Process for improved glass article coating, and such coated articles
Assignee: Lam Partnership
•
Filing: 1980-03-03
•
Granted: 1981-09-15
•
Expires: 2000-03-03
Abstract
Abstract A method for "hot end" coating of vitreous articles, and particularly glassware such as bottles, with zinc oxide and magnesium oxide coatings from aqueous solutions of organic and inorganic zinc compounds, magnesium compounds, and mixtures thereof. Particularly useful are zinc acetate and magnesium acetate, which are applied to the vitreous surface at an elevated temperature, and preferably between about 425° C. and 650° C., to evaporate the water from the solution and pyrolytically decompose the metal compound or compounds to form refractory oxide coatings which are transparent and adherent, and articles coated by such a method.
Inventors
- 👤 Clement V. Fogelberg
- 👤 Joseph H. Romig
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 09:00
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/34; C03C17/42; C03C17/22; C03C17/23; C03C17/25; C03C2217/00; C03C2217/20; C03C2217/21; C03C2217/216; C03C2217/228; C03C2217/23; C03C2218/00; C03C2218/10; C03C2218/11; C03C2218/112; C03C2218/17; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/131; Y10T428/1317; Y10T428/1321
Claims Analysis
Total Claims: 52
Claim 1
Independent Claim
119 words
A method for forming protective coatings upon glass articles comprising: positioning a glass article heated to an elevated temperature within a coating location; applying an aqueous solution of a coating compound selected from the group consisting of magnesium compounds, zinc compounds and mixtures thereof upon the surface of the heated glass article; evaporating the solvent from the solution at the surface of the glass article; pyrolytically decomposing the remaining compound at the surface of the glass article to form a continuous, adherent and substantially transparent coating of the coated compound metal oxide upon the surface of the glass article; cooling the glass article and metal oxide coating thereon; and applying a second, lubricious coating thereto at a lower temperature.
Claim 2
Independent Claim
119 words
A method for forming protective coatings upon glass articles comprising: positioning a glass article heated to an elevated temperature within a coating location; applying an aqueous solution of a coating compound selected from the group consisting of magnesium compounds, zinc compounds and mixtures thereof upon the surface of the heated glass article; evaporating the solvent from the solution at the surface of the glass article; pyrolytically decomposing the remaining compound at the surface of the glass article to form a continuous, adherent and substantially transparent coating of the coated compound metal oxide upon the surface of the glass article; cooling the glass article and metal oxide coating thereon; and applying a second, lubricious coating thereto at a lower temperature.
Claim 3
Dependent Claim
27 words
A method for coating glass articles as set forth in claim 1 in which the surface of the glass article is at a temperature above 400° C.
Claim 4
Dependent Claim
31 words
A method for coating glass articles as set forth in claim 1 in which the surface of the glass article is at a temperature between about 425° C. and 650° C.
Claim 5
Dependent Claim
49 words
A method for coating glass articles as set forth in claim 1 in which the solution compound is melted after the water is substantially evaporated to form a coating of the solution compound upon the glass article surface and thereafter is pyrolyzed to form the coating of metal oxide.
Claim 6
Dependent Claim
32 words
A method for coating glass articles as set forth in claim 1 in which the aqueous solution is sprayed upon the surface of the glass articles in the form of a mist.
Claim 7
Dependent Claim
32 words
A method for coating glass articles as set forth in claim 1 in which the dissolved coating compound comprises between about 10% by weight and 50% by weight of the aqueous solution.
Claim 8
Dependent Claim
41 words
A method for coating glass articles as set forth in claim 1 in which the coating solution includes a mixture of coating compounds one of which is zinc fluosilcate in amounts not greater than about 30% by weight of the solution.
Claim 9
Dependent Claim
56 words
A method for coating glass articles as set forth in claim 1 in which the coating compound is highly soluble in water, has a melting point below the surface temperature of the glass articles, and a pyrolytic decomposition point below the surface temperature of the glass articles but above the melting point of the coating compound.
Claim 10
Dependent Claim
45 words
A method for coating glass articles as set forth in claim 8 in which the coating compound is selected from the group consisting of magnesium acetate, magnesium nitrate, magnesium formate, magnesium perchlorate, magnesium chloride, zinc acetate, zinc formate, zinc nitrate, zinc perchlorate and zinc chloride.
Claim 11
Dependent Claim
20 words
A method for coating glass articles as set forth in claim 9 in which the coating compound is magnesium acetate.
