Process for forming rust resistant tin oxide coatings on glass containers
Assignee: GLASS CONTAINERS Corp A CORP OF CA
•
Filing: 1982-07-12
•
Granted: 1984-10-16
•
Expires: 2002-07-12
Abstract
Abstract Rust resistant, scratch resistant coatings are formed on glass containers during passage thereof through a tunnel at 500°-720° C. by forming a first fluid stream by passing dry air through a bath of tin tetrachloride, forming a second fluid stream by passing dry air through a bath of phosphorous trichloride or phosphorous oxychloride, combining the two fluid streams to form a fluid coating stream, and introducing the fluid coating stream containing tin tetrachloride and phosphorous halide in a weight ratio of between 2:1 to 9:1 into the tunnel to contact the hot glass containers and form a coating on the glass containers.
Inventors
- 👤 Syed R. Ali-Zaidi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 09:27
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C03C17/245; C03C17/2453; C03C2217/00; C03C2217/20; C03C2217/21; C03C2217/23; C03C2218/00; C03C2218/10; C03C2218/15; C03C2218/152
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
181 words
In a process for the formation of a coating on a glass container by the formation of a tin oxide coating on the containers during passage through a tunnel adjacent the forming machine, wherein the bottles are at a temperature of between about 500°-720° C.; the improvement wherein said coating is rendered rust resistant and the scratch resistance thereof is enhanced by: passing dry air through a bath of tin tetrachloride to form a first fluid stream; passing dry air through a bath of a phosphorous halide, selected from the group consisting of phosphorous trichloride or phosphorous oxychloride, to form a second fluid stream; combining the first and second fluid streams, and intimately mixing said streams, to form a fluid coating stream comprising air containing tin tetrachloride and said phosphorous halide in a ratio, by weight, of between 2:1 and 9:1; combining said fluid coating stream with additional air, and introducing said fluid coating stream combined with said additional air into said tunnel for contact with containers passing therethrough, whereby said rust resistant, scratch resistant coating is formed on said containers.
Claim 2
Dependent Claim
181 words
In a process for the formation of a coating on a glass container by the formation of a tin oxide coating on the containers during passage through a tunnel adjacent the forming machine, wherein the bottles are at a temperature of between about 500°-720° C.; the improvement wherein said coating is rendered rust resistant and the scratch resistance thereof is enhanced by: passing dry air through a bath of tin tetrachloride to form a first fluid stream; passing dry air through a bath of a phosphorous halide, selected from the group consisting of phosphorous trichloride or phosphorous oxychloride, to form a second fluid stream; combining the first and second fluid streams, and intimately mixing said streams, to form a fluid coating stream comprising air containing tin tetrachloride and said phosphorous halide in a ratio, by weight, of between 2:1 and 9:1; combining said fluid coating stream with additional air, and introducing said fluid coating stream combined with said additional air into said tunnel for contact with containers passing therethrough, whereby said rust resistant, scratch resistant coating is formed on said containers.
Claim 3
Dependent Claim
13 words
The process defined in claim 1 wherein said phosphorous halide is phosphorous trichloride.
Claim 4
Dependent Claim
13 words
The process defined in claim 1 wherein said phosphorous halid is phosphorous oxychloride.
Claim 5
Dependent Claim
20 words
The process defined in claim 1 wherein the ratio of tin tetrachloride and phosphorous halide is between 3:1 to 4:1.
Claim 6
Dependent Claim
17 words
The process defined in claim 1 wherein the coating formed has a thickness of between 350-450 angstroms.
Claim 7
Dependent Claim
17 words
The process defined in claim 5 wherein the coating found has a thickness of about 400 angstroms.
Claim 8
Dependent Claim
32 words
The process defined in claim 1 wherein up to ten percent of said tin tetrachloride is replaced by a metal halide selected from the group consisting of silicon tetrachloride and titanium tetrachloride.
Claim 9
Dependent Claim
33 words
The process defined in claim 1 wherein up to ten percent of said tin tetrachloride is replaced by a metal halide selected from the group consisting of chlorides of aluminum, zinc or zirconium.
Claim 10
Dependent Claim
170 words
In a process for the formation of a coating on a glass container by the formation of a tin oxide coating on the containers during passage through a tunnel adjacent the forming machine, wherein the bottles are at a temperature of between about 500°-720° C.; the improvement wherein said coating is rendered rust resistant and the scratch resistance thereof is enhanced by: passing dry air through a bath of tin tetrachloride to form a first fluid stream; passing dry air through a bath of phosphorous trichloride to form a second fluid stream; combining and intimately mixing the first and second fluid streams to form a fluid coating stream comprising air containing tin tetrachloride and said phosphorous halide in a ratio, by weight, of between 3:1 to 4:1; combining said fluid coating stream with a stream of air; and introducing said combined streams into said tunnel for contact with containers passing therethrough, whereby said rust resistant, scratch resistant coating, having a thickness of between 350-450 angstroms, is formed on said containers.
Claim 11
Dependent Claim
170 words
In a process for the formation of a coating on a glass container by the formation of a tin oxide coating on the containers during passage through a tunnel adjacent the forming machine, wherein the bottles are at a temperature of between about 500°-720° C.; the improvement wherein said coating is rendered rust resistant and the scratch resistance thereof is enhanced by: passing dry air through a bath of tin tetrachloride to form a first fluid stream; passing dry air through a bath of phosphorous trichloride to form a second fluid stream; combining and intimately mixing the first and second fluid streams to form a fluid coating stream comprising air containing tin tetrachloride and said phosphorous halide in a ratio, by weight, of between 3:1 to 4:1; combining said fluid coating stream with a stream of air; and introducing said combined streams into said tunnel for contact with containers passing therethrough, whereby said rust resistant, scratch resistant coating, having a thickness of between 350-450 angstroms, is formed on said containers.
References Cited (Backward Citations)
US3093508A
Cited
US3012902A
Cited
US3989864A
Cited
US4100310A
Cited
US4123244A
Cited
US4289816A
Cited
US4294868A
Cited
US4261722A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-16 | 1988-04-16 | 1988-10-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-16 | 1992-04-16 | 1992-10-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-16 | 1996-04-16 | 1996-10-16 | $7700.00 | Window Closed / Lapsed |