US4484978A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Etching method
Assignee: National Semiconductor Corp
•
Filing: 1983-09-23
•
Granted: 1984-11-27
•
Expires: 2003-09-23
Abstract
Abstract The disclosure relates to techniques for etching layered materials to produce features with beveled edges, for example, wells in silicon oxide layers employed in integrated circuit fabrication. An anisotropic etch may be employed to form wells with vertical walls in the silicon oxide layer, and an isotropic etch may be employed to bevel peripheral corners of the walls. In preferred embodiments, a double mask of a photoresist layer on an underlying thin film may be used to define the limits of the anisotropic and isotropic etches, respectively.
Inventors
- 👤 Thomas Keyser
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 13:49
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/004; G03F7/09; G03F7/094; H; H10; H10P; H10P50/00; H10P50/73; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/081; H10W20/082; Y; Y10; Y10S; Y10S148/00; Y10S148/106
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
202 words
A method for forming a feature in a layer of silicon oxide overlying a substrate, wherein the feature is defined, at least in part, by a wall of the silicon oxide layer extending substantially perpendicularly from a horizontal principal plane of the substrate to a beveled edge joining the wall to a principal surface of the silicon oxide layer, comprising the steps of: providing a substrate with a layer of silicon oxide thereon; forming an etching mask for the layer of silicon oxide including a first mask layer and a second mask layer overlying the first layer, wherein an opening is formed in the second mask layer for defining the feature in the silicon oxide layer, said opening having a peripheral edge, and wherein said first mask layer is etched to undercut the second mask layer in a region adjacent to the peripheral edge of the opening; anisotropically etching silicon oxide exposed in the opening to form a generally vertical wall in the silicon oxide at the edge of the opening in the second mask layer; and isotropically, chemically etching the silicon oxide to bevel the edge in the undercut region; whereby, the beveled edge is formed in the silicon oxide layer.
Claim 2
Independent Claim
202 words
A method for forming a feature in a layer of silicon oxide overlying a substrate, wherein the feature is defined, at least in part, by a wall of the silicon oxide layer extending substantially perpendicularly from a horizontal principal plane of the substrate to a beveled edge joining the wall to a principal surface of the silicon oxide layer, comprising the steps of: providing a substrate with a layer of silicon oxide thereon; forming an etching mask for the layer of silicon oxide including a first mask layer and a second mask layer overlying the first layer, wherein an opening is formed in the second mask layer for defining the feature in the silicon oxide layer, said opening having a peripheral edge, and wherein said first mask layer is etched to undercut the second mask layer in a region adjacent to the peripheral edge of the opening; anisotropically etching silicon oxide exposed in the opening to form a generally vertical wall in the silicon oxide at the edge of the opening in the second mask layer; and isotropically, chemically etching the silicon oxide to bevel the edge in the undercut region; whereby, the beveled edge is formed in the silicon oxide layer.
Claim 3
Dependent Claim
16 words
The method of claim 1 wherein the anisotropic etching is performed with a fluorine deficient plasma.
Claim 4
Dependent Claim
56 words
The method of claim 1 wherein the second mask layer is a photoresist layer and the first mask layer is a film separately deposited on the silicon oxide layer and wherein said film is selectively etched by an etchant which more rapidly attacks the film than the silicon oxide or photoresist, to form said undercut region.
Claim 5
Dependent Claim
27 words
The method of claim 3 wherein the film is of a material selected from the group consisting of metal film, silicon nitride film, silicon and polymer film.
Claim 6
Dependent Claim
19 words
The method of claim 3 wherein the film is an aluminum film between 100 and 2,000 Angstroms in thickness.
Claim 7
Dependent Claim
36 words
The method of claim 1 wherein the first mask layer is formed by ion damaging a surface layer of the silicon dioxide layer and selectively etching the ion damaged layer to undercut the second mask layer.
Claim 8
Dependent Claim
17 words
The method of claim 6 wherein the ion damaged layer is from 100 to 2,000 Angstroms thick.