Claim 12
Dependent Claim
36 words
A method for coating glass articles as set forth in claim 10 in which the magnesium acetate is applied as a solution containing between 10% and 50% by weight of magnesium acetate relative to the solvent.
Claim 13
Dependent Claim
28 words
A method for coating glass articles as set forth in claim 10 in which the surface of the glass articles are at a temperature above about 400° C.
Claim 14
Dependent Claim
31 words
A method for coating glass articles as set forth in claim 10 in which the surface of the glass articles are at a temperature between about 425° C. and 650° C.
Claim 15
Dependent Claim
20 words
A method for coating glass articles as set forth in claim 9 in which the coating compound is zinc acetate.
Claim 16
Dependent Claim
36 words
A method for coating glass articles as set forth in claim 14 in which the zinc acetate is applied as a solution containing between 10% and 50% by weight of zinc acetate relative to the solvent.
Claim 17
Dependent Claim
28 words
A method for coating glass articles as set forth in claim 14 in which the surface of the glass articles are at a temperature above about 400° C.
Claim 18
Dependent Claim
31 words
A method for coating glass articles as set forth in claim 14 in which the surface of the glass articles are at a temperature between about 425° C. and 650° C.
Claim 19
Dependent Claim
27 words
A method for coating glass articles as set forth in claim 1 in which the aqueous solvent includes not more than 50% by volume of an alcohol.
Claim 20
Dependent Claim
22 words
A method for coating glass articles as set forth in claim 18 in which the alcohol contains 1 to 4 carbon atoms.
Claim 21
Dependent Claim
27 words
A method for coating glass articles as set forth in claim 1 in which the metal oxide coating is between about 0.1 micron and 1 micron thick.
Claim 22
Dependent Claim
42 words
A method for coating glass surfaces as set forth in claim 1 in which the lubricious coating includes at least one compound selected from the group consisting of waxy polylefins, beeswax, fatty acids, alkali metal salts of fatty acids, and polyvinyl alcohols.
Claim 23
Independent Claim
90 words
A method for forming protective coatings on glass comprising: spraying an aqueous solution of magnesium acetate onto the surface of glass at an elevated temperature; evaporating the solvent from the aqueous solution of magnesium acetate at the surface of the glass; pyrolytically decomposing the magnesium acetate at the surface of the glass to form a continuous, transparent film of magnesium oxide which tenaciously adheres to the surface of the glass; cooling the glass article and magnesium oxide film thereon; and applying a second, lubricious coating thereto at a lower temperature.
Claim 24
Independent Claim
90 words
A method for forming protective coatings on glass comprising: spraying an aqueous solution of magnesium acetate onto the surface of glass at an elevated temperature; evaporating the solvent from the aqueous solution of magnesium acetate at the surface of the glass; pyrolytically decomposing the magnesium acetate at the surface of the glass to form a continuous, transparent film of magnesium oxide which tenaciously adheres to the surface of the glass; cooling the glass article and magnesium oxide film thereon; and applying a second, lubricious coating thereto at a lower temperature.
Claim 25
Dependent Claim
64 words
A method for forming a protective coating on glassware as set forth in claim 22 in which, the aqueous solution of magnesium acetate contains about 10% by weight to 50% by weight of magnesium acetate relative to the solvent, is applied as a spray to the glassware, and the surface of the glassware is at a temperature between about 425° C. And 650° C.
Claim 26
Independent Claim
90 words
A method for forming protective coatings on glass comprising: spraying an aqueous solution of zinc acetate onto the surface of glass at an elevated temperature; evaporating the solvent from the aqueous solution of zinc acetate at the surface of the glass; pyrolytically decomposing the zinc acetate at the surface of the glass to form a continuous, transparent film of zinc oxide which tenaciously adheres to the surface of the glass cooling the glass article and zinc oxide film thereon; and applying a second, lubricious coating thereto at a lower temperature.
Claim 27
Independent Claim
90 words
A method for forming protective coatings on glass comprising: spraying an aqueous solution of zinc acetate onto the surface of glass at an elevated temperature; evaporating the solvent from the aqueous solution of zinc acetate at the surface of the glass; pyrolytically decomposing the zinc acetate at the surface of the glass to form a continuous, transparent film of zinc oxide which tenaciously adheres to the surface of the glass cooling the glass article and zinc oxide film thereon; and applying a second, lubricious coating thereto at a lower temperature.
