US4478771A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of manufacturing fibre-reinforced plastic articles, a prepreg for the manufacture of fibre-reinforced plastic articles and a fibre-reinforced plastic article
Assignee: Individual
•
Filing: 1982-03-09
•
Granted: 1984-10-23
•
Expires: 2002-03-09
Abstract
Abstract A method of manufacturing fibre-reinforced plastic articles out of prepregs, prepregs for the manufacture of fibre-reinforced plastic articles and fibre-reinforced plastic articles manufactured by such method. The prepregs contain glass-fibre mats having a fiber length of preferably 4 to 30 mm and a curable resin having a preferred viscosity in the range between 100 and 100 000 Ns/m 2 . The prepregs are shaped in a mold by vacuum forming and are cured by UV-light.
Inventors
- 👤 Herbert Schreiber
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 02:09
CPC Classifications
B; B29; B29C; B29C33/00; B29C33/56; B29C33/68; B29C70/00; B29C70/04; B29C70/28; B29C70/40; B29C70/42; B29C70/44; B29C70/54; B29C70/542; C; C08; C08J; C08J5/00; C08J5/24; C08J5/241; C08J5/244; B29C35/00; B29C35/02; B29C35/08; B29C35/0805; B29C2035/0827; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249924; Y10T428/24994; Y10T428/24995; Y10T428/249952
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
132 words
A method of manufacturing fibre-reinforced plastic articles, said method comprising the steps of providing a planar prepreg containing reinforcing fibres impregnated by curable resins, covering at least one side of said prepreg with a flexible and stretchable resin, providing an open contoured mold, utilizing air pressure exerted on the covered side of the prepreg deforming the covered prepreg to conform to the contour of the mold, and curing the shaped prepreg thereafter, the viscosity of the totality of flowable materials present in the prepreg inclusive of possible filling agents and exclusive of any reinforcing fibres measured at the temperature of said deformation and a low shearing speed amounts to at least 10 Na/m 2 and less than about 100,000 Na/m 2 and the length of individual reinforcing fibres exceeds about 2 mm.
Claim 2
Independent Claim
132 words
A method of manufacturing fibre-reinforced plastic articles, said method comprising the steps of providing a planar prepreg containing reinforcing fibres impregnated by curable resins, covering at least one side of said prepreg with a flexible and stretchable resin, providing an open contoured mold, utilizing air pressure exerted on the covered side of the prepreg deforming the covered prepreg to conform to the contour of the mold, and curing the shaped prepreg thereafter, the viscosity of the totality of flowable materials present in the prepreg inclusive of possible filling agents and exclusive of any reinforcing fibres measured at the temperature of said deformation and a low shearing speed amounts to at least 10 Na/m 2 and less than about 100,000 Na/m 2 and the length of individual reinforcing fibres exceeds about 2 mm.
Claim 3
Dependent Claim
23 words
The method of claim 1, further comprising the step of covering the other side of the prepreg with the flexible and stretchable foil.
Claim 4
Dependent Claim
24 words
The method of claim 1, wherein said step of pressing the prepreg is effected by the means of vacuum shaping onto the open mold.
Claim 5
Dependent Claim
16 words
The method of claim 1, wherein the viscosity is at least about 100 Ns/m 2 .
Claim 6
Dependent Claim
24 words
The method of claim 1, wherein the length of the reinforcing fibres is in the range from about 4 mm to about 50 mm.
Claim 7
Dependent Claim
20 words
The method of claim 1, wherein the length of the reinforcing fibres amounts to not more than about 30 mm.
Claim 8
Dependent Claim
31 words
The method of claim 1, wherein the curable resin impregnated in the prepreg is an electron beam curable resin and said step of curing is by means of such electron beam.
Claim 9
Dependent Claim
30 words
The method of claim 1, wherein the curable resin impregnated in the prepreg is an ultraviolet light curable resin and said step of curing is by means of ultraviolet light.
Claim 10
Dependent Claim
30 words
The method of claim 1, wherein the curable resin impregnated in the prepreg is a visible light curable resin and said step of curing is by means of visible light.
Claim 11
Dependent Claim
25 words
The method of claim 1, wherein the covering foil is a foil which is detachable form the cured resin and consists of a soft polyolefin.
Claim 12
Dependent Claim
24 words
The method of claim 1, wherein the covering foil is a foil which is detachable from the cured resin and consists of a polyvinylidene-chloride.
Claim 13
Dependent Claim
24 words
The method of claim 1, wherein the covering foil is a foil which strongly adheres to the cured resin after said step of curing.
Claim 14
Dependent Claim
19 words
The method of claim 12, wherein the covering foil is a vinylchloride-polymeric or -copolymeric foil containing a curable monomer.
Claim 15
Dependent Claim
31 words
The method of claim 12, further including the step of heat curing the foil wherein the side of the foil facing the open form is provided with a ray impermeable coloring.
Claim 16
Dependent Claim
31 words
The method of claim 7, wherein there is provided between the covering foil facing the open mold and the prepreg a colored thin layer which is cured by the electron beam.
Claim 17
Dependent Claim
31 words
The method of claim 8, wherein there is provided between the covering foil facing the open mold and the prepreg a colored thin layer which is cured by the ultraviolet light.
Claim 18
Dependent Claim
31 words
The method of claim 9, wherein there is provided between the covering foil facing the open mold and the prepreg a colored thin layer which is cured by the visible light.
Claim 19
Dependent Claim
13 words
The method of claim 1, wherein the curable resin is an unsaturated polyester.
Claim 20
Dependent Claim
13 words
The method of claim 1, wherein the curable resin is an unsaturated polyurethane.
Claim 21
Dependent Claim
18 words
The method of claim 18, wherein the unsaturated polyester is present as a solution in a polymerizable monomer.
Claim 22
Dependent Claim
18 words
The method of claim 19, wherein the unsaturated polyurethane is present as a solution in a polymerizable monomer.
Claim 23
Dependent Claim
11 words
The method of claim 20, wherein the polymerizable monomer is styrene.
Claim 24
Dependent Claim
11 words
The method of claim 21, wherein the polymerizable monomer is styrene.
Claim 25
Dependent Claim
27 words
The method of claim 1, wherein the viscosity of a resin having a lower viscosity is increased to the required viscosity by dissolving therein a soluble polymer.
Claim 26
Dependent Claim
24 words
The method of claim 24, wherein the increasing of the viscosity is carried out by dissolving a cellulose-ester which is soluble in a UP-resin.
Claim 27
Dependent Claim
11 words
The method of claim 24, wherein the cellulose-ester is a cellulose-acetobutyrate.
Claim 28
Dependent Claim
28 words
The method of claim 24, wherein the viscosity of the lower viscosity resin is increased by dissolving therein a soluble polymer prior to the manufacture of the prepreg.
Claim 29
Dependent Claim
27 words
The method of claim 24, wherein the viscosity of the lower viscosity resin is increased by dissolving therein a soluble polymer during the manufacture of the prepreg.
Claim 30
Dependent Claim
27 words
The method of claim 1, wherein there is provided between said covering foil and said prepreg a colored heat curable thin layer which is cured by heat.
References Cited (Backward Citations)
US4054713A
Cited
US4012553A
Cited
US4178406A
Cited
US4201612A
Cited
US4207282A
Cited
US4311753A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-23 | 1988-04-23 | 1988-10-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-23 | 1992-04-23 | 1992-10-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-23 | 1996-04-23 | 1996-10-23 | $7700.00 | Window Closed / Lapsed |