Claim 9
Independent Claim
153 words
A method of etching a well in first layer of material overlying a horizontal surface of a substrate comprising the steps of: depositing a film of etchable material on an exposed surface of the first layer of material overlying the substrate; forming a mask layer on said film layer with at least one window opening onto the film of etchable material; etching said film to undercut said mask layer around a peripheral edge of the window opening; anisotropically etching the first layer through the window to form a well with a wall substantially vertical to the horizontal surface of the substrate; and isotropically etching the first layer to bevel a peripheral edge of the well formed in the first layer, whereby said edge in the first layer is exposed to the isotropic etching from a surface of the substantially vertical wall and from a surface exposed by the undercutting of said mask layer.
Claim 10
Independent Claim
153 words
A method of etching a well in first layer of material overlying a horizontal surface of a substrate comprising the steps of: depositing a film of etchable material on an exposed surface of the first layer of material overlying the substrate; forming a mask layer on said film layer with at least one window opening onto the film of etchable material; etching said film to undercut said mask layer around a peripheral edge of the window opening; anisotropically etching the first layer through the window to form a well with a wall substantially vertical to the horizontal surface of the substrate; and isotropically etching the first layer to bevel a peripheral edge of the well formed in the first layer, whereby said edge in the first layer is exposed to the isotropic etching from a surface of the substantially vertical wall and from a surface exposed by the undercutting of said mask layer.
Claim 11
Dependent Claim
14 words
The method of claim 8 wherein the first layer is a silicon oxide layer.
Claim 12
Dependent Claim
27 words
The method of claim 8 wherein the film of etchable material is selected from the group consisting of metal film, silicon nitride film, silicon and polymer film.
Claim 13
Dependent Claim
20 words
The method of claim 10 wherein the film is a film of aluminum from 100 to 2,000 Angstroms in thickness.
Claim 14
Dependent Claim
14 words
The method of claim 8 wherein the anisotropic etching is performed by dry etching.
Claim 15
Dependent Claim
26 words
The method of claim 8 wherein a thin residual layer of silicon oxide is removed in said well to expose the substrate during said isotropic etching.
Claim 16
Independent Claim
153 words
A method of etching a well with a beveled edge in a layer of silicon oxide overlying a horizontal surface of a substrate, comprising the steps of: ion implanting the layer of silicon oxide to damage a layer of silicon oxide at the surface of the layer of silicon oxide, the damaging of the silicon oxide rendering it more susceptible to chemical etching; forming a mask layer on the surface of the damaged silicon oxide layer to define at least one window opening onto the surface of the silicon dioxide; anisotropically etching said silicon dioxide to form a well with a generally vertical wall intersecting the surface of the silicon dioxide generally perpendicularly at a window edge defined by said mask layer; and isotropically chemically etching said silicon dioxide layer to bevel said window edge, said window edge being exposed to the chemical etching from the vertical wall and through the damaged layer.
Claim 17
Independent Claim
153 words
A method of etching a well with a beveled edge in a layer of silicon oxide overlying a horizontal surface of a substrate, comprising the steps of: ion implanting the layer of silicon oxide to damage a layer of silicon oxide at the surface of the layer of silicon oxide, the damaging of the silicon oxide rendering it more susceptible to chemical etching; forming a mask layer on the surface of the damaged silicon oxide layer to define at least one window opening onto the surface of the silicon dioxide; anisotropically etching said silicon dioxide to form a well with a generally vertical wall intersecting the surface of the silicon dioxide generally perpendicularly at a window edge defined by said mask layer; and isotropically chemically etching said silicon dioxide layer to bevel said window edge, said window edge being exposed to the chemical etching from the vertical wall and through the damaged layer.
Claim 18
Dependent Claim
27 words
The method of claim 14 wherein a thin residual layer of silicon oxide is removed in said well to expose the substrate during said isotropic chemical etching.
Claim 19
Dependent Claim
16 words
The method of claim 14 wherein said anisotropic etching is performed with a fluorine deficient plasma.
References Cited (Backward Citations)
US4352724A
Cited
US4352724B1
Cited
JPS5720450A
Cited
US4372034A
Cited
US4372034B1
Cited
US4417947A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-27 | 1988-05-28 | 1988-11-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-27 | 1992-05-28 | 1992-11-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-27 | 1996-05-28 | 1996-11-27 | $7700.00 | Window Closed / Lapsed |