Claim 28
Dependent Claim
64 words
A method for forming a protective coating on glassware as set forth in claim 24 in which, the aqueous solution of zinc acetate contains about 10% by weight to 50% by weight of zinc acetate relative to the solvent, is applied as a spray to the glassware, and the surface of the glassware is at a temperature between about 425° C. and 650° C.
Claim 29
Independent Claim
105 words
A method for forming protective coatings on glass comprising: spraying an aqueous solution of magnesium acetate and zinc acetate onto the surface of glass at an elevated temperature; evaporating the solvent from the aqueous solution of magnesium acetate and zinc acetate at the surface of the glass; pyrolytically decomposing the magnesium acetate and zinc acetate at the surface of the glass to form a continuous, transparent film of magnesium oxide and zinc oxide which tenaciously adheres to the surface of the glass; cooling the glass article and magnesium oxide and zinc oxide film thereon; and applying a second, lubricious coating thereto at a lower temperature.
Claim 30
Independent Claim
105 words
A method for forming protective coatings on glass comprising: spraying an aqueous solution of magnesium acetate and zinc acetate onto the surface of glass at an elevated temperature; evaporating the solvent from the aqueous solution of magnesium acetate and zinc acetate at the surface of the glass; pyrolytically decomposing the magnesium acetate and zinc acetate at the surface of the glass to form a continuous, transparent film of magnesium oxide and zinc oxide which tenaciously adheres to the surface of the glass; cooling the glass article and magnesium oxide and zinc oxide film thereon; and applying a second, lubricious coating thereto at a lower temperature.
Claim 31
Dependent Claim
70 words
A method for forming a protective coating on glassware as set forth in claim 26 in which, the aqueous solution of magnesium acetate and zinc acetate contains about 10% by weight to 50% by weight of magnesium acetate and zinc acetate relative to the solvent, is applied as a spray to the glassware, and the surface of the glassware is at a temperature between about 425° C. and 650° C.
Claim 32
Dependent Claim
51 words
A glass article having protective and lubricious coatings thereon, said articles comprising: a glass surface; a metal oxide coating selected from the group consisting of transparent magnesium oxide, zinc oxide and mixtures thereof adhered directly to the surface; and a lubricious coating of an organic compound adhered to the metal oxide.
Claim 33
Dependent Claim
51 words
A glass article having protective and lubricious coatings thereon, said articles comprising: a glass surface; a metal oxide coating selected from the group consisting of transparent magnesium oxide, zinc oxide and mixtures thereof adhered directly to the surface; and a lubricious coating of an organic compound adhered to the metal oxide.
Claim 34
Dependent Claim
40 words
A coated vitreous surface as set forth in claim 28 in which the lubricious coating includes at least one constituent selected from the group consisting of waxy polyolefins, beeswax, fatty acids, alkali metal salts of fatty acids, and polyvinyl alcohols.
Claim 35
Dependent Claim
24 words
A coated vitreous surface as set forth in claim 28 in which the metal oxide coating is not greater than one quarter micron thick.
Claim 36
Dependent Claim
59 words
Glassware having protective coatings thereon, the glassware comprising: a glass surface; a transparent, continuous, thin coating of magnesium oxide adhered to the glass surface; and a lubricious coating including at least one constituent selected from the group consisting of waxy polyolefins, beeswax, fatty acids, alkali metal salts of fatty acids and polyvinyl alcohols adhered to the magnesium oxide coating.
Claim 37
Dependent Claim
59 words
Glassware having protective coatings thereon, the glassware comprising: a glass surface; a transparent, continuous, thin coating of magnesium oxide adhered to the glass surface; and a lubricious coating including at least one constituent selected from the group consisting of waxy polyolefins, beeswax, fatty acids, alkali metal salts of fatty acids and polyvinyl alcohols adhered to the magnesium oxide coating.
Claim 38
Dependent Claim
22 words
Coated glassware as set forth in claim 31 in which the magnesium oxide coating is not greater than one quarter micron thick.
Claim 39
Dependent Claim
59 words
Glassware having protective coatings thereon, the glassware comprising: a glass surface; a transparent, continuous, thin coating of zinc oxide adhered to the glass surface; and a lubricious coating including at least one constituent selected from the group consisting of waxy polyolefins, beeswax, fatty acids, alkali metal salts of fatty acids and polyvinyl alcohols adhered to the zinc oxide coating.
