
Claim 14
Dependent Claim
127 words
A waferboard panel comprising wood wafers predominantly of aspen species hardwoods, said wood wafers having a length of at least about 1.5 inches and a width in the range of about 0.125 to 1.5 inches, at least a portion of the wood wafers being oriented generally in a lengthwise direction such that length to width strength ratio of the waferboard panel, measured as modulus of rupture, is in the range of about 1.3:1 to 2:1, the density of the waferboard panel being in the range of about 38 to 45 lbs/ft 3 , the content of adhesive resin in the waferboard panel being in the range of about 4% to 10%, and the thickness of the panel being in the range of about 1/2 to 1-1/2 inches.
Claim 15
Dependent Claim
106 words
The waferboard panel according to claim 12 having a thickness of about 13/16 of an inch, the waferboard panel after a seven day water soak having a load carrying capacity lengthwise of at least about 4800 lb in/ft 3 , stiffness lengthwise being at least about 500,000 lb in 2 /ft, shear modulus being at least about 9500 lb/in 2 , mean maximum deflection of not more than about 0.27 inches at a uniformly distributed load of 720 lb/ft 2 over a 24 inch support spacing and the waferboard panel having a weight gain of not more than about 14% after a ten week exterior exposure.
Claim 16
Dependent Claim
25 words
The waferboard panel according to claim 1 wherein wax in the range of about 1% to 2-1/2% by weight of the wood wafers is added.
Claim 17
Dependent Claim
23 words
The waferboard panel according to claim 1 wherein said wood wafers have a length in the range of about 1.5 to 3 inches.
Claim 18
Dependent Claim
23 words
The waferboard panel according to claim 12 wherein said wood wafers have a length in the range of about 1.5 to 3 inches.
References Cited (Backward Citations)
CA565840A
Cited
CA597584A
Cited
CA711688A
Cited
US2786005A
Cited
US2773790A
Cited
US3164511A
Cited
US4053339A
Cited
US4061823A
Cited
US4158713A
Cited
US4241133A
Cited
US4246310A
Cited
US4364984A
Cited
US4361612A
Cited
US4404252A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-01-08 | 1988-07-09 | 1989-01-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-01-08 | 1992-07-09 | 1993-01-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-01-08 | 1996-07-09 | 1997-01-08 | $7700.00 | Window Closed / Lapsed |