Edge profile control during patterning of silicon by dry etching with CCl4 -O2 mixtures
Assignee: Signetics Corp
•
Filing: 1982-07-16
•
Granted: 1983-11-29
•
Expires: 2002-07-16
Abstract
Abstract The edge profile of a silicon layer is shaped to have a gradual incline considerably less than 90° by continuously reducing the amount of oxygen mixed with carbon tetrachloride in a reactive ion etching environment. The etching mode varies from complete isotropic etching when the amount of oxygen is maximum, to complete anisotropic etching when the oxygen content is zero.
Inventors
- 👤 Alfred I. Pan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 11:12
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/26; H10P50/264; H10P50/266; H10P50/267; H10P50/268; H10P50/24; H10P50/242; Y; Y10; Y10S; Y10S438/00; Y10S438/978
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
87 words
A method for selectively etching a silicon region of an integrated circuit component, the method comprising the steps of: forming a mask along a surface of the region such that the mask has at least one edge along which silicon of the region is exposed; and subjecting the component to a plasma comprising ions of carbon tetrachloride and oxygen to etch away silicon exposed through the mask while varying the proportion of oxygen in the plasma so as to control the etching between isotropic and anisotropic modes.
Claim 2
Independent Claim
87 words
A method for selectively etching a silicon region of an integrated circuit component, the method comprising the steps of: forming a mask along a surface of the region such that the mask has at least one edge along which silicon of the region is exposed; and subjecting the component to a plasma comprising ions of carbon tetrachloride and oxygen to etch away silicon exposed through the mask while varying the proportion of oxygen in the plasma so as to control the etching between isotropic and anisotropic modes.
Claim 3
Dependent Claim
34 words
A method as in claim 1 wherein the proportion of oxygen in the plasma is sufficiently high at the beginning of the step of subjecting that the etching is substantially isotropic at that point.
Claim 4
Dependent Claim
35 words
A method as in claim 2 wherein the proportion of oxygen in the plasma at the beginning of the step of subjecting does not significantly exceed the value at which the etching is substantially isotropic.
Claim 5
Dependent Claim
32 words
A method as in claim 2 wherein the volume proportion of oxygen in the plasma to that of carbon tetrachloride is approximately one half at the beginning of the step of subjecting.
Claim 6
Dependent Claim
34 words
A method as in claim 2 wherein the proportion of oxygen in the plasma is substantially zero at the end of the step of subjecting, whereby the etching is substantially anisotropic at that point.
Claim 7
Dependent Claim
61 words
A method as in claim 5 wherein the proportion of oxygen in the plasma is gradually reduced during the step of subjecting, whereby a resulting edge of the region at a location where silicon was etched away and which is adjacent to an unetched surface portion of the region is generally sloped at less than 90° relative to the unetched portion.
Claim 8
Dependent Claim
110 words
A method as in claim 5 wherein the proportion of oxygen in the plasma is gradually reduced during an initial part of the step of subjecting, substantially reaches zero at the end of the initial part, and remains there during the remainder of the step of subjecting, whereby a resulting edge of the region at a location where silicon was etched away and which is adjacent to an unetched surface portion of the region comprises a first part adjacent to the unetched portion and generally sloped at less than 90° relative to it and a second part adjacent to the first part and oriented generally orthogonal to the unetched portion.
Claim 9
Dependent Claim
29 words
A method as in claim 1 wherein the step of subjecting is performed as a continuous operation without stops during which there is essentially no etching of the region.
Claim 10
Dependent Claim
22 words
A method as in claim 8 wherein the proportion of oxygen in the plasma is gradually reduced during the step of subjecting.
Claim 11
Dependent Claim
21 words
A method as in claim 1 wherein ions of the plasma are bombarded toward the component during the step of subjecting.
Claim 12
Dependent Claim
14 words
A method as in claim 1 wherein silicon of the region is polycrystalline type.
Claim 13
Dependent Claim
14 words
A method as in claim 1 wherein silicon of the region is monocrystalline type.
References Cited (Backward Citations)
JPS5021573A
Cited
US4352724A
Cited
US4352724B1
Cited
JPS5687666A
Cited
US4383885A
Cited
JPS56125838A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-11-28 | 1987-05-30 | 1987-11-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-11-28 | 1991-05-30 | 1991-11-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-11-28 | 1995-05-30 | 1995-11-29 | $7700.00 | Window Closed / Lapsed |