Claim 40
Dependent Claim
59 words
Glassware having protective coatings thereon, the glassware comprising: a glass surface; a transparent, continuous, thin coating of zinc oxide adhered to the glass surface; and a lubricious coating including at least one constituent selected from the group consisting of waxy polyolefins, beeswax, fatty acids, alkali metal salts of fatty acids and polyvinyl alcohols adhered to the zinc oxide coating.
Claim 41
Dependent Claim
22 words
Coated glassware as set forth in claim 33 in which the zinc oxide coating is not greater than one quarter micron thick.
Claim 42
Dependent Claim
65 words
Glassware having protective coatings thereon, the glassware comprising: a glass surface; a transparent, continuous, thin coating of zinc oxide and magnesium oxide adhered to the glass surface; and a lubricious coating including at least one constituent selected from the group consisting of waxy polyolefins, beeswax, fatty acids, alkali metal salts of fatty acids and polyvinyl alcohols adhered to the zinc oxide and magnesium oxide coating.
Claim 43
Dependent Claim
65 words
Glassware having protective coatings thereon, the glassware comprising: a glass surface; a transparent, continuous, thin coating of zinc oxide and magnesium oxide adhered to the glass surface; and a lubricious coating including at least one constituent selected from the group consisting of waxy polyolefins, beeswax, fatty acids, alkali metal salts of fatty acids and polyvinyl alcohols adhered to the zinc oxide and magnesium oxide coating.
Claim 44
Dependent Claim
27 words
Coated glass ware as set forth in claim 35 in which the zinc oxide and the magnesium oxide coating is not greater than one quarter micron thick.
Claim 45
Independent Claim
121 words
A method for forming protective coatings on glass articles, the method comprising: positioning a glass article heated to an elevated temperature within a coating location; applying a coating compound selected from the group consisting of magnesium compounds, zinc compounds and mixtures thereof to the surface of the heated glass article; melting the coating compound to form a coating at the surface of the glass article; pyrolytically decomposing the coating compound at the surface of the glass article to form a continuous, adherent and substantially transparent coating of the coating compound metal oxide upon the surface of the glass article; and applying a second lubricious coating to the metal oxide coating at a temperature below that at which pyrolytic decomposition takes place.
Claim 46
Independent Claim
121 words
A method for forming protective coatings on glass articles, the method comprising: positioning a glass article heated to an elevated temperature within a coating location; applying a coating compound selected from the group consisting of magnesium compounds, zinc compounds and mixtures thereof to the surface of the heated glass article; melting the coating compound to form a coating at the surface of the glass article; pyrolytically decomposing the coating compound at the surface of the glass article to form a continuous, adherent and substantially transparent coating of the coating compound metal oxide upon the surface of the glass article; and applying a second lubricious coating to the metal oxide coating at a temperature below that at which pyrolytic decomposition takes place.
Claim 47
Dependent Claim
42 words
A method for coating glass articles as set forth in claim 37 in which the lubricious coating includes at least one compound selected from the group consisting of waxy polylefins, beeswax, fatty acids, alkali metal salts of fatty acids, and polyvinyl alcohols.
Claim 48
Dependent Claim
28 words
A method for coating glass articles as set forth in claim 37 in which the surface of the glass article is initially at a temperature above 400° C.
Claim 49
Dependent Claim
32 words
A method for coating glass articles as set forth in claim 39 in which the surface of the glass article is initially at a temperature between about 425° C. and 650° C.
Claim 50
Dependent Claim
45 words
A method for coating glass articles as set forth in claim 37 in which the coating compound is selected from the group consisting of magnesium acetate, magnesium nitrate, magnesium formate, magnesium perchlorate, magnesium chloride, zinc acetate, zinc formate, zinc nitrate, zinc perchlorate and zinc chloride.
Claim 51
Dependent Claim
20 words
A method for coating glass articles as set forth in claim 41 in which the coating compound is magnesium acetate.
Claim 52
Dependent Claim
20 words
A method of coating glass articles as set forth in claim 41 in which the coating compound is zinc acetate.
References Cited (Backward Citations)
US2617741A
Cited
US2617742A
Cited
US2791521A
Cited
US2662035A
Cited
US3323889A
Cited
US3357857A
Cited
US3944683A
Cited
US3694299A
Cited
US3984591A
Cited
US4191585A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-09-14 | 1985-03-16 | 1985-09-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-09-14 | 1989-03-16 | 1989-09-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-09-14 | 1993-03-16 | 1993-09-15 | $7700.00 | Window Closed / Lapsed |