Method for applying an inorganic coating to a glass surface
Assignee: American Glass Research Inc
•
Filing: 1979-12-27
•
Granted: 1981-04-14
•
Expires: 1999-12-27
Abstract
Abstract Inorganic coatings for glass surfaces, especially hot end coatings for glassware, are produced by applying vapors of thermally decomposable metal compounds such as stannic chloride to the surface of glass at an elevated temperature and maintaining in a zone adjacent to and in close proximity to the heated surface a region of elevated moisture content. In a preferred form, separate streams of metal compound vapor and water vapor are directed onto the surface of the heated glass.
Inventors
- 👤 John H. Novak
- 👤 Gary L. Smay
- 👤 John S. Wasylyk
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 12:16
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C03C17/245; C03C2217/00; C03C2217/20; C03C2217/21; C03C2217/211; C03C2217/212; C03C2218/00; C03C2218/10; C03C2218/15; C03C2218/152
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
77 words
In a method for forming an inorganic coating on the surface of glass by directing onto said surface at an elevated temperature, a gas stream containing a vapor of a metal compound which is thermally decomposable to form said inorganic coating, the improvement of establishing in a zone in close proximity to said surface a relative humidity of at least about 55 percent, sufficient to increase the rate of formation of said metal oxide on said surface.
Claim 2
Dependent Claim
77 words
In a method for forming an inorganic coating on the surface of glass by directing onto said surface at an elevated temperature, a gas stream containing a vapor of a metal compound which is thermally decomposable to form said inorganic coating, the improvement of establishing in a zone in close proximity to said surface a relative humidity of at least about 55 percent, sufficient to increase the rate of formation of said metal oxide on said surface.
Claim 3
Dependent Claim
39 words
A method according to claim 1 wherein said increase in relative humidity is achieved by directing onto said surface a gas stream including water vapor, which stream is separate from said stream containing a vapor of said metal compound.
Claim 4
Dependent Claim
18 words
A method according to claim 1 wherein said metal compound is tin tetrachloride, titanium tetrachloride or tetraisopropyl titanate.
Claim 5
Dependent Claim
13 words
A method according to claim 1 wherein said metal compound is tin tetrachloride.
Claim 6
Dependent Claim
15 words
A method according to claim 1 wherein said gas stream including water vapor is steam.
Claim 7
Dependent Claim
18 words
A method according to claim 1 wherein said zone has a thickness not greater than about 7.5 cm.
Claim 8
Dependent Claim
16 words
A method according to claim 6 wherein said thickness is not greater than about 5.0 cm.
Claim 9
Dependent Claim
21 words
A method according to claim 1 wherein the temperature of said glass is from about 100° C. to about 700° C.
Claim 10
Dependent Claim
18 words
A method according to claim 8 wherein said temperature is from about 300° C. to about 650° C.
Claim 11
Dependent Claim
73 words
In a method for applying an inorganic coating to glassware by contacting glassware at an elevated temperature with a thermally decomposable compound, the improvement of directing onto the surface of said glassware a stream of a vapor of said thermally decomposable compound and a separate stream of steam, wherein said streams are not permitted to contact one another until they are in a zone in close proximity to the surface of said glassware.
Claim 12
Dependent Claim
73 words
In a method for applying an inorganic coating to glassware by contacting glassware at an elevated temperature with a thermally decomposable compound, the improvement of directing onto the surface of said glassware a stream of a vapor of said thermally decomposable compound and a separate stream of steam, wherein said streams are not permitted to contact one another until they are in a zone in close proximity to the surface of said glassware.
Claim 13
Dependent Claim
18 words
A method according to claim 10 wherein said metal compound is tin tetrachloride, titanium tetrachloride or tetraisopropyl titanate.
Claim 14
Dependent Claim
50 words
A method according to claim 11 wherein said glassware is transported on a conveyor past an application station including nozzles for application of said metal compound and said water vapor, and the distance from the side wall of the glassware closest to the nozzles does not exceed about 2.5 cm.
Claim 15
Dependent Claim
13 words
A method according to claim 12 wherein said metal compound is tin tetrachloride.
Claim 16
Dependent Claim
39 words
A method according to claim 11 wherein said glassware is rotated adjacent to nozzles for application of said metal compound and said water vapor, and the distance from said glassware to said nozzles does not exceed about 7.0 cm.
Claim 17
Dependent Claim
15 words
A method according to claim 14 wherein said distance does not exceed about 5 cm.
Claim 18
Dependent Claim
15 words
A method according to claim 14 wherein said method does not exceed about 2.5 cm.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-04-13 | 1984-10-13 | 1985-04-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-04-13 | 1988-10-13 | 1989-04-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-04-13 | 1992-10-13 | 1993-04-14 | $7700.00 | Window Closed / Lapsed |