US4478893A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Polyisocyanate addition products useful as mold release agents and a process for their production
Assignee: Bayer AG
•
Filing: 1983-10-06
•
Granted: 1984-10-23
•
Expires: 2003-10-06
Abstract
Abstract Polyisocyanate addition products are made by reacting a polysiloxane having isocyanate reactive end groups, excess polyisocyanate and a compound selected from the group consisting of aliphatic alcohols, primary aliphatic amines, secondary aliphatic amines and mixtures thereof having a molecular weight of from 75 to 5000 and at least one tertiary amino group and/or oxyalkylene unit. In a preferred embodiment, the polysiloxane is reacted with excess polyisocyanate and the reaction product is subsequently reacted with the alcohol and/or amine. The addition products of this invention are particularly useful as mold release agents in the production of molded lacquer coated plastics by the "in-mold coating process."
Inventors
- 👤 Manfred Schonfelder
- 👤 Peter Haas
- 👤 Geza Avar
- 👤 Helmut Steinberger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 11:08
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/70; C08G18/72; C08G18/80; C08G18/8061; C08G18/807; B; B29; B29C; B29C33/00; B29C33/56; B29C33/60; B29C33/62; C08G18/08; C08G18/10; C08G18/28; C08G18/40; C08G18/61; C08G2125/00
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
156 words
A process for the production of polyurethane-based molded articles covered with a lacquer in which (1) internal walls of a mold are lacquered with an in-mold coating lacquer containing a mold release agent which is a reaction product of: (a) a first reaction product of a polysiloxane having isocyanate reactive end groups and an excess of organic polyisocyanate which first reaction product contains at least two isocyanate end groups and (b) a compound selected from the group consisting of aliphatic alcohols, primary aliphatic amines, secondary aliphatic amines and mixtures thereof which have a molecular weight of from 75 to 5000 and which is monofunctional in the isocyanate addition reaction and contains at least one tertiary amino group and/or oxyalkylene unit before a reaction mixture for producing the polyurethane is introduced into the mold, (2) filling the mold with polyurethane-forming mixture after the lacquer has partially dried, and (3) allowing the contents of the mold to solidify.
Claim 2
Dependent Claim
156 words
A process for the production of polyurethane-based molded articles covered with a lacquer in which (1) internal walls of a mold are lacquered with an in-mold coating lacquer containing a mold release agent which is a reaction product of: (a) a first reaction product of a polysiloxane having isocyanate reactive end groups and an excess of organic polyisocyanate which first reaction product contains at least two isocyanate end groups and (b) a compound selected from the group consisting of aliphatic alcohols, primary aliphatic amines, secondary aliphatic amines and mixtures thereof which have a molecular weight of from 75 to 5000 and which is monofunctional in the isocyanate addition reaction and contains at least one tertiary amino group and/or oxyalkylene unit before a reaction mixture for producing the polyurethane is introduced into the mold, (2) filling the mold with polyurethane-forming mixture after the lacquer has partially dried, and (3) allowing the contents of the mold to solidify.
Claim 3
Dependent Claim
154 words
A process for the production of polyurethane-based molded articles covered with a lacquer in which (1) internal walls of a mold are lacquered with an in-mold coating lacquer containing a mold release agent which is the reaction product of: (a) a first reaction product of a (i) compound selected from the group consisting of aliphatic alcohols, primary aliphatic amines, secondary aliphatic amines and mixtures thereof having a molecular weight of from 75 to 5000 and which is monofunctional in the isocyanate addition reaction and contains at least one tertiary amino group and/or oxyalkylene unit and (ii) an excess of organic polyisocyanate and (b) a polysiloxane containing isocyanate reactive end groups which is difunctional in an isocyanate addition reaction before reaction mixture for producing the polyurethane is introduced into the mold, (2) filling the mold after the lacquer has partially dried with polyurethane forming mixture and (3) allowing the contents of the mold to solidify.
Claim 4
Dependent Claim
154 words
A process for the production of polyurethane-based molded articles covered with a lacquer in which (1) internal walls of a mold are lacquered with an in-mold coating lacquer containing a mold release agent which is the reaction product of: (a) a first reaction product of a (i) compound selected from the group consisting of aliphatic alcohols, primary aliphatic amines, secondary aliphatic amines and mixtures thereof having a molecular weight of from 75 to 5000 and which is monofunctional in the isocyanate addition reaction and contains at least one tertiary amino group and/or oxyalkylene unit and (ii) an excess of organic polyisocyanate and (b) a polysiloxane containing isocyanate reactive end groups which is difunctional in an isocyanate addition reaction before reaction mixture for producing the polyurethane is introduced into the mold, (2) filling the mold after the lacquer has partially dried with polyurethane forming mixture and (3) allowing the contents of the mold to solidify.
Claim 5
Dependent Claim
15 words
The process of claim 1 wherein the lacquer topcoat contains a linear polyurethane polyurea binder.
Claim 6
Dependent Claim
15 words
The process of claim 2 wherein the lacquer topcoat contains a linear polyurethane polyurea binder.
Claim 7
Dependent Claim
21 words
The process of claim 1 wherein the lacquer topcoat contains a binder made of an organic polyisocyanate and a polyhydroxyl compound.
Claim 8
Dependent Claim
21 words
The process of claim 2 wherein the lacquer topcoat contains a binder made of an organic polyisocyanate and a polyhydroxyl compound.
References Cited (Backward Citations)
US3726952A
Cited
GB1365215A
Cited
GB1420293A
Cited
US4033912A
Cited
US4024090A
Cited
US4058492A
Cited
US3993606A
Cited
US4098731A
Cited
US4163830A
Cited
DE3012126A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-23 | 1988-04-23 | 1988-10-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-23 | 1992-04-23 | 1992-10-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-23 | 1996-04-23 | 1996-10-23 | $7700.00 | Window Closed / Lapsed |